The type specimen of liskeardite, (Al, Fe)3AsO4(OH)6·5H2O, from the Marke Valley Mine, Liskeard District, Cornwall, has been reinvestigated. The revised composition from electron microprobe analyses and structure refinement is [Al29.2Fe2.8(AsO4)18(OH)42(H2O)22]·52H2O. The crystal structure was determined using synchrotron data collected on a 2 μm diameter fibre at 100 K. Liskeardite has monoclinic symmetry, space group I2, with the unit-cell parameters a = 24.576(5), b = 7.754(2) Å, c = 24.641(5) Å, and β = 90.19(1)º. The structure was refined to R = 0.059 for 9769 reflections with I > 3σ(I). It is of an open framework type in which intersecting polyhedral slabs parallel to (101) and (10) form 17.4 Å × 17.4 Å channels along [010], with water molecules occupying the channels. Small amounts (<1 wt.%) of Na, K and Cu are probably adsorbed at the channel walls The framework comprises columns of pharmacoalumite-type, intergrown with chiral chains of six cis edge-shared octahedra. It can be described in terms of cubic close packing, with vacancies at both the anion and cation sites. The compositional and structural relationships between liskeardite and pharmacoalumite are discussed and a possible mechanism for liskeardite formation is presented.

Weissite, Cu2–xTe (x ≈ 0.21), a very rare copper telluride, occurs in a sample from the Gambatesa mine, Val Graveglia, Liguria, Italy, where it occurs as purplish black anhedral grains up to 0.1 mm in length and shows a black streak. No cleavage is observed and the Vickers hardness (VHN100) is 142 kg/mm2. Weissite is dark bluish black, weakly pleochroic, and moderately anisotropic in bluish tints. Reflectance percentages in air for Rmin and Rmax are 37.0, 38.4 (471.1 nm), 33.2, 34.2 (548.3 nm), 31.2, 32.1 (586.6 nm), and 28.6, 31.0 (652.3 nm), respectively.

Weissite is trigonal and belongs to the space group P3m1 with the following unit-cell parameters: a = 8.3124(7) Å, c = 21.546(1) Å, V = 1289.3(2) Å3, and Z = 24. Electron microprobe analyses gave the chemical formula (Cu1.62Ag0.04Au0.04Fe0.04Sb0.04)Σ=1.78(Te0.96S0.02Se0.02). The crystal structure has been solved and refined to R = 1.95%. It consists of Cu and Te polyhedra forming complex crystal-chemical environments as is typical of many intermetallic compounds. The exceedingly short bond distances observed among the metals are discussed in relation to other copper tellurides and pure metals.

Meisserite (IMA2013-039), Na5(UO2)(SO4)3(SO3OH)(H2O), is a new uranyl sulfate mineral from the Blue Lizard mine, San Juan County, Utah (USA). It is named in honour of the prominent Swiss mineralogist Nicolas Meisser. The new mineral was found in a sandstone matrix and is associated with chalcanthite, copiapite, ferrinatrite, gypsum, johannite and another new Na-bearing uranyl sulfate, belakovskiite (IMA2013-075). Meisserite is a secondary mineral formed by the post-mining weathering of uraninite. The mineral is triclinic, P, a = 5.32317(10), b = 11.5105(2), c = 13.5562(10) Å, α = 102.864(7)°, β = 97.414(7)°, γ = 91.461(6)°, V = 801.74(6) Å3, and Z = 2. Crystals are prisms elongated on [100], up to 0.3 mm long, exhibiting the forms {010} and {001}. Meisserite is pale green to yellowish green, translucent to transparent and has a very pale yellow streak. It is brittle, with fair cleavage on {100} and {001}, and uneven fracture. The Mohs hardness is estimated at 2. Meisserite is somewhat hygroscopic and easily soluble in water. The calculated density based on the empirical formula is 3.208 g/cm3. Meisserite exhibits bright yellow green fluorescence under both long- and shortwave UV radiation. The mineral is optically biaxial (–), with α = 1.514(1), β = 1.546(1), γ = 1.557(1) (measured in white light). The measured 2V is 60(2)° and the calculated 2V is 60°. Dispersion is r > v, perceptible, and the optical orientation is X ≈ a, Z ≈ c*. The mineral is pleochroic, with X (colourless) < Y (pale yellow) ≈ Z (pale greenish yellow). The empirical formula of meisserite (based on 19 O a.p.f.u.) is Na5.05(U0.94O2)(SO4)3[SO2.69(OH)1.31](H2O). The Raman spectrum is dominated by the symmetric stretching vibrations of UO22+, SO42– and also weaker O–H stretching vibrations. The eight strongest powder X-ray diffraction lines are [dobs in Å (hkl)Irel]: 13.15 (001) 81, 6.33 (02) 62, 5.64 (01,020) 52, 5.24 (100,012,01) 100, 4.67 (101) 68, 3.849 (1,102,022) 48, 3.614 (02,3) 41, and 3.293 (13,004) 43. The crystal structure of meisserite (R1 = 0.018 for 3306 reflections with Iobs > 3σI) is topologically unique among known structures of uranyl minerals and inorganic compounds. It contains uranyl pentagonal bipyramids linked by SO4 groups to form chains. Na+ cations bond to O atoms in the chains and to an SO3OH group and an H2>O group between the chains, thereby forming a heteropolyhedral framework.

