Photoluminescence properties of BaGdB9O16:Tb3+ codoped Zn2+ or Ce3+ under ultraviolet and vacuum ultraviolet excitation

Published online by Cambridge University Press:  03 March 2011

Yu Hua Wang  and
Xiao Xia Li
Yu Hua Wang*
Affiliation:
Department of Materials Science, School of Physical Science and Technology, Lanzhou University, Lanzhou 730000, People’s Republic of China
Xiao Xia Li
Affiliation:
Department of Materials Science, School of Physical Science and Technology, Lanzhou University, Lanzhou 730000, People’s Republic of China
*
a) Address all correspondence to this author. e-mail: wyh@lzu.edu.cn
Get access

Abstract

Single phase of Ba1−xZnxGd0.75Tb0.25B9O16 and BaGd0.75−xCexTb0.25B9O16 (0 ≤ x ≤ 0.125) was prepared by the solid-state reaction. Under 254 nm excitation, Zn2+ impaired the emission of Tb3+; Ce3+ sensitized the luminescence of Tb3+ ascribing to the energy transfer of Ce3+ → Tb3+ and/or Ce3+ → Gd3+ → Tb3+ occurring, and the optimum emission was observed at x = 0.05 in BaGd0.75−xCexTb0.25B9O16. Under 147 nm excitation, Zn2+ sensitized the emission of Tb3+ and the optimum emission was obtained at x = 0.075 in Ba1−xZnxGd0.75Tb0.25B9O16, which could be due to the fact that the energy absorption relating to Zn2+ occurred and the absorbed energy was transferred to Tb3+ finally; Ce3+ depressed the luminescence of Tb3+, which could be attributed to the fact that Ce3+ has no absorption in vacuum ultraviolet region and the role of Gd3+ was weakened. Compared with BaGd0.75Tb0.25B9O16 and the commercial phosphor Zn2SiO4:Mn2+, the optimum phosphor Ba0.925Zn0.075Gd0.75Tb0.25B9O16 exhibited about 127% and 51% integrated emission intensity respectively and the shorter decay time of about 2.822 ms under 147 nm excitation.

Keywords

Luminescence
Type
Articles
Information
Journal of Materials Research , Volume 22 , Issue 1 , January 2007 , pp. 238 - 243
Copyright
Copyright © Materials Research Society 2007

