Dislocations in InAs Epilayers Grown by MBE on GaAs Substrates Under Various Conditions

Published online by Cambridge University Press:  10 February 2011

Hongmei Wang
Affiliation:
Division of Novel Materials, Institute of Semiconductors, Chinese Academy of Sciences, P.O.Box 912, Beijing 100083, P.R.China
Yiping Zeng
Affiliation:
Division of Novel Materials, Institute of Semiconductors, Chinese Academy of Sciences, P.O.Box 912, Beijing 100083, P.R.China
Liang Pan
Affiliation:
Division of Novel Materials, Institute of Semiconductors, Chinese Academy of Sciences, P.O.Box 912, Beijing 100083, P.R.China
Hongwei Zhou
Affiliation:
Division of Novel Materials, Institute of Semiconductors, Chinese Academy of Sciences, P.O.Box 912, Beijing 100083, P.R.China
Zhanping Zhu
Affiliation:
Division of Novel Materials, Institute of Semiconductors, Chinese Academy of Sciences, P.O.Box 912, Beijing 100083, P.R.China
Meiying Kong
Affiliation:
Division of Novel Materials, Institute of Semiconductors, Chinese Academy of Sciences, P.O.Box 912, Beijing 100083, P.R.China
Get access

Abstract

Using Transmission Electron Microscopy, we studied the misfit and threading dislocations in InAs epilayers. All the samples, with thickness around 0.5μm, were grown on GaAs(001) substrates by molecular beam epitaxy under As-rich or In-rich conditions. The As-rich growth undergoes 2D-3D mode transition process, which was inhibited under In-rich surface. High step formation energy under As-deficient reconstruction inhibits the formation of 3D islands and leads to 2D growth. The mechanism of misfit dislocations formation was different under different growth condition which caused the variation of threading dislocation density in the epilayers.

Type
Research Article
Copyright
Copyright © Materials Research Society 1998

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

[1]. Kawai, T., Yonezu, H., Ogasawara, Y., Saito, D. and Pak, K., Appl. Phys. Lett., 63, p.2067 (1993).10.1063/1.110594Google Scholar
[2]. Grandjean, N. and Massies, J., J. Cryst. Growth., 134, p. 51 (1993).10.1016/0022-0248(93)90008-KGoogle Scholar
[3]. Trampert, A., Tournie, E. and Ploog., K. H., Appl. Phys. Lett., 66, p. 2265 (1995).10.1063/1.113187Google Scholar
[4]. Tournie, E. and Ploog., K. H., Appl. Phys. Lett., 62. p. 858 (1993).10.1063/1.108546Google Scholar
[5]. Tournie, E., Grandjean, N., Trampert, A., Massies, J. and Ploog., K. H. J.Cryst.Growth., 150, p. 460 (1995).10.1016/0022-0248(95)80254-AGoogle Scholar
[6]. Tamura, M., Hashimoto, A. and Sugiyama, N., J. Appl. Phys., 70, p.4770 (1991).10.1063/1.349069Google Scholar
[7]. Yamaguchi, H., Fahy, M. R. and Joyce., B. A., Appl. Phys. Lett., 69, p.776 (1996).10.1063/1.117888Google Scholar
[8]. Dodson, B. W., Appl. Phys. Lett., 53, p.394 (1988).10.1063/1.99889Google Scholar