This study is the first to investigate the mineral composition of the atmospheric particulate matter deposited at Rio Tinto, Spain, an historical mining district of world-class importance, with emphasis on metal-bearing particles and their environmental implications. The dustfall is composed of quartz, feldspars, phyllosilicates (mica, chlorite and/or kaolinite) and a variety of accessory heavy minerals, the most common being primary sulfides (pyrite, chalcopyrite with minor galena, sphalerite and bornite) and their oxidation products (notably goethite, hematite and jarosite). This mineral assemblage suggests a local source of wind-blown dust and it is consistent with the large deposition levels of sulfide-related elements (As, Bi, Cd, Cu, Pb, Sb and Zn) registered at the sampling site adjacent to the mine waste dumps. However, the generation of potentially harmful dust particles is not restricted to mine wastes. Anthropogenic metallic compounds arising from a nearby hazardous waste disposal centre can make a relevant additional contribution to the metal deposition, particularly for Fe, Ni, Cr and Mn. Atmospheric fallout is a major mechanism for metal input to soils and plants around or near the mining area.

The ideal formula for members of the cerchiaraite group is Ba4M4(Si4O12)O2(OH)4Cl2[Si2O3(OH)4], where M represents Mn3+, Fe3+ or Al in the octahedral site. A suffix-based naming scheme is used in which the original cerchiaraite is renamed cerchiaraite-(Mn) and two new minerals are named cerchiaraite-(Fe) and cerchiaraite-(Al). The type localities for cerchiaraite-(Fe) are the Cerchiara mine, Liguria, Italy and the Esquire No. 7 and No. 8 claims, Big Creek, Fresno County, California, USA. The type localities for cerchiaraite-(Al) are the Esquire No. 1 claim, Rush Creek, Fresno County, California, USA and the Esquire No. 7 and No. 8 claims noted above. At the Cerchiara mine, cerchiaraite-(Fe) occurs in small fractures and veinlets in a Jurassic ophiolitic sequence. It is of secondary hydrothermal origin and occurs as tan to brown thin prisms and matted fibres. Cerchiaraite(Fe) and cerchiaraite-(Al) from the Esquire No. 1, No. 7 and No. 8 claims occur in parallel-bedded quartz-sanbornite vein assemblages which formed as a result of fluid interaction along the margin of the vein. At the Esquire No. 1, No. 7 and No. 8 claims, both cerchiaraite-(Fe) and cerchiaraite-(Al) occur as subparallel aggregates of blue to bluish green irregular prisms. Both minerals are transparent with a vitreous lustre, Mohs hardness ~4½ , brittle tenacity, irregular fracture and no cleavage. The calculated density of cerchiaraite-(Fe) is 3.710 g cm-3; the measured density of cerchiaraite-(Al) is 3.69(3) g cm-3and the calculated density is 3.643 g cm-3. Cerchiaraite-(Fe) is uniaxial (+), with ω = 1.741(2) and ε = 1.768(2); it is weakly pleochroic and O is colourless and E is yellow. Cerchiaraite-(Al) is uniaxial (-), with ω = 1.695(2) and e = 1.677(2); it is strongly pleochroic and O is colourless and E is blue. Electron-microprobe analyses yielded empirical formulae ranging from (Ba3.82Na0.02Ca0.04)Σ3.88(Fe3+3.42Ti4+0.27Al3+0.25Mn3+0.04Mg0.02)Σ4.00Si5.62O15.47(OH)9.31Cl2.22 (Cerchiara mine) to Ba4.00(Al3+2.40Fe3+1.12Mg0.15Fe2+0.12Mn2+0.06)Σ3.85Si5.78O15.34(OH)8.75Cl2.91 (Esquire No. 1 claim). Cerchiaraite is tetragonal with Z = 2 and crystallizes in space group I4/mmm. The cell parameters for cerchiaraite-(Fe) are a = 14.3554(12), c = 6.0065(5) Å and V = 1237.80(5) Å3; those for cerchiaraite(Al) are a = 14.317(4), c = 6.0037(18) Å and V = 1230.6(6) Å3. In the cerchiaraite-(Fe) structure, SiO4 tetrahedra share corners forming a four-membered Si4O12 ring. The ring is corner-linked to an edgesharing chain of Fe3+ O6 octahedra running parallel to c. A Cl site alternates along c with the Si4 O12 ring. A large channel in the framework contains Ba atoms around its periphery and statistically distributed Si2 O7 silicate dimers and Cl atoms. The strong blue pleochroic colour is attributed to Fe2+ - Fe3+intervalence charge transfer along the octahedral chain.

