Samples from Russia and Scotland are used to examine the interaction of the REE-Ti silicate chevkinite-(Ce) with hydrothermal fluids. Altered zones in crystals are distinguished by using areas of low intensity on backscattered-electron images, low analytical totals, increasingly large departures from stoichiometry and, in some cases, the presence of micropores. Initial alteration of the chevkinite results in strong Ca enrichment. With increasing degrees of alteration, Ca abundances drop sharply, as do those of the REE, Fe and Si. In contrast, Ti levels increase strongly, usually accompanied by higher Nb ± Th levels. The most altered zones contain up to 36 wt.% TiO2 and the formula cannot be expressed in the standard chevkinite formula. In detail, samples follow different alteration trends, presumably reflecting different P, T, fO2 and fluid composition. The Ti enrichment may have been related to a reaction front of dissolution-reprecipitation passing through the outer zones of the original chevkinite, leaving behind a reprecipitated Ti-enriched phase which may or may not be chevkinite.

Chevkinite-(Ce) in a mineralized quartz-epidote metasomatite from the Keivy massif, Kola Peninsula, Russia, underwent at least two stages of low-temperature alteration. In the first, it interacted with hydrothermal fluids, with loss of Ca, Fe, LREE and Si and strong enrichment in Ti. The altered chevkinite was then rimmed and partially replaced by a zone of ferriallanite-(Ce) and davidite-(La), in turn rimmed by a zone of allanite-(Ce) richer in the epidote component. The allanite zone was in turn partially replaced by rutile-titanite-quartz assemblages, the formation of titanite postdating that of rutile. Aeschynite-(Y), aeschynite-(Ce) and REE-carbonates are accessory phases in all zones. The hydrothermal fluids were alkaline, with significant proportions of CO2 and F. At various alteration stages, the Ca, Si ± Al activities in the fluid were high. Formation of the aeschynite is discussed in relation to its stability in broadly similar parageneses; it was a primary phase in the unaltered chevkinite zone whereas in other zones it formed from Nb, Ti, REE and Th released from the major phases.

The new mineral nabimusaite, KCa12(SiO4)4(SO4)2O2F (R3m, a = 7.1905(4), c = 41.251(3) Å, V = 1847.1(2) Å3, Z = 3), has been discovered in larnite-ye' elimite nodules of pyrometamorphic rocks of the Hatrurim Complex. Nabimusaite is colourless, transparent with a white streak, has a vitreous lustre and does not show luminescence. It is brittle, but shows pronounced parting and imperfect cleavage along (001). Nabimusaite is uniaxial (–), ω = 1.644(2), ε = 1.640(2) (589 nm), nonpleochroic, Mohs' hardness is ∼5 and the calculated density is 3.119 g cm–3. The crystal structure has been solved and refined to R1 = 0.0416. Its artificial analogue is known. The nabimusaite structure may be derived from that of hatrurite, also known as the clinker phase 'alite' (C3S = Ca3SiO5), and is built up by an intercalation of three positively charged hatrurite-like modules of composition [Ca12(SiO4)4O2F]3+ with inserted modules of [K(SO4)2]3–. The hatrurite-like modules in nabimusaite are characterized by octahedrally coordinated anion sites and tetrahedrally coordinated cation sites. The structure is representative of the intercalated antiperovskite type. In contrast to its synthetic analogue, nabimusaite is P-bearing. The shortened bond T–O lengths for one tetrahedral site indicates P preference at the Si2 site, located at the border of the hatrurite-like modules. Significant variations of isomorphous substitutions in nabimusaite suggest the possibility of other isostructural minerals occurring in Nature. It also seems likely that nabimusaite could serve as a prototype for new advanced synthetic materials, given the discovery of two other new minerals in the Hatrurim Complex with related modular structures, placed in the nabimusaite group. These are zadovite and aradite, as described in a companion paper (Galuskin et al., 2015a).

The mineral assemblage and paragenesis of nabimusaite suggests that nabimusaite formed as a result of the reaction of potassium-enriched, sulfate-bearing melt with larnite and ellestadite. This contradicts the isochemical model that pyrometamorphic rocks of the Hatrurim Complex formed relatively fast in a practically dry system.

