Characterization and catalytic properties of a saponite clay modified by acid activation

Published online by Cambridge University Press:  09 July 2018

F. Kooli  and
W. Jones
F. Kooli
Affiliation:
Department of Chemistry, University of Cambridge, Lensfield Road, Cambridge CB2 1EW, UK
W. Jones*
Affiliation:
Department of Chemistry, University of Cambridge, Lensfield Road, Cambridge CB2 1EW, UK
*
2Author for correspondence.
Get access Rights & Permissions [Opens in a new window]

Abstract

A natural saponite was acid activated at room temperature or 90°C with different acid/clay ratios and the products were characterized by powder X-ray diffraction, infrared spectroscopy and thermogravimetry. The leaching of Mg from the octahedral sheets is enhanced by an increase in the acid/clay ratio and by an increase in temperature of activation. Textural properties are reported, and it appears that they are strongly correlated to the presence of a noncrystalline silica phase which is formed during the acid activation process. The desorption of cyclohexylamine indicates that for samples activated at 90°C the number of acid sites in the acidactivated saponites decreases following severe acid treatment. Infrared spectroscopy of adsorbed pyridine on samples after calcination at 500°C suggests that acid activation at 90°C produces a single type of Bronsted site but two types of Lewis sites whereas activation at room temperature results in only one type of Lewis site in addition to a Brønsted site. The two Lewis sites are suggested to originate from residual Al in the clay structure and to AI exsolved from the layers during activation. The dehydration of pentan-1-ol has been used as a further probe to measure acidity by monitoring the degree of conversion and selectivity for the different samples.

Type
Research Article
Information
Clay Minerals , Volume 32 , Issue 4 , December 1997 , pp. 633 - 643
Copyright
Copyright © The Mineralogical Society of Great Britain and Ireland 1997