Minohlite, a new copper-zinc sulfate mineral related to schulenbergite, was found in the oxidized zone of the Hirao mine at Minoh (Minoo) City, Osaka Prefecture, Japan. The mineral occurs in cracks in altered shale as rosette aggregates up to 100 m m in diameter, composed of hexagonal platy crystals up to 50 μm m in diameter and 10 μm m in thickness. The associated minerals are chamosite, muscovite, smithsonite, serpierite, ramsbeckite, 'limonite' and chalcopyrite. Minohlite has hexagonal (or trigonal) symmetry with unit-cell parameters of a = 8.2535(11), c = 8.1352(17) Å, V = 479.93(16) Å3 and Z = 1, and possible space groups P6, P, P6/m, P22, P6mm, P2m and P6/mmm (or P3, P3, P321, P3m1, Pm1, P312, P31m and P1m). The six strongest reflections in the powder X-ray diffraction pattern [d in Å (I) hkl] are 8.138 (20) 001; 4.128 (24) 110; 2.702 (100) 120; 2.564 (76) 121; 1.560 (43) 140; and 1.532 (24) 141. Electron microprobe analyses gave the following values (wt.%): CuO 37.18, ZnO 21.08, FeO 0.49, SO3 16.78, SiO2 0.44, and H2O 24.03 (by difference). The empirical formula, calculated on the basis of Cu + Zn + Fe + S + Si = 9 atoms per formula unit, is (Cu4.43Zn2.45Fe0.06)Σ6.94[(SO4)1.99(SiO4)0.07]Σ2.06(OH)9.64·7.81H2O, which leads a simplified formula of (Cu,Zn)7(SO4)2(OH)10·8H2O where Cu > Zn. The mineral is bluish-green and transparent with a pearly to vitreous lustre. The streak is pale green. Cleavage is perfect on {001}. The Mohs hardness number is less than 2. The calculated density is 3.28 g cm−3. The mineral is named after Minoh City, where it was discovered.

Bobmeyerite, Pb4(Al3Cu)(Si4 O12)(S0.5Si0.5O4)(OH)7 Cl(H2O)3, is a new mineral from the Mammoth - Saint Anthony mine, Tiger, Pinal County, Arizona, USA. It occurs in an oxidation zone assemblage attributed to progressive alteration and crystallization in a closed system. Other minerals in this assemblage include atacamite, caledonite, cerussite, connellite, diaboleite, fluorite, georgerobinsonite, hematite, leadhillite, matlockite, murdochite, phosgenite, pinalite, quartz, wulfenite and yedlinite. Bobmeyerite occurs as colourless to white or cream-coloured needles, up to 300 m m in length, that taper to sharp points. The streak is white and the lustre is adamantine, dull or silky. Bobmeyerite is not fluorescent. The hardness could not be determined, the tenacity is brittle and no cleavage was observed. The calculated density is 4.381 g cm-3. Bobmeyerite is biaxial (-) with α ≈ β = 1.759(2), γ = 1.756(2) (white light), it is not pleochroic; the orientation is X = c; Y or Z = a or b. Electron-microprobe analyses provided the empirical formula Pb3.80Ca0.04Al3.04Cu2+0.96Cr3+0.13Si4.40S0.58O24.43Cl1.05F0.52H11.83. Bobmeyerite is orthorhombic (pseudotetragonal), Pnnm with unit-cell parameters a = 13.969(9), b = 14.243(10), c = 5.893(4) Å, V = 1172.5(1.4) Å3 and Z = 2. The nine strongest lines in the X-ray powder diffraction pattern, listed as [dobs (Å)(I)(hkl)], are as follows: 10.051(35)(110); 5.474(54)(011,101); 5.011(35)(220); 4.333(43)(121,211); 3.545(34)(040,400); 3.278(77)(330,231,321); 2.9656(88)(141,002,411); 2.5485(93)(051,222,501); 1.873(39)(multiple). Bobmeyerite has the same structural framework as cerchiaraite and ashburtonite. In the structure, which refined to R1 = 0.079 for 1057 reflections with F > 4σF, SiO4 tetrahedra share corners to form four-membered Si4O12 rings centred on the c axis. The rings are linked by chains of edge-sharing AlO6 octahedra running parallel to [001]. The framework thereby created contains large channels, running parallel to [001]. The Cl site is centred on the c axis alternating along [001] with the Si4O12 rings. Two non-equivalent Pb atoms are positioned around the periphery of the channels. Both are elevencoordinate, bonding to the Cl atom on the c axis, to eight O atoms in the framework and to two O (H2O) sites in the channel. The Pb atoms are off-centre in these coordinations, as is typical of Pb2+ with stereo-active lone-electron pairs. A (S, Si, Cr)O4 group is presumed to be disordered in the channel. The name honours Robert (Bob) Owen Meyer, one of the discoverers of the new mineral.