Zadovite, BaCa6[(SiO4)(PO4)](PO4)2F (R3m, a = 7.0966(1) Å, c = 25.7284(3), V = 1122.13(3) Å3, Z = 3) and aradite, BaCa6[(SiO4)(VO4)] (VO4)2F (R3m, a = 7.1300(1), c = 26.2033(9) Å, V = 1153.63(6) Å3, Z = 3) are two new mineral species of a novel modular structure type related closely to the structure of nabimusaite, KCa12(SiO4)4(SO4)2O2F. Both minerals occur in paralavas enclosed in pyrometamorphic rocks of the Hatrurim Complex, Negev desert, Israel. Zadovite and aradite are colourless, transparent with a white streak, have a vitreous lustre and an uneven fracture. Both minerals are uniaxial (–) with refractive indices (589 nm) ω = 1.711(2), ε = 1.708(2) (zadovite) and ω = 1.784(3), ε = 1.780(3) (aradite). The zadovite structure type comprises two tetrahedral sites, which may host a broad compositional range of atoms such as Si, P, V and S. Results of electron microprobe analyses show a correlation between excess Si4+ and S6+ contents, suggesting the substitution scheme 2(P,V)5+ = Si4+ + S6+ at the tetrahedral sites. This points to the possibility of new minerals isostructural with zadovite with end-member formulae BaCa6(SiO4)2[(PO4)(SO4)]F, BaCa6(SiO4)2[(VO4)(SO4)]F, BaCa6[(SiO4)1.5(SO4)0.5](PO4)2F and BaCa6[(SiO4)1.5(SO4)0.5](VO4)2F. The Raman spectra of aradite and zadovite reflect the varying PO4 (e.g. change of band intensity at ∼1031 cm–1) and VO4 contents (e.g. change of band intensity at ∼835 cm–1). The presence of SO4 leads to an additional Raman band at ∼997 cm–1. The structure of zadovite-series minerals belonging to the nabimusaite group is characterized by a 1:1 alternation of antiperovskite-like {[FCa6](TO4)2}4+ modules and Ba(TO4)2–4 modules.

The new mineral species ralphcannonite, AgZn2TlAs2S6, was discovered in the Lengenbach quarry, Binn Valley, Wallis, Switzerland. It occurs as metallic black equant, isometric to prismatic crystals, up to 50 μm, associated with dufrénoysite, hatchite, realgar and baryte. Minimum and maximum reflectance data for COM wavelengths in air are [λ (nm): R (%)]: 471.1: 25.8/27.1; 548.3: 25.2/26.6; 586.6: 24.6/25.8; 652.3: 23.9/24.8. Electron microprobe analyses give (wt.%): Cu 2.01(6), Ag 8.50(16), Zn 10.94(20), Fe 3.25(8), Hg 7.92(12), Tl 24.58(26), As 18.36(19), Sb 0.17(4), S 24.03(21), total 99.76(71). On the basis of 12 atoms per formula unit, the chemical formula of ralphcannonite is Ag0.63(2)Cu0.25(2)Zn1.35(5)Fe0.47(1)Hg0.32(2)Tl0.97(3)[As1.97(6)Sb0.01(1)]Σ1.98(5)S6.03(8). The new mineral is tetragonal, space group I42m, with a = 9.861 (2), c = 11.125(3) Å, V = 1081.8(4) Å3, Z = 4. The main diffraction lines of the calculated powder diagram are [d (in Å), intensity, hkl]: 4.100, 85, 211; 3.471, 40, 103; 2.954, 100, 222; 2.465, 24, 400; 2.460, 39, 303. The crystal structure of ralphcannonite has been refined by X-ray single-crystal data to a final R1 = 0.030, on the basis of 140 observed reflections [Fo > 4σ(Fo)]. It shows a three dimensional framework of (Ag,Zn)-centred tetrahedra (1 M1 + 2 M2), with channels parallel to [001] hosting TlS6 and (As,Sb)S3 disymmetric polyhedra. Ralphcannonite is derived from its isotype routhierite M1CuM2Hg2TlAs2S6 through the double heterovalent substitution M1Cu+ + M2Hg2+ → M1Zn2+ + M2Ag+. This substitution obeys a steric constraint, with Ag+, the largest cation relative to Zn2+ and Cu+, entering the largest M2 site, as observed in arsiccioite. The ideal crystal-chemical formula of ralphcannonite is M1ZnM2(Zn0.5Ag0.5)2TlAs2S6.

