Emanation thermal analysis (ETA), based on radon release measurements from previously labeled samples, was used for the first time in the characterization of the thermal behavior of natural Mg2+-vermiculite (Santa Olalla, Huelva, Spain) and of Na+- and ${\text{NH}}_4^{+}$-exchanged vermiculite samples. In addition, vermiculite samples subjected to a chemical treatment with an aqueous solution of (NH4)2SiF6 and partially or totally re-saturated with Na+ ions were also investigated by ETA. The ETA results of natural Mg2+-vermiculite, Na+-vermiculite and ${\text{NH}}_4^{+}$-vermiculite gave supplementary information about microstructure changes of the samples observed under dynamic heating conditions. The method has proved to be very useful for characterization of microstructure changes due to modification in the interlayer space of samples during the heat treatment. The crystallization of vermiculite into new phases, such as enstatite (for ${\text{NH}}_4^{+}$-vermiculite and Mg2+-vermiculite) and forsterite (for Na+-vermiculite) was also observed by ETA.

Illite is a distinctive clay mineral formed by K alteration within hydrothermal alteration zones in porphyry Cu deposits. Based on differences in spatial distribution, Kübler index, number of swelling layers, and polytype, two kinds of illite are recognized within the Dexing porphyry Cu deposit, East China. One is a hydrothermal mineral within hydrothermally-altered granodiorite porphyry and altered tuffaceous phyllite near the contact zone with the granodiorite porphyry cupola. The hydrothermal illite is formed by illitization of plagioclase and/or micas during hydrothermal fluid-rock interaction. The considerable variation of their higher Kübler indices (0.17–1.41°Δ2θ) with swelling layer is affected by fluid/rock ratio or fluid flux. The other type of illite is a product of low-grade metamorphism within tuffaceous phyllite away from the porphyry cupola (>2 km), and has a lower Kübler index (0.06–0.13°Δ2θ), a 2M1 polytype, and no swelling layers. We suggest that, within the mineralized alteration zone, the lower the Kübler index, the stronger the degree of alteration, and the higher the copper grade. This is caused by a higher fluid/rock ratio in the middle-upper portions of the contact zone.

The occurrence of kerolite in association with various secondary Ca-Mg carbonate mineral deposits (speleothems) was identified in basaltic sea caves on the island of Kauai, Hawaii. Kerolite is the dominant clay mineral in the deposits. X-ray diffraction (XRD) peaks of the kerolite are characteristically broadened indicating its extremely poor crystallinity. Few changes were observed in the XRD patterns of this kerolite when it was subjected to various humidity, temperature and ethylene-glycol treatments. The crystals appear as flaky masses with irregular or jagged edges in scanning (SEM) and transmission electron microscopy (TEM). Electron probe and energy dispersive X-ray (EDX) microanalysis show that the clay material is dominated by Mg-Si-O, with minor amounts of Al and Ca in some samples. The chemical composition, thermal analysis and TEM observations suggest that smaller amounts of an amorphous serpentine-like phase are mixed with the kerolite. Kerolite is often the only mineral associated with poorly mineralized, actively-growing microbial mats in these caves and it is common in completely lithified microbial mats. The latter commonly have microstromatolitic structures with kerolite as a dominant phase. These features suggest that kerolite formation is at least in part a result of microbial activity. The abundant extracellular polymers of the mat-forming bacteria bind and concentrate ions (Mg2+, silica) from solution and serve as nucleation sites for kerolite precipitation. Conditions within the mats also probably lead to formation of Mg-Si-gels, amorphous Mg-silicate precursors and ultimately kerolite. Evaporation of the cave solutions may also contribute to kerolite formation.

Bentonite, biotite, illite, kaolin, vermiculite and zeolite were treated with 0.1, 1.0 and 5.0 mol. dm−3 HCl or NaOH. Suspensions of Na homoionic forms of the initial and the treated minerals were back titrated with 0.1 mol. dm−3 NaOH. From back-titration data variable surface charge, QV, vs. pH dependencies and apparent surface dissociation constant distribution functions were estimated. Variable charge vs. pH curves were scaled against cation exchange capacity at pH 7.2 to obtain actual charge, QA, vs. pH plots. In general both treatments led to an increase of QV, while the QA value increased and decreased depending on the mineral and the treatment. Products of 5 mol dm−3 NaOH action on zeolite and of 1 and 5 mol. dm−3 NaOH on kaolin apparently developed a positive surface charge below pH ∼3.7 and below ∼4.3, respectively.