The crystal chemistry of sekaninaite from Dolní Bory, Czech Republic, was characterized by a multimethod approach. Particular emphasis was put on the characterization of the channel constituents (i.e. H2O and CO2). Electron microprobe analysis shows the sample to be close to the Fe endmember [XFe = Fe/(Fe+Mg) = 94%) with significant Mn (1.48 wt.%) present; laser ablation mass-spectrometry showed the presence of 0.42 wt.% Li2O. H2O and CO2 contents (1.48 and 0.17 wt.%, respectively) were determined via secondary-ion mass-spectrometry. Sample homogeneity was checked by Fourier-transform infrared (FTIR) imaging using a microscope equipped with a focal plane array detector. Single-crystal FTIR spectroscopy confirmed the presence of two types of H2O groups in different orientations (with prevalence of the type II orientation), and that CO2 is oriented preferentially normal to the crystallographic c axis. Using the Beer-Lambert relation, integrated molar coefficients, εi, were calculated for both types of H2O (εi H2O[I] = 6000±2000; εi H2O[II] = 13000±1000) and for CO2 (εiCO2 = 2000±1000).

Fluorcalciomicrolite, (Ca, Na, ☐)2Ta2O6F, is a new microlite-group, pyrochlore supergroup mineral approved by the CNMNC (IMA 2012-036). It occurs as an accessory mineral in the Volta Grande pegmatite, Nazareno, Minas Gerais, Brazil. Associated minerals include: microcline, albite, quartz, muscovite, spodumene, “lepidolite”, cassiterite, tantalite-(Mn), monazite-(Ce), fluorite, “apatite”, beryl, “garnet” , epidote, magnetite, gahnite, zircon, “tourmaline” , bityite, hydrokenomicrolite, and other microlite-group minerals under study. Fluorcalciomicrolite occurs as euhedral, untwinned, octahedral crystals 0.1–1.5 mm in size, occasionally modified by rhombododecahedral faces. The crystals are colourless and translucent; the streak is white, and the lustre is adamantine to resinous. It does not fluoresce under ultraviolet light. Mohs' hardness is 4½–5, tenacity is brittle. Cleavage is not observed; fracture is conchoidal. The calculated density is 6.160 g/cm3. The mineral is isotropic, ncalc. = 1.992. The Raman spectrum is dominated by bands of B–X octahedral bond stretching and X–B–X bending modes. The chemical composition (n = 6) is (by wavelength dispersive spectroscopy, H2O calculated to obtain charge balance, wt.%): Na2O 4.68, CaO 11.24, MnO 0.01, SrO 0.04, BaO 0.02, SnO20.63, UO20.02, Nb2O53.47, Ta2O576.02, F 2.80, H2O 0.48, O=F–1.18, total 98.23. The empirical formula, based on 2 cations at the B site, is (Ca1.07Na0.81☐0.12)Σ2.00(Ta1.84Nb0.14Sn0.02)Σ2.00[O5.93(OH)0.07]6.00[F0.79(OH)0.21]. The strongest eight X-ray powder-diffraction lines [d in Å (I)(hkl)] are: 5.997(59)(111), 3.138(83)(311), 3.005(100)(222), 2.602(29)(400), 2.004(23)(511), 1.841(23)(440), 1.589(25)(533), and 1.504(24)(444). The crystal structure refinement (R1 = 0.0132) gave the following data: cubic, Fdm, a = 10.4191(6) Å, V = 1131.07(11) Å3, Z = 8.

Accessory rare earth element (REE) minerals occur in small quantities in agpaitic and miaskitic nepheline syenite gneisses of the Sushina Hill Complex, India. The REE-rich minerals restricted mainly to the agpaitic rocks are rinkite, cerianite-(Ce), and cerian thorite. Rinkite, formed at the ortho-magmatic stage predates other REE-rich phases and is the most Nd-F-rich rinkite (6.62–7.45 wt.% Nd2O3; 8.75–9.74 wt.% F) with very high Nd/Ce (>2.46) ratios reported to date. Hydrothermal cerianite-(Ce), formed by the decomposition of eudialyte in the agpaitic rocks, occurs as small rounded crystals rich in Ce (∼63–74 wt.% CeO2) and Y (6.03–11.69 wt.% Y2O3). The presence of cerianite-(Ce) indicates formation in an evolving hydrothermal fluid in an oxidizing milieu. Hingganite-(Ce) is present in the miaskitic unit and is considered to represent the superposition of an agpaitic mineral on an initial miaskitic assemblage. Hingganite-(Ce) is characterized by elevated contents of Ce (18.03–21.94 wt.% Ce2O3), and Nd (13.90–15.40 wt.% Nd2O3). Experimental data, coupled with the observed assemblage, suggest that the hingganite-(Ce) precipitated from the hydrothermal fluid between 400 and 300°C followed by cerianite-(Ce) (<∼300°C). This conclusion implies that eudialyte decomposition was probably initiated above 400°C.