We have characterized the crystal structure of natural kutinaite, a rare mineral from the ores of Černý Důl, Czech Republic, by single-crystal X-ray diffraction and chemical analysis. We found that the structure of natural kutinaite is not identical to that of synthetic Cu14Ag6As7, previously reported to be cubic, space group Pm3m. Although topologically similar, the structure of natural kutinaite is indeed tetragonal, space group P4/mmm, with cell parameters: a = 11.789(2), c = 11.766(2) Å, V = 1635.5(4) Å3 and Z = 4. Electron microprobe analyses pointed to the (K,Tl)0.25Cu14Ag6As6.75 stoichiometry (Z = 4), or (K, Tl)Cu56Ag24As27 with Z = 16. The crystal structure of an untwinned crystal has been refined to R1 = 2.61%. It consists of clusters of eight edge-sharing tetrahedra of Cu, which alternate in a 3D chess-board manner with octahedral clusters of six Ag atoms. The latter are surrounded by triangularly coordinated copper in eight faces of a cuboctahedron. The last structure components are large cavities containing partly occupied (K,Tl) sites, coordinated by 18 Ag and As ligands. The structure is full of direct metal-metal contacts although As plays the role of anion, associating especially with copper.

The new oxalate mineral antipinite is found in a guano deposit located on the Pabellón de Pica Mountain, Iquique Province, Tarapacá Region, Chile. Associated minerals are halite, salammoniac, chanabayaite, joanneumite and clays. Antipinite occurs as blue, imperfect, short prismatic crystals up to 0.1 mm × 0.1 mm × 0.15 mm in size, as well as their clusters and random aggregates. The mineral is brittle. Mohs hardness is 2; Dmeas = 2.53(3), Dcalc = 2.549 g cm–3. The infrared spectrum shows the presence of oxalate anions and the absence of absorptions associated with H2O molecules, C–H bonds, CO32–, NO3– and OH– ions. Antipinite is optically biaxial (+), α = 1.432(3), β = 1.530(1), γ = 1.698(5), 2Vmeas = 75(10)°, 2Vcalc = 82°. The chemical composition (electron-microprobe data, C measured by gas chromatography of products of ignition at 1200°C, wt.%) is Na2O 15.95, K2O 5.65, CuO 27.34, C2O3 48.64, total 99.58. The empirical formula is K0.96Na3.04Cu2.03(C2.00O4)4 and the idealized formula is KNa3Cu2(C2O4)4. The crystal structure was solved and refined to R = 0.033 based upon 4085 unique reflections with I > 2σ(I). Antipinite is triclinic, space group P1, a = 7.1574(5), b = 10.7099(8), c = 11.1320(8) Å, α = 113.093(1), β = 101.294(1), γ = 90.335 (1)°, V = 766.51(3) Å3, Z = 2. The strongest reflections of the powder X-ray diffraction pattern [d, Å (I,%) (hkl)] are 5.22 (40) (111), 3.47 (100) (032), 3.39 (80) (210), 3.01 (30) (033, 220), 2.543 (40) (122, 034, 104), 2.481 (30) (213), 2.315 (30) (143, 310), 1.629 (30) (146, 414, 243, 160).

The new minerals fermiite (IMA2014-068), Na4(UO2)(SO4)3·3H2O and oppenheimerite (IMA2014-073), Na2(UO2)(SO4)2·3H2O, were found in the Blue Lizard mine, San Juan County, Utah, USA, where they occur together as secondary alteration phases in association with blödite, bluelizardite, chalcanthite, epsomite, gypsum, hexahydrite, kröhnkite, manganoblödite, sideronatrite, tamarugite and wetherillite.

Fermiite descriptive details: pale greenish-yellow prisms; transparent; vitreous lustre; bright greenishwhite fluorescence; white streak; hardness (Mohs) 2½; brittle; conchoidal fracture; no cleavage; slightly deliquescent; easily soluble in RT H2O; densitymeas = 3.23(2) g cm–3; densitycalc = 3.313 g cm–3. Optically, biaxial (+), α = 1.527(1), β = 1.534(1), γ = 1.567(1) (white light); 2Vmeas. = 51(1)°, 2Vcalc. = 50°; dispersion r < v, distinct. Pleochroism: X, Y = colourless, Z = pale greenish yellow; X = Y < Z. Energy dispersive spectroscopic (EDS) analyses yielded the empirical formula Na3.88(U1.05O2)(S0.99O4)3(H2O)3. Fermiite is orthorhombic, Pmn21, a = 11.8407(12), b = 7.8695(5), c = 15.3255(19) Å, V = 1428.0(2) Å3 and Z = 4. The structure (R1 = 2.21% for 1951 Io > 3σI) contains [(UO2)(SO4)3] chains that are linked by bonds involving five different Na–O polyhedra to form a framework. The mineral is named for Italian-American theoretical and experimental physicist Dr. Enrico Fermi (1901–1954).

