Rutile nanoparticles have been synthesized by acid hydrolysis of titanium isopropoxide by low-temperature dissolution-reprecipitation process. High-resolution transmission electron micrographs of the rutile colloidal solution show needle-shaped rutile nanoparticles with the dimensions of 10–30 nm in diameter and 100–150 nm in length. X-ray diffraction (XRD) data show the existence of only the rutile polymorph in TiO2 powder with a crystallite size of 11.3 nm. The dielectric constant of rutile nanoparticles has been found to be 57 at 10 MHz AC frequency and DC conductance as 2.3 × 10−6 S/cm. Transmission electron micrographs and XRD data analysis imply that the rutile crystallites are self-organized in a regular fashion to produce multilayer three-dimensional linear clusters. The clusters have been found to be microporous (average porosity 1.4 nm) with high specific surface area (132.2 m2/g). At higher concentration, the clusters aggregate to produce interconnected network of star- or flower-like structures. This organized crystalline microporous metal-oxide semiconductor might find various practical applications.

The liquid phase plasma reduction method has been applied to prepare silver nanoparticles from a solution of silver nitrate (AgNO3) using a bipolar pulsed electrical discharge system. The excited states of atomic silver, hydrogen and oxygen as well as the molecular bands of hydroxyl radicals were detected in the emission spectra. As the discharge duration increased up to 10 min, silver particle peaks produced by surface plasmon absorption were observed around 430 nm. Both the particle size and the particle numbers were observed to increase with the length of the plasma treatment time and with the initial AgNO3 concentration. Spherical nanoparticles of about 5–20 nm in size were obtained with the discharging time of 5 min, whereas aggregates of nanoparticles of about 10–50 nm in size were mainly produced with the discharging time of 20 min. The cationic surfactant of cetyltrimethylammonium bromide (CTAB) added with the CTAB/AgNO3 molar ratio of 30% was shown to inhibit nanoparticle aggregation.

The ultraviolet (UV) color-color relation of early-type galaxies (ETGs) in the nearby universe (0.05 < z < 0.12) is re-examined with the latest GALEX GR6 and SDSS DR7 data. By drawing the FUV – NUV (as a measure of UV temperature) versus FUV – r (as a measure of UV amplitude) color-color diagram for the morphologically-cleaned, spectroscopically-cleaned sample of ~3700 quiescent ETGs, we find that the “old and dead“ ETGs consist of a well-defined sequence in UV colors, the “UV red sequence”, so that the stronger UV excess galaxies should have a harder UV spectral shape systematically. However, the observed UV spectral slope is too steep to be reproduced by the canonical models in which the UV flux is mainly controlled by age or metallicity parameters. The observed data support the helium enhancement scenario in which the UV spectral shape of UV upturn (FUV – NUV < 0.9; FUV – r ~ 6) galaxies may be governed by the minority population of helium-enhanced horizontal-branch (HB) stars.

The purpose of this study was to investigate whether there is any association between preeclampsia and eNOS, DDAH, and VEGF gene polymorphisms, and also to search for a possible association between haplotypes in eNOS, DDHA, and VEGF genes and the risk for preeclampsia. DNA was extracted from whole blood of 223 preeclampsia patients and 237 healthy pregnant women. The genotypes were analyzed by a single base primer extension assay using a SNaPShot assay kit. Results were analyzed with the Student's t-test, Chi-square test, and Logistic regression analysis. Haplotype analyses were performed using Haploview 3.2 version. There were no significant differences in genotype or allele frequencies of eNOS, DDAH, and VEGF gene polymorphisms between preeclampsia patients and controls. No increase in the risk of preeclampsia for those genes was observed under any model of inheritance and there were no statistically significant associations between any haplotypes and preeclampsia risk. Polymorphisms in eNOS, DDAH, and VEGF gene do not seem to be risk factors for preeclampsia.