Joteite (IMA2012-091), Ca2CuAl[AsO4][AsO3(OH)]2(OH)2·5H2O, is a new mineral from the Jote mine, Tierra Amarilla, Copiapó Province, Atacama, Chile. The mineral is a late-stage, low-temperature, secondary mineral occurring with conichalcite, mansfieldite, pharmacoalumite, pharmacosiderite and scorodite in narrow seams and vughs in the oxidized upper portion of a hydrothermal sulfide vein hosted by volcanoclastic rocks. Crystals occur as sky-blue to greenish-blue thin blades, flattened and twinned on {001}, up to ~300 μm in length, and exhibiting the forms {001}, {010}, {10}, {20} and {111}. The blades are commonly intergrown in wheat-sheaf-like bundles, less commonly in sprays, and sometimes aggregated as dense crusts and cavity linings. The mineral is transparent and has a very pale blue streak and vitreous lustre. The Mohs hardness is estimated at 2 to 3, the tenacity is brittle, and the fracture is curved. It has one perfect cleavage on {001}. The calculated density based on the empirical formula is 3.056 g/cm3. It is optically biaxial (–) with α = 1.634(1), β = 1.644(1), γ = 1.651(1) (white light), 2Vmeas = 78(2)° and 2Vcalc = 79.4°. The mineral exhibits weak dispersion, r < v. The optical orientation is X ≈ c*; Y ≈ b*. The pleochroism is Z (greenish blue) > Y (pale greenish blue) > X (colourless). The normalized electron-microprobe analyses (average of 5) provided: CaO 15.70, CuO 11.22, Al2O38.32, As2O546.62, H2O 18.14 (structure), total 100 wt.%. The empirical formula (based on 19 O a.p.f.u.) is: Ca1.98Cu1.00Al1.15As2.87H14.24O19. The mineral is slowly soluble in cold, concentrated HCl. Joteite is triclinic, P, with the cell parameters: a = 6.0530(2), b = 10.2329(3), c = 12.9112(4) Å, α = 87.572(2), β = 78.480(2), γ = 78.697(2)°, V = 768.40(4) Å3 and Z = 2. The eight strongest lines in the X-ray powder diffraction pattern are [dobs Å (I)(hkl)]: 12.76(100)(001), 5.009(23)(020), 4.206(26)(120,003,121), 3.92(24)(022,02,02), 3.40(25)(13), 3.233(19)(031,023,123,03), 2.97(132,201) and 2.91(15)(22,13). In the structure of joteite (R1 = 7.72% for 6003 Fo > 4σF), AsO4 and AsO3 (OH) tetrahedra, AlO6 octahedra and Cu2+O5 square pyramids share corners to form sheets parallel to {001}. In addition, 7- and 8-coordinate Ca polyhedra link to the periphery of the sheets yielding thick slabs. Between the slabs are unconnected AsO3(OH) tetrahedra, which link the slabs only via hydrogen bonding. The Raman spectrum shows features consistent with OH and/or H2O in multiple structural environments. The region between the slabs may host excess Al in place of some As.

The stabilities of possible Y(R3+ + R2+ + Li+) clusters around the W anion (O1 site) of the tourmaline structure were checked using the bond-valence approach. Arrangements involving R3+ = Al3+ or Fe3+ and R2+ = (Fe, Mn, Mg)2+ were all found to be stable. Structural data show a strong linear correlation between the mean formal valence (MFV) of the Y cations and the long-range average bond valence sum (BVS) at the O1 site, as estimated from bond-valence parameters. This correlation is observed for all chemical compositions of tourmaline, except for fluor-buergerite where the O3 site is dominated by oxygen anions. Results show that the long-range site populations of the Y and O1 sites are related to each other by valence constraints described by the empirical and theoretical equations: BVS(O1) = [0.99 MFV(Y) − 1.20] and MFV(O1) = [1.00 MFV(Y) − 1.00], respectively. The systematic deviation of the empirical equation from the ideal one is ascribed to the occurrence of bond strain involving the O1 site. An important implication of the correlation between MFV(Y) and BVS(O1) is that the (OH) content at the O1 site may be estimated by the equation W(OH) = 2 − [1.01 BVS(O1)] − 0.21 − F.