The heterogeneity of charge-generating surface groups was observed in natural minerals. During acid treatment, the number of weakly-acidic surface functional groups increased while the number of groups of stronger acidic character decreased. The opposite was found for alkaline treatment: the number of surface groups of intermediate acidity increased and that of low acidity decreased.

The substitution in layered double hydroxide-like phases (LDH) of composition $\begin{array}{cc}{\left({\text{Co}}_{1-y}^{2+}{\text{Cu}}_y^{2+}\right)}_2{\text{Al}}^{3+}{\left(\text{OH}\right)}_6{\text{Cl}}^{-}\cdot n{\text{H}}_{\text{2}}\text{O}& \left(0⩽y⩽1\right)\end{array}$ was studied by X-ray diffraction and X-ray absorption spectroscopy. It was found that the lamellar character is maintained over the entire range of the substitution. The local order for the composition {Co2Al} is typical of brucite-like sheets, whereas segregation into small domains may explain the results obtained when the percentage of Cu atoms is increased. The {Cu2Al} end-member material presents a local order around the Cu atoms closely related to the botallackite structure as present in basic layered Cu salts, with the presence of two distinct Cu-Cu distances.

Illite-smectite (I-S) minerals isolated from Upper Jurassic oil-source rock shales from Denmark and the North Sea have been investigated by X-ray diffraction, thermal analysis, infrared, Mössbauer, and solid-state nuclear magnetic resonance spectroscopies and chemical analysis. Detailed structures have been determined in order to reveal the diagenetic transformation mechanism in these shales. Generally, in oil-source rocks of sedimentary basins, oil generation takes place simultaneously with the diagenetic transformation of I-S. We demonstrate a link between the two reactions: NH3 released from kerogen during maximum oil generation is fixed as NH4+ in the NH4-bearing mica or tobelite layers formed from smectite or vermiculite layers in I-S, in a diagenetic interval which we name the ‘tobelitization window’. Due to this solid-state transformation, mixed-layer structures have been formed consisting of interstratified illite, tobelite, smectite and vermiculite layers (I-T-S-V) and having maximum ordering of illite + tobelite and smectite layers for R = 1. The tobelitization of smectite in I-S is probably typical for all oil-source rock shales.

The ultrasound technique was applied to the synthesis of layered double hydroxides. The use of ultrasound in the synthesis of these compounds was studied in terms of its effect on their crystal qualities and surface properties. The crystal qualities of the compounds synthesized with ultrasound were compared with those of compounds synthesized without ultrasound to elucidate the effect of the ultrasound on the synthesis. The effect of crystal quality (crystallite size) on the adsorption behavior of humic substances was examined. The compounds synthesized under ultrasonic conditions showed a larger crystallite size and a larger adsorption capacity for humic substances than those synthesized without ultrasonic treatment. The degree of adsorption correlated well with crystal quality.

New experimental data with respect to the solubility of natural and synthesized magadiite at elevated temperatures and in alkaline solutions are presented. The results show that the solubility of magadiite increases according to the expression ln(Kmag) = −8146·T(K)−1 − 5.71 from 20 to 100°C ($(\Delta G_{\text{R}}^0({\text{K}}_{\text{mag}})=19.6\pm 0.3$ and $\Delta H_{\text{R}}^0({\text{K}}_{\text{mag}})=16.2\pm 0.4\text{kcal}{\text{mol}}^{-1}$). The experimental results and the related data from the literature suggest that the formation of magadiite may be favored by a decrease of temperature and pH (pH >9) as well by large amounts of Na+ ions and low ionic strength. These effects are related to the value of $\Delta H_{\text{R}}^0({\text{K}}_{\text{mag}})$, the distribution of dissolved silica species, the stoichiometry of magadiite, and the occurrence of negatively-charged species, respectively.

We studied a set of 15 reference clays from The Clay Minerals Society (CMS) Source Clays repository. Our aim was to use them as reference materials in our version of the QUAX mineral database. The QUAX software (Quantitative Phase-Analysis with X-ray Powder Diffraction) has been used successfully at the KTB site (German Continental Deep Drillling) to determine mineral assemblages quickly, in an automatic fashion, on a large number of samples (∼40,000). It was also applied to Quaternary marine sediments of the Japan Sea. Our current research focuses on marine and lacrustrine sediments from the Arctic Ocean and Siberia.