Oppenheimerite descriptive details: pale greenish-yellow prisms; transparent; vitreous lustre; bright greenish-white fluorescence; white streak; hardness (Mohs) 2½; slightly sectile; three good cleavages, {110}, {011} and {101}; irregular fracture; slightly deliquescent; easily soluble in RT H2O; densitycalc = 3.360 g cm–3. Optically, biaxial (+), α = 1.537(1), β = 1.555(1), γ = 1.594(1) (white light); 2Vmeas. = 72(2)°, 2Vcalc. = 70°; dispersion is r > v, moderate, inclined; optical orientation: X ≈ ⊥ {101}, Z ≈ [111]; pleochroism: X very pale greenish yellow, Y pale greenish yellow, Z greenish yellow; X < Y < Z. EDS analyses yielded the empirical formula Na1.94(U0.97O2)(S1.02O4)2(H2O)3. Oppenheimerite is triclinic, P1, a = 7.9576(6), b = 8.1952(6), c = 9.8051(7) Å, α = 65.967(5), β = 70.281(5), γ = 84.516(6)°, V = 549.10(8) Å3 and Z = 2. The structure (R1 = 3.07% for 2337 Io > 3σI) contains [(UO2)(SO4)2(H2O)] chains that are linked by bonds involving two different Na–O polyhedra to form a framework. The mineral is named for American theoretical physicist Dr. J. Robert Oppenheimer (1904–1967).

Pilawite-(Y), ideally Ca2(Y,Yb)2Al4(SiO4)4O2(OH)2, was discovered in a pegmatite near Piława Górna, Lower Silesia, Poland. The mineral occurs as white, translucent, brittle crystals up to 1.5 mm in size. It has a white streak, vitreous lustre and a hardness of 5 on Mohs scale. The calculated density is 4.007 g/cm3. Pilawite-(Y) is non-pleochroic, biaxial (+), with refractive indices α = 1.743(5), β = 1.754(5) and γ = 1.779(5), birefringence Δ = 0.03–0.04, 2Vmeas. = 65(2)° and 2Vcalc. = 68°. Pilawite-(Y) is monoclinic P21/c, with unit-cell parameters a = 8.558(3) Å, b = 7.260(3) Å, c = 11.182(6) Å, β = 90.61(4)o, V = 694.7(4) Å3. The crystal structure was refined to an R1 index of 2.76% and consists of chains of edge- and corner-sharing octahedra decorated by tetrahedra and having the stoichiometry [Al2(SiO4)4O(OH)] that link by sharing corners to form an octahedron–tetrahedron framework with large interstices that contain Ca2+ and (Y,Ln)3+. It is a graphical isomer of the Al–P framework in palermoite, Sr2Li4[Al2(PO4)2(OH)2]2. The pilawite-(Y)-bearing assemblage began crystallization at high Y + Ln activities and was modified progressively by a Ca-enriched fluid, resulting in the sequence: keiviite-(Y) → gadolinite-(Y) to hingganite-(Y) + hellandite-(Y) → pilawite-(Y) → allanite-(Y) → epidote/zoisite.

The crystal structure of the mineral koninckite was solved from synchrotron powder X-ray diffraction (XRD) data and refined using density-functional theory (DFT) calculations. Koninckite is tetragonal, with the space group P41212, a = 11.9800(5) Å, c = 14.618(1) Å, V = 2097.9(2) Å3, Z = 8. Its structure is a heteropolyhedral framework with zeolite-like tunnels along [001]. Owing to the severe peak overlap in the powder XRD data and the probable intergrowth of enantiomorphic domains in koninckite, the DFT calculations were applied to provide precise atomic positions (including hydrogen). Additionally, the DFT calculations suggest strongly that koninckite is an antiferromagnetic semiconductor, at least at low temperatures. The DFT computations were used to locate H2O molecules in the channels and to complete the structural description. Thermogravimetric analysis and powder XRD data at variable temperatures show that the structure of koninckite dehydrates and eventually collapses between 160–180°C. Negative thermal expansion was observed between 80 and 150°C. A list of the known occurrences of koninckite suggests that this mineral is not as rare as assumed previously; koninckite is often fine-grained, inconspicuous, and thereby easy to overlook. Koninckite is yet another natural example of an Fe-phosphate zeolitic material.