Shimazakiite occurs as greyish white aggregates up to 3 mm in diameter. Two polytypes, shimazakiite-4M and shimazakiite-4O, have been identified, the former in nanometre-sized twin lamellae and the latter in micrometre-sized lamellae. Shimazakiite was discovered in an irregular vein in crystalline limestone near gehlenite-spurrite skarns at Fuka mine, Okayama Prefecture, Japan. Associated minerals include takedaite, sibirskite, olshanskyite, parasibirskite, nifontovite, calcite and an uncharacterized hydrous calcium borate. The mineral is biaxial (–), with the following refractive indices (at 589 nm): α = 1.586(2), β = 1.650(2), γ = 1.667(2) and 2Vcalc = 53º [shimazakiite-4M]; and α = 1.584(2), β = 1.648(2), γ = 1.670(2) and 2Vcalc = 54.88º [shimazakiite-4O]. Quantitative electronmicroprobe analyses (means of 28 and 25 determinations) gave the empirical formulae Ca2B1.92O4.76(OH)0.24 and Ca2B1.92O4.76(OH)0.24 for shimazakiite-4M and shimazakiite-4O, respectively. The crystal structure refinements: P21/c, a = 3.5485(12), b = 6.352(2), c = 19.254(6) Å , β = 92.393(13)°, V = 433.6(3) Å3 [for shimazakiite-4M]; and P212121, a = 3.55645(8), b = 6.35194(15), c = 19.2534(5) Å , V = 434.941(18) Å3[for shimazakiite-4O], converged into R1 indices of 0.1273 and 0.0142, respectively. The crystal structure of shimazakiite consists of a layer containing B2O5 units (two near-coplanar triangular corner-sharing BO3 groups) and 6- and 7-coordinate Ca atoms. Different sequences in the c direction of four layers are observed in the polytypes. The five strongest lines in the powder-diffraction pattern [listed as d in Å (I)(hkl)] are: 3.02(84)(022); 2.92(100)(10) 2.81(56)(104); 2.76(32)(113); 1.880(32)(11,12,126,118) [for shimazakiite-4M]; and 3.84(33)(014); 3.02(42)(022); 2.86(100)(104); 2.79(29)(113); 1.903(44)(126,118) [for shimazakiite-4O].

Schlüterite-(Y), ideally (Y,REE)2Al(Si2O7)(OH)2F, is a new silicate mineral species from the Stetind pegmatite, Tysfjord, Nordland, Norway. It forms dense, fibrous, radiating aggregates (up to ∼2 mm) diverging to individual needle-like crystals (up to ∼1 mm long) in cavities. Crystals are acicular to bladed, flattened on {001} and elongated along [010], and the dominant form is {001}. Schlüterite-(Y) is transparent, pale pink with a white streak and a vitreous lustre, and does not fluoresce under short-wave ultraviolet light. Mohs hardness is 5½–6, and schlüterite-(Y) is brittle with an irregular fracture, and has no cleavage. The calculated density is 4.644 g/cm3. The indices of refraction are α = 1.755, β = 1.760, γ = 1.770, all ± 0.005, 2Vobs = 71.8 (5)°, 2Vcalc = 71°, non-pleochroic, optic orientation is X ˆ a = 83.1° (β obtuse), Y//b, Z ˆ c = 50.3° (β acute). Schlüterite-(Y) is monoclinic, space group P21/c, a 7.0722(2), b 5.6198(1), c 21.4390(4) Å, β 122.7756(3)°, V 716.43(5) Å3, Z = 4. The seven strongest lines in the X-ray powder-diffraction pattern are as follows: [d (Å), I, (hkl)]: 4.769, 100, (012); 2.972, 55, (14); 3.289, 51, (112); 2.728, 49, (16); 2.810, 37, (020); 3.013, 37, ((16); 4.507, 36, (004). Chemical analysis by electron microprobe gave SiO2 22.64, Al2O3 9.45, Y2O3 15.35, La2O3 3.25, Ce2O3 9.69, Pr2O3 2.05, Nd2O3 9.50, Sm2O3 3.57, Gd2O3 4.65, Dy2O3 4.21, Er2O3 2.31, Yb2O3 1.86, F 2.71, H2Ocalc 3.78, O = F −1.14, sum 93.88 wt%. The H2O content was determined by crystal-structure analysis. On the basis of 10 anions with (OH) + F = 3 a.p.f.u. (atoms per formula unit), the empirical formula is (Y0.73Ce0.32Nd0.30Gd0.14Dy0.12La0.11Sm0.11Pr0.07Er0.06Yb0.05)Σ=2.01Al0.99Si2.01O7(OH)2.24F0.76. The crystal structure of schlüterite-(Y) was solved by direct methods and refined to an R1 index of 1.8% based on 1422 unique observed reflections. In the structure of schlüterite-(Y), Al(OH)4O2 octahedra share (OH)–(OH) edges to form [MΦ4] chains that are decorated by (Si2O7) groups that bridge O vertices of neighbouring octahedra in a staggered fashion on either side of the chain. These [Al(OH)2(Si2O7)] chains extend parallel to b, and are linked into a continuous framework via bonds to interstitial [8](Y,REE) (= <2.400 Å>) and [9](Y,REE) (= <2.548 Å>) atoms.

