Temperature Dependence of Deformation Behaviour and Dislocation Structure of Al67Mn8Ti25 L12, Intermetallic Alloy

Published online by Cambridge University Press:  01 January 1992

Xiaohua Wu ,
Shipu Chen ,
Yonghua Rong ,
Xiaofu Chen  and
Gengxiang Hu
Xiaohua Wu
Affiliation:
Department of Materials Science, Shanghai Jiao Tong University, Shanghai 200030, China
Shipu Chen
Affiliation:
Department of Materials Science, Shanghai Jiao Tong University, Shanghai 200030, China
Yonghua Rong
Affiliation:
Department of Materials Science, Shanghai Jiao Tong University, Shanghai 200030, China
Xiaofu Chen
Affiliation:
Department of Materials Science, Shanghai Jiao Tong University, Shanghai 200030, China
Gengxiang Hu
Affiliation:
Department of Materials Science, Shanghai Jiao Tong University, Shanghai 200030, China
Get access

Abstract

The Al3Ti-based L12 alloy Al67Mn8Ti25 shows different temperature dependence of the yield stress and ductility from that of the model L12 alloy Ni3Al. The dislocation structures and dissociation modes of the alloy deformed at room temperature, 673 and 873K were investigated by TEM. It is determined that at room-temperature and 673K, a<110> dislocation dissociated into two a/3<112> superpartials with SISF between them on {111} plane, while at 873K, the dissociation is a/2<110> pairs on {111} planes separated by APB. The temperature dependence of yield stress and ductility may be related to the dislocation structures at various temperatures.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 288: Symposium L – High-Temperature Ordered Intermetallic Alloys V , 1992 , 605
Copyright
Copyright © Materials Research Society 1995

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1. Kumar, K.S. and Brown, S.A., Phil. Mag. A 65, 91 (1992)Google Scholar
2. Chen, Xiaofu, Wu, Xiaohua, Chen, Shipu and Hu, Gengxiang, Scripta Metall et Mater. 26, 1775 (1992)Google Scholar
3. Kumar, K.S. and Pickens, J.R., Scripta Metall 22, 1015 (1988)Google Scholar
4. Zhang, S., Nic, J.P., Milligan, W.W. and Mikkola, D.E., Scripta Metall 24, 1441 (1990)Google Scholar
5. Wu, Z.L., Pope, D.P. and Vitek, V. in High-Temperature Ordered Intermetallic Alloys, edited by Johnson, L., Pope, D.P. and Stiegler, J.O. (Mater. Res. Soc. Symp. Proc. 213, Pittsburgh, PA, 1991) pp.487 Google Scholar
6. Brown, S.A., Kumar, K.S., Scripta Metall 24, 2001 (1990)Google Scholar
7. Vasudevan, V.K. Wheeler, R. and Fraser, H.L. in High-Temperature Ordered Intermetallic Alloys, edited by Liu, C.T., Taub, A.I., Stoloff, N.S. and Koch, C.C. (Mater. Res. Soc. Symp. Proc. 133, Pittsburgh, PA, 1989) pp.705 Google Scholar
8. Tuner, C.D., Powers, W.O. and Wert, J.A., Acta Metall 37, 2635 (1989)Google Scholar
9. Lerf, R. and Morris, D.G., Acta Metall 39, 2419 (1991)Google Scholar
10. George, E.P., Horton, J.A., Porter, W.D. and Schneibel, J.H., J. Mater. Res. 5, 1639 (1990)Google Scholar
11. Inoue, H.R.P., Cooper, C.V., Favrow, L.H., Hamada, Y, and Wayman, C.M. in High-Temperature Ordered Intermetallic Alloys, edited by Johnson, L., Pope, D.P. and Stiegler, J.O. (Mater. Res. Soc. Symp. Proc. 213, Pittsburgh, PA, 1991) pp.493 Google Scholar
12. Morris, D.G., J. Mater. Res. 7, 303 (1992)Google Scholar
13. Gengxiang, Hu, Shipu, Chen, Xiaohua, Wu and Xiaofu, Chen, J. Mater. Res. 6, 957 (1991)Google Scholar
14. Inui, H., Luzzi, D.E., Porters, W.D., Pope, D.P., Vitek, V. and Yamaguchi, M., Phil. Mag. A. 65, 1245 (1992)Google Scholar
15. Vitek, V., Sodani, Y. and Cserti, J. in High-Temperature Ordered Intermetallic Alloys, edited by Johnson, L., Pope, D.P. and Stiegler, J.O. (Mater. Res. Soc. Symp. Proc. 213, Pittsburgh, PA, 1991) pp.195 Google Scholar