Flurlite, ideally Zn3Mn2+Fe3+(PO4)3(OH)2·9H2O, is a new mineral from the Hagendorf-Süd pegmatite, Hagendorf, Oberpfalz, Bavaria, Germany. Flurlite occurs as ultrathin (<1 μm) translucent platelets that form characteristic twisted accordion-like aggregates. The colour varies from bright orange red to dark maroon red. Cleavage is perfect parallel to (001). The mineral occurs on mitridatite and is closely associated with plimerite. Other associated minerals are beraunite, schoonerite, parascholzite, robertsite and altered phosphophyllite. The calculated density of flurlite is 2.84 g cm–3. It is optically biaxial (–), α = 1.60(1), β= 1.65(1) and γ = 1.68(1), with weak dispersion and parallel extinction, X ≈ c, Y ≈ a, Z ≈ b. Pleochroism is weak, with colours: X = pale yellow, Y = pale orange, Z = orange brown. Electron microprobe analyses (average of seven) with FeO and Fe2O3 apportioned and H2O calculated on structural grounds, gave ZnO 25.4, MnO 5.28, MgO 0.52, FeO 7.40, Fe2O3 10.3, P2O5 27.2, H2O 23.1, total 99.2 wt.%. The empirical formula, based on 3 P a.p.f.u. is Zn2.5Mn2+0.6Fe2+0.8Mg0.1Fe3+(PO4)3(OH)2·9H2O. Flurlite is monoclinic, P21/m, with the unit-cell parameters (at 100 K) of a = 6.3710(13), b = 11.020(2), c = 13.016(3) Å, β = 99.34 (3)°. The strongest lines in the X-ray powder diffraction pattern are [dobs in Å(I) (hkl)] 12.900(100)(001); 8.375(10)(011); 6.072(14)(101); 5.567(8)(012); 4.297(21)(003); 2.763(35)(040). Flurlite (R1 = 0.057 for 995 F > 4σ(F)) has a heteropolyhedral layer structure, with layers parallel to (001) and with water molecules packing between the layers. The slab-like layers contain two types of polyhedral chains running parallel to [100]: (a) chains of edge-sharing octahedra containing predominantly Zn and (b) chains in which Fe3+-centred octahedra share their apices with dimers comprising Zn-centred trigonal bipyramids sharing an edge with PO4 tetrahedra. The two types of chains are interconnected by corner-sharing along [010]. A second type of PO4 tetrahedron connects the chains to MnO2(H2O)4 octahedra along [010] to complete the structure of the (001) slabs. Flurlite has the same stoichiometry as schoonerite, but with dominant Zn rather than Fe2+ in the edge-shared chains. Schoonerite has a similar heteropolyhedral layer structure with the same layer dimensions 6.4 × 11.1 Å. The different symmetry (orthorhombic, Pmab) for schoonerite reflects a different topology of the layers.

Microcrystals of platinum-group element (PGE)-bearing cobaltite occur in the Gulcari A deposit of vanadiferous titanomagnetite in the lower zone of the Rio Jacaré mafic-ultramafic layered intrusion, Brazil. Aggregates of cobaltite and sperrylite are cluster-like and developed generally along the boundary of Fe-Ti oxide grains with deuteric silicates. Our observations of cryptic zoning, compositional variability and interelement correlations are based on 37 analytical points (wavelength-dispersion spectrometry mode) of cobaltite, and indicate that Ir and Rh behave uniformly with Ni and antipathetically with Co which, in turn, correlates directly with S content. Iridium, Rh and Ni apparently substitute for Co in the As-enriched grain core, and the substitution mechanism invokes solid solution with a cattierite-type molecule: (Ni + Ir + Rh) + (AsS) = Co + (S2). The PGE-bearing cobaltite probably crystallized as a primary phase at 500 to 300°C, from microvolumes of a late fluid phase. The observed enrichment in S and decrease in the As:S ratio at the cobaltite grain margins is a reflection of the increase in sulfur fugacity (fS2) with decrease in temperature of crystallization.