Diegogattaite (IMA2012-096), Na2CaCu2Si8O20·H2O, is a new mineral from the Wessels mine in the Kalahari manganese fields of South Africa. It occurs as a minor phase with other copper-bearing silicates, Cu-rich pectolite, sugilite, quartz, aegirine and undifferentiated Fe-Mn oxides. Diegogattaite is pale turquoise through teal blue. It is found as sub-mm sized grains in a main crystalline patch 3–4 mm in size, and is currently known from only one sample. The mineral is transparent with a vitreous lustre and may have a good cleavage on {001}. It is brittle, with an uneven fracture and a very pale-blue streak. It is non-fluorescent in short- and long-wave UV light and has an estimated Mohs hardness of ∼5–6. Diegogattaite is biaxial (–), α = 1.598(2), β = 1.627(2), γ = 1.632(2); 2Vmeas = 44.0(6)°, 2Vcalc = 44.5°; dispersion: strong r < v, orientation: X = b, Y ≈ ⊥(001), Z ≈ a; pleochroism X colourless << Y ≈ Z blue green. The calculated density is 3.10 g/cm3. Electron-microprobe analysis gave: Na2O 8.07, CaO 7.3, CuO 20.5, FeO 0.36, SiO262.4, H2O(calc) 2.34, total 100.97 wt.%. A charge-balanced formula on the basis of 21 oxygen a.p.f.u. is: Na2.00Ca1.00Cu1.98Fe0.04Si7.99H2O21. Diegogattaite is monoclinic, space group C2/m, a = 12.2439(6) Å, b = 15.7514(4) Å, c = 10.6008(3) Å, β = 125.623(2)°, V = 1661.87(10) Å3 and Z = 4. The five strongest lines in the X-ray powder pattern are [dobs in Å (Iobs)(hkl)]: 4.25(75)(002,22,220), 3.951(77)(040), 3.261(100)(31,13), 2.898(89)(042,03,003), 2.332(66)(331,43,62,260,043). The crystal structure of diegogattaite was determined by single-crystal X-ray diffraction to final agreement indices of R1 = 0.027, wR2 = 0.071 and GoF = 1.090. It represents a completely new silicate topology based upon a double-sheet of SiO4 tetrahedra composed of connected 6482 cages. The structure of diegogattaite is related to those of synthetic nanoporous Na-Cu-Si-O-(OH)-H2O (CuSH) compounds, which are of interest to the solid-state chemistry community as potential ion-exchangers, catalysts and molecular sieves. The structure of diegogattaite forms a bridge between these structures and those of the gillespite-group minerals, including wesselsite. The close spatial association of wesselsite and diegogattaite suggests a possible reaction between them that may point to a synthetic route for the production of novel alkaline-earth-based nanoporous copper silicates.

Although the distinction between magnesiodumortieite and dumortierite, i.e. Mg vs. Al dominance at the partially vacant octahedral Al1 site, had met current criteria of the IMA Commission on New Minerals, Nomenclature and Classification (CNMNC) for distinguishing mineral species, the distinction between holtite and dumortierite had not, since Al and Si are dominant over Ta and (Sb, As) at the Al1 and two Si sites, respectively, in both minerals. Recent studies have revealed extensive solid solution between Al, Ti, Ta and Nb at Al1 and between Si, As and Sb at the two Si sites or nearly coincident (As, Sb) sites in dumortierite and holtite, further blurring the distinction between the two minerals.

This situation necessitated revision in the nomenclature of the dumortierite group. The newly constituted dumortierite supergroup, space group Pnma (no. 62), comprises two groups and six minerals, one of which is the first member of a potential third group, all isostructural with dumortierite. The supergroup, which has been approved by the CNMNC, is based on more specific end-member compositions for dumortierite and holtite, in which occupancy of the Al1 site is critical.

(1) Dumortierite group, with Al1 = Al3+, Mg2+ and ☐, where ☐ denotes cation vacancy. Charge balance is provided by OH substitution for O at the O2, O7 and O10 sites. In addition to dumortierite, endmember composition AlAl6BSi3O18, and magnesiodumortierite, endmember composition MgAl6BSi3O17(OH), plus three endmembers, “hydroxydumortierite”, ☐Al6BSi3O15(OH)3 and two Mg-Ti analogues of dumortierite, (Mg0.5Ti0.5)Al6BSi3O18 and (Mg0.5Ti0.5)Mg2Al4BSi3O16(OH)2, none of which correspond to mineral species. Three more hypothetical endmembers are derived by homovalent substitutions of Fe3+ for Al and Fe2+ for Mg.

(2) Holtite group, with Al1 = Ta5+, Nb5+, Ti4+ and ☐. In contrast to the dumortierite group, vacancies serve not only to balance the extra charge introduced by the incorporation of pentavalent and quadrivalent cations for trivalent cations at Al1, but also to reduce repulsion between the highly charged cations. This group includes holtite, endmember composition (Ta0.6☐0.4)Al6BSi3O18, nioboholite (2012-68), endmember composition (Nb0.6☐0.4)Al6BSi3O18, and titanoholtite (2012-69), endmember composition (Ti0.75☐0.25)Al6BSi3O18.

(3) Szklaryite (2012-70) with Al1 = ☐ and an endmember formula ☐Al6BAs3+3O15. Vacancies at Al1 are caused by loss of O at O2 and O7, which coordinate the Al1 with the Si sites, due to replacement of Si4+ by As3+ and Sb3+, and thus this mineral does not belong in either the dumortierite or the holtite group. Although szklaryite is distinguished by the mechanism introducing vacancies at the Al1 site, the primary criterion for identifying it is based on occupancy of the Si/As, Sb sites: (As3+ + Sb3+) > Si4+ consistent with the dominant-valency rule. A Sb3+ analogue to szklaryite is possible.