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

Footnotes

1

Present address: NIRIM, 1-1 Namiki, Tsukuba, 305 Japan

References

Bagshaw, S.A. & Cooney, R.P. (1993) FTIR surface sites analysis of pillared clays using pyridine probe species. Chem. Mater. 5, 1101–1109.CrossRefGoogle Scholar
Ballantine, J.A., Davies, M., Patel, I., Purnell, J.H., Rayanakorn, M. & Williams, K.J. (1984) Organic reactions catalysed by sheet silicates: Ether formation by the intermolecular dehydration of alcohols and by addition of alcohols to alkenes. J. Mol. Catal. 26, 37–56.CrossRefGoogle Scholar
Ballivet, D., Barthomeuf, D. & Pichat, P. (1972) Acidic sites on silica-alumina catalysts with reduced aluminium content. J. Chem. Soc. Faraday Trans. I, 68, 1712–1719.CrossRefGoogle Scholar
Bovey, J. & Jones, W. (1995) Characterization of Al-pillared acid activated clay catalysts. J. Mater Chem. 5, 2027–2035.CrossRefGoogle Scholar
Bovey, J., Kooli, F. & Jones, W. (1996) Preparation and characterization of Ti-pillared acid-activated clay catalysts. Clay Miner. 31, 491–504.CrossRefGoogle Scholar
Breen, C. (1991) Thermogravimetrie study of the desorption of cyclohexylamine and pyridine from an acid-treated Wyoming bentonite. Clay Miner. 26, 473–486.CrossRefGoogle Scholar
Breen, C., Madejova, J. & Komadel, P. (1995) Characterization of moderately acid-treated, sizefractionated montmorillonites using IR and NMRspectroscopy and thermal analysis. J. Mater. Chem. 5, 469–474.CrossRefGoogle Scholar
Chevalier, S., Franck, R., Lambert, J. F., Barthomeuf, D. & Suquet, H. (1994) Characterization of the porous structure and cracking activity of Al-pillared sapohires. AppL Catal. A: General, 110, 153–165.CrossRefGoogle Scholar
Connerton, J., Joyner, R.W. & Padley, M.B. (1995) Characterization of the acidity of well defined Cu- ZSM-5 catalysts using pyridine as a probe molecule. J. Chem. Soc. Faraday Trans. 91, 1841–1844.CrossRefGoogle Scholar
Corma, A., Mifsud, A. & Perez, J. (1986) Etude cinetique de l'attaque acide de la sepiolite: Modification des proprietes texturales. Clay Miner. 21, 69–84.CrossRefGoogle Scholar
Corma, A., Mifsud, A. & Sanz, E. (1990) Kinetics of the acid leaching of palygorskite: influence of the octahedral sheet composition. Clay Miner. 25, 197–205.CrossRefGoogle Scholar
Fahn, R. & Fended, K. (1983) Reaction-products of organic-dye molecules with acid-treated montmorillonite. Clay Miner. 18, 447–458.CrossRefGoogle Scholar
Farmer, V.C. (1974) Layered silicates. Pp. 331-363 in: Infrared Spectra of Minerals (Farmer, V.C., editor). Mineralogical Society, London.CrossRefGoogle Scholar
Frenkel, M. (1974) Surface acidity of montmorillonites. Clays Clay Miner. 22, 435–441.CrossRefGoogle Scholar
Gonzalez, L., lbarra, D.A. & Rodriguez, J.S. (1989) Structural and textural evolution of Al- and Mg-rich palygorskites, I. Under acid treatment. Appl. Clay Sci. 4, 373–388.CrossRefGoogle Scholar
Hirokawa, A. (1980) Characteristics and application of acid-treated ‘acid clay’. Nendo Kagaku, 20, 99–106.Google Scholar
Janek, M. & Komadel, P. (1993) Autotransformation of H-smectites in aqueous solution. The effect of octahedral iron content. Geol. Carpath. Ser. Clays 44, 59–64.Google Scholar
Jiang, M. & Karge, H.G. (1995) FTIR study of the kinetics of solid-state ion exchange in zeolites using pyridine as a probe. J. Chem. Soe. Faraday Trans. 91, 1845–1851.CrossRefGoogle Scholar
Kaviratna, H. & Pinnavaia, T.J. (1994) Acid hydrolysis of octahedral Mg2+ sites in 2:1 layered silicates: an assessment of edge attack and gallery access mechanisms. Clays Clay Miner. 42, 717–723.CrossRefGoogle Scholar
Komadel, P., Schmidt, D., Madejova, J. & Cicel, B. (1990) Alteration of smectites by treatments with hydrochloric acid and sodium carbonate solutions. Appl. Clay Sci. 5, 113–122.CrossRefGoogle Scholar
Komadel, P., Madejova, J., Janek, M., Gates, W.P., Kirkpatrick, R.G. & Stucki, J.W. (1996) Dissolution of hectorite in inorganic acids. Clays Clay Miner. 44, 228–236.CrossRefGoogle Scholar
Kooli, F. & Jones, W. (1997) Pillared acid-activated saponite clays. Chem. Mater. (in press).Google Scholar
Lefrançois, M. & Malbois, G. (1971) The nature of the acidic sites on mordenite. Characterization of adsorbed pyridine and water by infrared study. J. Catal. 20, 350–358.CrossRefGoogle Scholar
Lopez Gonzalez, J.D., Ramirez Saenz, A., Rodriguez Reinoso, F., Valenzue la Calahorro, C. & Zurita Herrera, L. (1981) Activacion de una sepiolita con disoluciones diluidas de NOaH y posteriores tratamientos termicos. I. Estudio de la superficia especifica. Clay Miner. 16, 103–113.CrossRefGoogle Scholar
Mackenzie, R.C. (1970) Simple phyllosilicates based on gibbsite and brucite-like sheets. Pp. 497-537 in: Differential Thermal Analysis. Vol. I (Mackenzie, R.C., editor) Academic Press, London.Google Scholar
Malla, P.B. & Komarneni, S. (1993) Properties and characterization of Al2O3 and SiO2-TiO2 pillared saponite. Clays Clay Miner. 41, 472–483.CrossRefGoogle Scholar
Martin, C., Martin, I., del Moral, C. & Rives, V. (1994) Changes in the structure of TiO2-supported molybdena induced by Na-doping. J. Catal. 146, 415–421.Google Scholar
Mendioroz, S., Pajares, J.A., Pesquera, C., Gonzalez, F. & Blanco, C. (1987) Texture evolution of montmorillonite under progressive acid treatment: Change from H-3 to H-2 type of hysteresis. Langmuir, 3, 676–681.CrossRefGoogle Scholar
Mokaya, R., Jones, W., Davies, M.E. & Whittle, M.E. (1993) Chlorophyll adsorption by alumina pillared acid-activated clay. J. Am. Oil Chem. Soc. 70, 241–244.CrossRefGoogle Scholar
Mokaya, R. & Jones, W. (1994) Pillared acid-activated clay catalysts. 3. Chem. Soc. Chem. Commun. 8, 929–930.CrossRefGoogle Scholar
Mokaya, R. & Jones, W. (1995) Pillared clays and pillared acid-activated clays: A comparative study of physical, acidic and catalytic properties. J. Catal. 153, 76–85.CrossRefGoogle Scholar
Morgan, D.A., Shaw, D.B., Sidebottom, M.J., Soon, T.C. & Taylor, R.S. (1985) The function of bleaching earths in the processing of palm, palm kernel and coconut oils. J. Am. Oil Chem. Soc. 62, 292–299.CrossRefGoogle Scholar
Parry, E.P. (1963) An infrared study of pyridine adsorbed on acidic solids. Characterization of surface acidity. J. Catal. 2, 371–379.CrossRefGoogle Scholar
Post, J.L. (1984) Saponite from near Ballarat, California. Clays Clay Miner. 32, 147–153.CrossRefGoogle Scholar
Rhodes, C.N. & Brown, D.R. (1992) Structural characterization and optimization of acid-treated montmorillonite and high porosity silica supports for ZnCl2 alkylation catalysts. J. Chem. Soc. Faraday Trans. 88, 2269–2274.CrossRefGoogle Scholar
Rhodes, C.N. & Brown, D.R. (1994) Catalytic activity of acid-treated montmorillonite in polar and non polar media. Catal. Lett. 24, 285–291.CrossRefGoogle Scholar
Suquet, H., Chevalier, S., Marcilly, C. & Barthomeuf, D. (1991) Preparation of porous materials by chemical activation of the Llano vermiculite. Clay Miner. 26, 49–60.CrossRefGoogle Scholar
Taylor, D.R. & Jenkins, D.B. (1988) Acid activated clays. Trans. Soc. Min. Eng. 282, 1901–1910.Google Scholar
Urabe, K., Sakumi, H. & Izumi, Y. (1986) Pillared synthetic saponite as an efficient alkylation catalyst. J. Chem. Soc. Chem. Commun. 1074-1075.CrossRefGoogle Scholar
Vicente, M.A., Suarez, M., Lopez Gonzalez, J.D. & Banaras Munoz, M.A. (1996) Characterization, surface area and porosity analyses of the solids obtained by acid leaching of a saponite. Langmuir 12, 566–572.CrossRefGoogle Scholar
Vicente Rodriguez, M.A., Suarez Barrios, M., Lopez Gonzalez, J.D. & Banares Munoz, M.A. (1994) Acid activation of a ferrous saponite (Griffithite): Physico-chemical characterization and surface area of the products obtained. Clays Clay Miner. 42, 724–730.CrossRefGoogle Scholar