Minjiangite, ideally BaBe2(PO4)2, is a new mineral species which has been found in the Nanping No. 31 pegmatite, Fujian Province, southeastern China. It occurs in the fractures of montebrasite from pegmatite zone IV, and is associated with quartz, muscovite, hydroxylapatite and palermoite. Minjiangite forms subhedral to euhedral white crystals from 5 to 200 μm long, transparent to translucent, with a vitreous lustre. The estimated Mohs hardness is ∼6, the tenacity is brittle and no cleavage was observed. The calculated density is 3.49 g/cm3. Optically, minjiangite is uniaxial (+), with ω = 1.587(3), ε = 1.602(2) (λ = 589 nm). Electron-microprobe analyses (average of 8) give P2O5 40.16, BaO 43.01, BeO 14.06 (measured by Secondary Ion Mass Spectrometry), SiO2 0.17, CaO 0.17, SrO 0.08, FeO 0.03, MgO 0.01, TiO2 0.07, K2O 0.05, Na2O 0.11, total 97.92 wt.%. The empirical formula, calculated on the basis of 8 O a.p.f.u., is (Ba0.99Ca0.01Na0.01)Σ1.01Be1.98(P1.99Si0.01)Σ2.00O8. The powder X-ray diffraction (XRD) pattern of minjiangite perfectly fits that of synthetic BaBe2(PO4)2; the strongest eight lines of the powder XRD pattern of the natural phosphate [d in Å (I)(hkl)] are: 3.763(100)(101); 2.836(81.3)(102); 2.515(32.3)(110); 2.178(25.6)(200); 2.1620(19)(103); 2.090(63.9)(201); 1.770(16.2)(113); 1.507(25.4)(212). Unit-cell parameters, refined from the powder XRD pattern of natural minjiangite, are a = 5.030(8), c = 7.467 (2) Å, V = 163.96(3) Å3. These unit-cell parameters confirm that minjiangite is the natural analogue of synthetic BaBe2(PO4)2(P6/mmm, a = 5.029(1), c = 7.466 (1) Å, V = 163.52(1) Å3, Z = 1); its crystal structure is topologically similar to that of dmisteinbergite, CaAl2Si2O8, a hexagonal polymorph of anorthite. The formation of minjiangite is related to the hydrothermal alteration of montebrasite by late Ba- and Be-rich fluids.

Yeomanite, Pb2O(OH)Cl, is a new Pb-oxychloride found in the manganese pod mineral assemblage at Merehead (Torr Works) Quarry, near Cranmore, Somerset, England. Yeomanite is named in joint recognition of Mrs Angela Yeoman (1931–) and her company, Foster Yeoman, who operated Merehead Quarry for aggregate until 2006. The mineral is normally white, occasionally grey, with a white streak and a vitreous to transparent lustre. Invariably intimately associated with mendipite, yeomanite appears to be formed of small, twisted, rope-like fibres growing from the end of columnar mendipite masses, forming loose mats and strands resembling asbestos. Individual fibres are generally <8 mm long, but exceptionally may reach up to 15 mm. There is a perfect cleavage parallel to the long axis of the fibres but this is masked by the fibrous nature, especially as individual fibres break easily. The Dcalc for the ideal formula is 7.303 g/cm3. The mean RI in air at 589 nm is 2.27. The eight strongest reflections in the powder X-ray diffraction pattern [(d in Å) (Intensity) (hkl)] are: 2.880(100)(113); 2.802(78)(006); 3.293(61)(200); 3.770(32)(011); 2.166(22)(206); 1.662(19)(119); 2.050(18)(303); 3.054(17)(105) Yeomanite is orthorhombic, Pnma, a = 6.585(10), b = 3.855(6), c = 17.26(1) Å, V = 438(1) Å3, Z = 4. Yeomanite is a new example of the growing family of lead oxychloride minerals that have a structure based upon oxocentred OPb4 tetrahedra, which, in this mineral, jointly with OHPb3 triangles, form [O(OH)Pb2]+ chains similar to those observed in synthetic Pb2O(OH)I. Yeomanite is structurally related to sidpietersite, penfieldite and laurionite.