This paper relates an infrared (IR) (6000–2500; 1400–400 cm–1) spectroscopic study of sideronatrite, Na2Fe3+(SO4)2(OH)·3H2O. Spectra in the 600–1250 cm–1 range are dominated by fundamental S–O absorption bands. Factor-group analysis based on the space group P212121(D42) is in accordance with the observed band multiplicity. A broad and convolute absorption centred around 3400 cm–1 and a sharp band at 3605 cm–1 are observed in the 2900–3900 cm–1 frequency region. The resolution of the broad band is significantly improved at liquid nitrogen temperature; seven components can be fitted to the pattern and these can be assigned to H2O/OH molecules in the structure. All components in the broad band and the sharp absorption at 3605 cm–1 are strongly polarized for E//a, in accordance with the structure analysis results. Infrared transmission spectroscopy is a useful tool to identify these sulfate minerals occurring in specific geological environments.

A single crystal of natrojarosite, NaFe3(SO4)2(OH)6, was investigated by single-crystal X-ray diffraction at high-pressure conditions (up to 8.8 GPa) using a diamond-anvil cell. The unit-cell parameters were determined at 11 different pressures and no indications of a phase transition were found up to the maximum pressure reached. The volume and axial moduli were fitted to a third-order Birch–Murnaghan equation-of-state which gave the following values: V0 = 769.6(2) Å3, KT0 = 50.6(9) GPa, K' = 9.9(4); a = 7.3172(6) Å, KT0 = 104(2), K' = 7.6(9); c = 16.5965(20) Å, KT0 = 24.6(4) and K' = 7.1(2). The crystal structure of natrojarosite was refined at seven different pressures up to 8.779(11) GPa [a = 7.3170(4), c = 16.5955(5) Å and V = 769.46(9) Å3 in Rm at 0.00010(1) GPa and a = 7.1594(8), c = 15.6003(17) Å and V = 692.49(8) Å3 at 8.779(11) GPa]. The structural analysis shows that the 12-fold Na polyhedron accommodates most of the deformation by a large volume decrease (14%) and strong polyhedral distortion (63%). Our results indicate that natrojarosite has the most compressible structure of the supergroup studied so far, and has a very strong axial anisotropy.

Domerockite, Cu4(AsO4)2(AsO3OH)(OH)3·H2O, is a new mineral from the Dome Rock Mine, South Australia. It occurs as aggregates of bluish green, equant to short prismatic and tabular crystals up to 0.3 mm long and 0.2 mm across. Domerockite is translucent, with a vitreous lustre and pale green streak. It displays no fluorescence under UV irradiation. The mineral is brittle with an uneven fracture, a Mohs hardness of ∼3 and a calculated density of 4.44 g/cm3 (based on the structure refinement). Optically, it is biaxial negative, with α = 1.798(4), β = 1.814(4), γ = 1.817(4), 2Vcalc. = 46°; pleochroism is very weak; X pale greenish yellow, Y greenish blue, Z greenish blue; absorption X < Y = Z; orientation is uncertain. Chemical analysis by electron microprobe gave CuO 52.04, ZnO 0.78, BaO 0.11, As2O537.67, P2O50.32, SiO20.24, H2O 8.84, total 100.00 wt.%, with H2O calculated by difference. The empirical chemical formula is (Cu3.94, Zn0.06)Σ4.00H0.91(As1.97, P0.03, Si0.02)Σ2.02O8(OH)3.00˙H2O based on 12 oxygen atoms.

Domerockite is triclinic, space group P, with a = 5.378(11), b = 8.962(18) c = 9.841(2) Å, α = 75.25(3), β = 83.56(3), γ = 79.97(3)°, V = 450.5(16) Å3 and Z = 2. The eight strongest lines in the X-ray powder diffraction pattern are [d (Å), (I)(hkl)]: 4.716 (30)(101, 002, 111), 3.697 (25)(121), 3.605 (30)(120, 12), 3.119 (60)(12), 3.073 (100)(1), 2.856 (40)(02, 030), 2.464 (50)(212, 13), 2.443 (40)(014). The crystal structure of domerockite has been solved by direct methods and refined to an R index of 7.44% using 2635 observed reflections. The structure comprises [Cuφ4] (φ = O, OH) chains of edge-sharing sharing, distorted octahedra that extend along [10] and are decorated by AsO4 tetrahedra to form sheets in the (010) plane. Dimers of edge-sharing [CuO4(OH)(H2O)] octahedra share corners with dimers of edge-sharing [CuO4(OH)] square pyramids to form zigzag chains which extend along [101]. The chains lie between and link to the sheets by sharings corners of octahedra, square pyramids and tetrahedra to form a heteropolyhedral framework.