QUAX is a full-pattern method using a reference materials database. The quality of a particular quantification depends on the availability of the relevant mineral phases in the database. Our aim is to extend and improve the database continuously with new data from our current projects, particularly from clay and feldspar minerals.

A reference material in the QUAX software must be monomineralic. Before X-ray diffraction (XRD) patterns of CMS clays could be added to the database, quantification of any impurities was necessary. After measuring the bulk material by XRD, the <2 µm fraction was separated because we assumed it would contain the smallest amount of impurities. Here we present grain-size data, XRD data and X-ray fluorescence (XRF) data for this clay-sized fraction. The results of chemical and mineralogical preparation techniques and (elemental) analysis methods were combined. For XRD, random and oriented clay-aggregate samples as well as pressed pellets for QUAX analysis were prepared. Semi-quantitative clay mineral determinations were run for comparison.

The intercalation of europium ions (Eu3+) into the interlayer space of a layered silicate, magadiite, was conducted by ion-exchange reactions between magadiite and europium(III) chloride. X-ray diffraction and elemental analysis results indicated that Eu3+ cations were intercalated into the interlayer space of magadiite. The ion exchange between Eu3+ and Na+ occurred preferentially so that the adsorbed Eu3+ amounts were controlled quantitatively. Thermal transformation of the original layered structure was suppressed by the intercalation of Eu3+. The resulting intercalation compounds exhibited photoluminescence arising from the intercalated Eu3+. The luminescence intensity varied in accordance with the amount of Eu3+ absorbed, suggesting that the self-quenching occurred at higher loading levels. The luminescence intensity was also changed by the heat treatment, corresponding to the change in the surroundings of the Eu3+ adsorbed, induced by the removal of the adsorbed water molecules and the hydroxyl groups of the silicate.

One montmorillonite, STx-1 (Texas, USA), was activated with different amounts of Al and tetramethylammonium (TMA+) cations to obtain materials with a combined Al3+ and TMA+ content equal to its cation exchange capacity. The adsorption capacity of these samples was studied saturating them with hept-1-ene at room temperature. The samples were heated and the evolved gases analyzed by Fourier transform infrared spectroscopy and gas chromatography-mass spectrometry. Hept-1-ene reacted with the clays via proton transfer and resulted in the formation of a variety of reaction products (>60 hydrocarbons). In general, the presence of TMA+ cations significantly reduced the population of protons to selectively produce isomerization and hydration products.

Bacterial mineralization in weathered pyroclastic deposits of the Kaimondake volcanic ash (4040 ybp) and the Koya pyroclastic flow (6400 ybp) was investigated to evaluate the impacts of bacteria on mineral formation, and to characterize the microbiogenic minerals in the weathering environment. The mineralogy of abiogenic weathering products was also investigated for comparison with the microbiogenic products, and mineral saturation indices were calculated for porewaters using the PHREEQC computer code. The results indicated that these weathered pyroclastic deposits contain 108–109 cells/g, consisting of spherical to rod-shaped bacteria. Associated abiogenic allophane had an Al/Si ratio ranging from 1.01 to 2.13. The bacterial cell surfaces were completely or partially covered by poorly-ordered silicate minerals, which could be divided into two groups based on their chemical and morphological characteristics. Group I was characterized by well developed fibrous to smectite-like flaky habits with variable Al, Si and Fe, corresponding to compositions between proto-imogolite allophane and chamosite. These Al-Si-Fe minerals were the most abundant and major microbiogenic products in both lithologies. Group II exhibited poorly-developed aggregates of allophane-like granular materials composed mainly of Al and Si with minor Fe. Geochemical calculations revealed that the porewaters were saturated with respect to allophane and other crystalline clay minerals such as halloysite, kaolinite, montmorillonite and nontronite. These microbiogenic minerals may be formed as the earliest phase of these clay minerals after interaction of the bacterial cell surfaces with dissolved cations mainly Si, Al and Fe, in the porewaters.