Despite numerous previous studies, relationships between watershed land use and adjacent streams and rivers at various scales in Korea remain unclear. This study investigated the relationships between land uses and the physical, chemical, and biological characteristics of 720 sites of streams and rivers across the country. The land uses at two spatial scales, including a 1-km buffer and the base watershed management region (BWMR), were computed in a geographical information system (GIS) with a digital land use/land cover map. Characteristics of land uses at two spatial scales were then correlated with the monitored multidimensional characteristics of the streams and rivers. The results of this study indicate that land use types have significant effects on stream and river characteristics. Specifically, most characteristics were negatively correlated with the proportions of urban, rice paddy, agricultural, and bare soil areas and positively correlated with the amount of forest. The site-scale and BWMR-scale analyses suggest that BWMR land use patterns were more strongly related to ecological integrity than they were to site land use patterns. Improving our understanding of land use effects will largely depend on relating the results of site-specific studies that use similar response techniques and measures to evaluate ecological integrity. In addition, our results clearly indicate that the characteristics of streams and rivers are closely linked and that land use types differentially affect those characteristics. Thus, effective restoration and management for ecological integrity of lotic system should consider the physical, chemical, and biological factors in combination.

To enhance the lifetime of large-sized active matrix organic light emitting diodes (AMOLEDs), we developed a liquid desiccant for encapsulation. The liquid desiccant was prepared by mixing nano-sized calcium oxide (CaO) powders and silicone binder including polyalkylalkenylsiloxane, polyalkylhydrogensiloxane and platinum compound. It was confirmed that liquid desiccant had an effect on absorption of penetrated moisture and oxygen through calcium tests. Also, the test cells encapsulated with only epoxy sealant dispensed at the edge of the cell developed dark spots within 100 hrs, which grew larger with time at 85 oC and 85 % R.H. On the other hand, the test cell sealed with epoxy sealant and liquid desiccant showed no dark spots and retained 97% of its initial luminance even after being stored for 800 hrs at 85 oC and 85 % R.H. Furthermore, the accelerating storage lifetimes of 31-inch bottom-emitting AMOLEDs with epoxy sealant and liquid desiccant showed about 1000 hrs. These results suggest that the liquid desiccant can be applied to encapsulation of large-sized AMOLEDs.

The globular cluster system in M31 is an ideal laboratory for studying the formation and evolution of M31 as well as the globular clusters themselves. There have been numerous surveys and studies of the globular clusters in M31. However, only recently has the entire body of M31 been searched for globular clusters using wide-field CCD images by our group. A new era for the M31 globular cluster system has begun with the advent of wide-field CCD surveys of M31. We have discovered more than 100 new globular clusters in M31. Our catalog currently includes more than 500 globular clusters confirmed either based on spectra or HST images, many more than in the Milky Way. We present the structure, kinematics and chemical abundance of the M31 globular cluster system based on this large sample, and the implications for the formation and evolution of M31.

A systematic study on the effect of sputtering deposition parameters on material properties of Al doped ZnO (ZnO:Al) films prepared by an in-line rf magnetron sputtering and on surface morphology of the films after wet etching process was carried out. For application to silicon thin film solar cells as a front electrode, the as-deposited films were surface-textured by a dilute HCl solution to improve the light scattering properties such as haze and angle resolved distribution of scattered light on the film surfaces. The microstructure of as-deposited films is affected significantly by the working pressure and film compactness decreases with increasing working pressure from 1.5 mTorr to 10 mTorr. High quality ZnO:Al films with electrical resistivity of 4.25 × 10-4 Ω cm and optical transmittance of 80% in a visible range are obtained at low working pressure of 1.5 mTorr and substrate temperature of 100℃. Crater-like surface morphologies are observed on the textured ZnO:Al films after wet etching. The size and shape of craters are closely dependent on the microstructure and film compactness of as-deposited films. Haze values of the textured ZnO:Al films are improved in a whole wavelength of 300 – 1100 nm compared to commercial SnO2:F films (Asahi U type) and incident light on the textured films is scattered effectively with 30° angle.

We synthesized bulk amorphous alloy systems of Cu43Zr43Al7X7 (X = Be, Ag; numbers indicate at.%), with the objective of simultaneously enhancing the glass-forming ability (GFA) and the plasticity. The alloys not only exhibit high plasticity (∼7%, ∼8%), but also possess enhanced GFA (alloys with 12 and 8 mm diameter). The possible mechanisms underlying this enhanced GFA and plasticity exhibited by these alloys are discussed based on the atomic-packing state and atomistic-scale compositional separation associated with the mixing enthalpy difference. A strategy for designing bulk amorphous alloys with simultaneous improvement in the GFA and the plasticity is proposed from the viewpoint of atomic-packing state and atomistic-scale phase separation.