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1Morell, A. and Khiati, N.E.: Green phosphors for large plasma TV screens. J. Electrochem. Soc. 140, 2019 (1993).CrossRefGoogle Scholar
2Mayolet, A., Zhang, W., Martin, P., Chassiqneux, B., and Krupa, J.C.: The intermediate role of the Gd3+ ions in the efficiency of the host-sensitized luminescence in the lanthanum metaborate host lattice. J. Electrochem. Soc. 143, 330 (1996).CrossRefGoogle Scholar
3Park, W., Summers, C.J., Do, Y.R., and Yang, H.G.: Photoluminescence properties of red emitting BaGdB9O16:Eu phosphor. J. Mater. Sci. 37, 4041 (2002).CrossRefGoogle Scholar
4Tian, F.W., Fouassier, C., and Hagenmuller, P.: Luminescence of Eu3+ and Eu2+ in the new BaLnB9O16 borates (Ln = rare earth). Mater. Res. Bull. 22, 899 (1987).CrossRefGoogle Scholar
5Tian, F.W., Fouassier, C., and Hagenmuller, P.: Luminescence properties of Ce3+ and Tb3+ in a new family of boron-rich alkaline earth rare earth borates. Mater. Res. Bull. 22, 389 (1987).Google Scholar
6You, H.P., Wu, X.Y., Zeng, X.Q., Hong, G.Y., Kim, C-H., Pyun, C-H., and Park, C-H.: Infrared spectra and VUV excitation properties of BaLnB9O16:Re (Ln = La, Gd; Re = Eu, Tb). Mater. Sci. Eng., B 86, 11 (2001).CrossRefGoogle Scholar
7Wang, Y.H. and Li, X.X.: Synthesis of BaGd1- x Tbx B9O16 (0.05 < x ≤ 0.35) and its photoluminescence under VUV excitation. Opt. Mater. (accepted).Google Scholar
8Lin, C.K., Yu, M., Pang, M.L., and Lin, J.: Photoluminescent properties of sol-gel derived (La,Gd)MgB5O10:Ce3+/Tb3+ nanocrystalline thin films. Opt. Mater. 28, 913 (2006).CrossRefGoogle Scholar
9Jia, P.Y., Yu, M., and Lin, J.: Sol-gel deposition and luminescent properties of LaMgAl11O19:Ce3+/Tb3+ phosphor films. J. Solid State Chem. 178, 2734 (2005).CrossRefGoogle Scholar
10Blasse, G. and Bril, A.: Energy transfer in Tb3+-activated cerium (III) compounds. J. Chem. Phys. 51, 3252 (1969).CrossRefGoogle Scholar
11Bourcet, J-C. and Fong, F.K.: Quantum efficiency of diffusion limited energy transfer in La1−x−yCexTbyPO4. J. Chem. Phys. 60, 34 (1974).CrossRefGoogle Scholar
12Mishra, K.C., Johnson, K.H., DeBoer, B.G., Berkowitz, J.K., Olsen, J., and Dale, E.A.: First principles investigation of electronic structure and associated properties of zinc orthosilicate phosphors. J. Lumin. 47, 197 (1991).CrossRefGoogle Scholar
13Shen, C.F., Ximen, L.L., and Zong, X.F.: Investigation of a new phosphor host, BaLaB9O16 by AEM and XRD. Mater. Res. Bull. 24, 1223 (1989).CrossRefGoogle Scholar
14Yang, Z., Lin, J.H., and Su, M.Z.: Structural and luminescent properties of LnBaB9O16:Eu3+ (Ln = La, Y). Chemical Journal of Chinese University 20, 1832 (1999).Google Scholar
15Krupa, J.C. and Queffelec, M.: UV and VUV optical excitations in wide band gap materials doped with rare earth ions: 4f–5d transitions. J. Alloys Compd. 250, 287 (1997).CrossRefGoogle Scholar
16Liang, H.B., Tao, Y., Xu, J.H., He, H., Wu, H., Chen, W.X., Wang, S.B., and Su, Q.: Photoluminescence of Ce3+, Pr3+ and Tb3+ activated Sr3Ln(PO4)3 under VUV-UV excitation. J. Solid State Chem. 177, 901 (2004).CrossRefGoogle Scholar
17Tsuboi, T.: Absorption spectra due to the 4f7 → 4f7 transitions of Gd3+ in GdAl3(BO3)4 crystals. J. Phys.: Condens. Matter. 10, 9155 (1998).Google Scholar
18Zhou, D., He, D.W., Liang, Z.Y., and Hou, T.: Vacuum ultraviolet optical properties of MO–Y2O3–B2O3:Re (M = Mg, Sr; Re = Eu, Tb, Ce, Gd). J. Lumin. 122–123, 993 (2007).CrossRefGoogle Scholar
19Howe, B. and Diaz, A.L.: Characterization of host-lattice emission and energy transfer in BaMgAl10O17:Eu2+. J. Lumin. 109, 51 (2004).CrossRefGoogle Scholar
20Dawson, B., Ferfuson, M., Marking, G., and Diaz, A.L.: Mechanisms of VUV damage in BaMgAl10O17:Eu2+. Chem. Mater. 16, 5311 (2004).CrossRefGoogle Scholar
21Kang, Y.C., Lim, M.A., Park, H.D., and Han, M.: Ba2+ Co-doped Zn2SiO4:Mn phosphor particles prepared by spray pyrolysis process. J. Electrochem. Soc. 150, H7 (2003).CrossRefGoogle Scholar
22Sohn, K-S., Park, E.S., Kim, C.H., and Park, H.D.: Photoluminescence behavior of BaAl12O19:Mn phosphor prepared by pseudocombinatorial chemistry method. J. Electrochem. Soc. 147, 4368 (2000).CrossRefGoogle Scholar