Lattice dynamic calculations for the sepiolite and palygorskite structures using polarized Raman and FTIR spectra provide a fundamental basis for interpreting spectral features by assigning vibrational modes. The Si-O stretch and O-Si-O bond bending force constants determined for palygorskite are similar to equivalent values calculated previously for other phyllosilicates. The Mg-O bond stretch values, on the other hand, are about half of those determined for the equivalent Al-O and Mg-O bond stretch environments in other phyllosilicates, suggesting that the bonding within the octahedral ribbons in palygorskite and sepiolite is weaker than that in the continuous octahedral sheets in micas. The weaker bonding allows more flexible octahedral environments in palygorskite and sepiolite, giving rise to higher probabilities for cation substitutions and vacancies relative to the micas. Above ∼700 cm−1 in the IR and 750 cm−1 in the Raman spectra, the eigenmodes are dominated by atomic displacements within the silicate sheets. Below 700 cm−1 the eigenmodes become mixed with motions among the Mg octahedra and the silicate sheets; the eigenmodes assigned to the most prominent peaks in the Raman spectra (near 700 cm−1) belong to this group. As mode frequencies decrease, the corresponding eigenmodes evolve from more localized Mg-O stretch, O-Mg-O bend and O-Si-O bend motions to longer-range motions such as silicate sheet deformations caused by silicate tetrahedra rotation and silicate sheet shearing around the Mg-octahedral sheets.

Micromorphological studies were performed in order to understand the factors and processes involved in the formation of calcium carbonate (CaCO3) in twenty three soil series of Vertisols representing sub-humid, semi-arid and arid climatic regions of Peninsular India. The study indicates that Vertisols contain both pedogenic calcium carbonate (PC) and non-pedogenic calcium carbonate (NPC) irrespective of the ecosystems to which they belong. The NPCs are part of the parent material of Vertisols. Dissolution of NPCs and recrystallization of dissolved Ca2+ ions are responsible for the formation of PCs. Vertisols of arid and semi-arid climates contain more PC in their soil control section (SCS) than those of sub-humid climates. Formation of PC is the prime chemical reaction responsible for the increase in pH, the decrease in the Ca/Mg ratio of exchange site with depth and in the development of subsoil sodicity. Petrographic and scanning electron microscopic (SEM) examination of quartz, feldspars and micas indicate little or no alteration, discounting the possibile formation of smectite during Vertisol formation. X-ray diffraction (XRD) analysis of clays indicates that smectites of Vertisols are fairly well crystallized and do not show any sign of transformation except for hydroxy interlayering. The preservation of the crystallinity of smectite and the lack of transformation of primary minerals thus validate the hypothesis of positive entropy change during the formation of Vertisols.

The precise cause-effect relationship between CaCO3 of pedogenic and non-pedogenic origin, and exchangeable Mg, Na and Ca percentages (EMP, ESP and ECP) has been established in the study. This indicates that impoverishment of Ca2+ ions on the exchange sites of Vertisols needs to be controlled by rehabilitation methods that can replenish Ca2+ ions, and thus the study provides relevant information for future land resource management programmes not only on Vertisols of India but also on similar soils occurring elsewhere.

Kaolin, a possible source of Al, may be reacted with inorganic acids or salts to form different Al salts that can be further processed to prepare metallic Al. Although the reaction of kaolin and acid in aqueous solution can be monitored by chemical analysis of Al, the Al salts must be extracted from any unreacted kaolinite. Also, the lixiviation of Ti or Fe species present in kaolin should be monitored. A simple extraction procedure is reported to determine, quickly and quantitatively, water-soluble Al, Ti and Fe metals present in products of reaction of kaolin (85 wt.% kaolinite, 12 wt.% mica, 2 wt.% feldspar, 1 wt.% quartz) with inorganic salts, such as sodium hydrogensulfate, using conventional glassware for the glass reaction tubes. Optimum results are obtained with 250 mL glass reaction tubes. The best operating conditions found for this piece of equipment are: (1) sample weight of 0.05 g, (2) lixiviation time of 1 h, and (3) lixiviating agent, 50 mL of an aqueous solution of pH = 1 H2SO4 at its boiling point. Comparisons are made with soxhlet extraction and beaker and magnetic stirring methods.