The determination of the crystal structure of benleonardite (P3m1; R = 0.0321 for 1250 reflections and 102 parameters; refined formula Ag15.00Cu1.00Sb1.58As0.42S7.03Te3.97) obtained using data from a gem-quality, untwinned crystal recovered from the type material, revealed that benleonardite exhibits the structure observed for minerals of the pearceite-polybasite group. The structure consists of the stacking of [Ag6(Sb,As)2S6Te]2– A and [Ag9Cu(S,Te)2Te2]2+B layer modules in which (Sb, As) forms isolated SbS3 pyramids typically occurring in sulfosalts; Cu links two (S,Te) atoms with linear coordination, and Ag occupies sites with coordination geometries ranging from quasi-linear to almost triangular. The silver ions are found in the B layer module along two-dimensional diffusion paths and their electron densities are evidenced by means of a combination of a Gram-Charlier development of the atom displacement factors and a split model. In the structure, two S positions are completely replaced by Te (i.e. Te3 and Te4) and one is half occupied [S1: S0.514(9)Te0.486], whereas S2 is completely filled by sulfur. This distribution reflects the crystal-chemical environments of the different cations. On the basis of information gained from this characterization, the crystal-chemical formula of benleonardite was revised according to the structural results, yielding Ag15Cu(Sb,As)2S7Te4 (Z = 1) instead of Ag8(Sb,As)Te2S3(Z = 2) as previously reported. Thus, the mineral must be considered a member of the pearceite-polybasite group. A recalculation of the chemical data listed in the scientific literature for benleonardite according to the structural results obtained here leads to excellent agreement.

Anzaite-(Ce), ideally Ce43+Fe2+Ti6O18(OH)2, is a new, structurally complex mineral occurring as scarce minute crystals in hydrothermally altered silicocarbonatites in the Afrikanda alkali-ultramafic complex of the Kola Peninsula, Russia. The mineral is a late hydrothermal phase associated with titanite, hibschite, clinochlore and calcite replacing the primary magmatic paragenesis. The rare-earth elements (REE) (dominated by Ce), Ti and Fe incorporated in anzaite-(Ce) were derived from primary Ti oxides abundant in the host rock. Anzaite-(Ce) is brittle and lacks cleavage; the density calculated on the basis of structural data is 5.054(6) g cm–3. The mineral is opaque and grey with a bluish hue in reflected light; its reflectance values range from 15–16% at 440 nm to 13–14% at 700 nm. Its infrared spectrum shows a prominent absorption band at 3475 cm–1 indicative of OH– groups. The average chemical composition of anzaite-(Ce) gives the following empirical formula calculated on the basis of 18 oxygen atoms and two OH– groups: (Ce2.18Nd0.85La0.41Pr0.26Sm0.08Ca0.36Th0.01)Σ4.15Fe0.97(Ti5.68Nb0.22Si0.04)Σ5.94O18(OH)2. The mineral is monoclinic, space group C2/m, a = 5.290(2), b = 14.575(6), c = 5.234(2) Å, β = 97.233(7)°, V = 400.4(5) Å3, Z = 1. The ten strongest lines in the X-ray micro-diffraction pattern are [dobs in Å (I)hkl]: 2.596 (100) 002; 1.935 (18) 170; 1.506 (14) 133; 1.286 (13) 1.11.0; 2.046 (12) 241; 1.730 (12) 003; 1.272 (12) 0.10.2; 3.814 (11) 111; 2.206 (9) 061; 1.518 (9) 172. The structure of anzaite-(Ce), refined by single-crystal techniques to R1 = 2.1%, consists of alternating layers of type 1, populated by REE (+ minor Ca) in a square antiprismatic coordination and octahedrally coordinated Fe2+, and type 2, built of five-coordinate and octahedral Ti, stacked parallel to (001). This atomic arrangement is complicated by significant disorder affecting the Fe2+, five-coordinate Ti and two of the four anion sites. The order-disorder pattern is such that only one half of these positions in total occupy any given (010) plane, and the disordered (010) planes are separated by ordered domains comprising REE, octahedral Ti and two anion sites occupied by O2–. Structural and stoichiometric relations between anzaite-(Ce) and other REE-Ti (±Nb, Ta) oxides are discussed. The name anzaite-(Ce) is in honour of Anatoly N. Zaitsev of St Petersburg State University (Russia) and The Natural History Museum (UK), in recognition of his contribution to the study of carbonatites and REE minerals. The modifier reflects the prevalence of Ce over other REE in the composition of the new mineral.