The thermally-induced dehydroxylation and transformations of the 2:1 phyllosilicate pyrophyllite have been studied using infrared spectroscopy in the frequency range 350–11000 cm−1 and the temperature range 200–1500°C. The dehydroxylation of pyrophyllite to pyrophyllite dehydroxylate occurs between 500 and 900°C. It is characterized by a decrease in the intensity of the OH signals and phonon bands of pyrophyllite and the eventual disappearance of these features as well as the appearance of extra signals related to pyrophyllite dehydroxylate and an intermediate phase. Our results are consistent with previous observations that the SiO4 tetrahedral sheet structure still exists in pyrophyllite dehydroxylate, that the Si-O-Al linkages and 2:1 structure remain in the pyrophyllite dehydroxylate, and that AlO5 trigonal bipyramids form.

Two extra OH bands at 3690 and 3702 cm−1 and their overtones at 7208 and 7234 cm−1 are observed, for the first time, in samples annealed at the temperature range 550–900°C. Our results suggest that the formation and dehydroxylation of the extra OH species can be strongly affected by kinetic effects. The experimental evidence shows that the dehydroxylation of pyrophyllite is a two-stage process. The appearance of these additional OH bands is interpreted in terms of an unknown intermediate phase, and may be related to the second endothermic peak observed at high temperatures in DTA experiments. Pyrophyllite dehydroylate decomposes into a Si-rich amorphous phase and mullite in the temperature range 950–1100°C. Cristobalite is observed in the temperature range 1150–1500°C.

Diagenesis of the Holocene-Pleistocene volcanogenic sediments of the Mexican Basin produced, in strata of gravel and sand, 1H2O- and 2H2O-smectite, kaolinite, R3-2H2O-smectite (0.75)-kaolinite, R1-2H2O-smectite (0.75)-kaolinite, R3-kaolinite (0.75)-2H2O-smectite and R1-1H2O-smectite (0.75)-kaolinite. Smectite platelets were formed from volcanic glass by loss of Si4+. Partially-formed platelets have Si4+ between 4.55−4.10 a.p.f.u., Mg+Mn and the interlayer charge are relatively uniform while VIAl+Fe3++Ti varies between 0.98 and 1.63 a.p.f.u. Almost fully transformed platelets have Si4+ of 4.08−4.04 a.p.f.u.; Mg+Mn and the interlayer charge decrease proportionally to increasing VIAl+Fe3++Ti. Smectite-kaolinite mixed layers have octahedral occupancies of 2.01–2.15 a.p.f.u., IVAl3+ 0.09–0.55 a.p.f.u. and interlayer charges about half that of smectite; structural formulae corresponding to smectite (0.75–0.80)-kaolinite indicate octahedral occupancy of 2.50 a.p.f.u., tetrahedral replacement 0–0.31 a.p.f.u., and interlayer charge 0.24–0.51 equivalents, some indicating interstratifications of beidellite. Kaolinite is presumed to have formed from K-feldspar; smectite-kaolinite interstratifications sustain the transformation of kaolinite to smectite in an increasingly siliceous high-cation environment. In the mudstones of low-hydraulic conductivity and practically stagnant alkaline fluids, glass was transformed to 2H2O-smectite lamellae of IVAl between 0 and 0.47 a.p.f.u., octahedral occupancy 1.70–2.00 a.p.f.u. and interlayer charge of 0.23–1.21 equivalents, some corresponding to beidellite. The interlayer charge increases with IVAl and decreasing occupancy of the octahedral sheet; the abundance of Mg+Mn is inverse to that of VIAl+Fe3++Ti.

Clay suspensions containing 1H2O- and 2H2O-smectite, kaolinite and R3-2H2O-smectite (0.75)-kaolinite lead to low-energy edge-to-edge particle associations, non-Newtonian pseudoplastic behavior, and maximum apparent viscosity of 180 Pa s at 0.008 s−1 followed by rapid descent. Clay fractions with slightly larger 2H2O-smectite contents and smaller kaolinite contents reach maximum viscosity of 3611 Pa s at a shear rate of 0.0018 s−1 and of 3300 Pa s at 0.0024 s−1. They denote two high-energy face-to-face particle associations, followed by slow descent of the apparent viscosity under viscous flow. Suspensions change from elastic to viscous behavior at shear stresses of 1.03 and 5.91 Pa, respectively. Clay suspension vibrated at a frequency of 1 Hz develops a shear storage dynamic modulus greater than the shear dynamic loss modulus or the energy is preferentially stored, whereas at 5 Hz more energy is dissipated than stored.

The purpose of this report is to describe the appropriate use of indices relating to crystallinity, such as the ‘crystallinity index’, the ‘Hinckley index’, the ‘Kübler index’, and the ‘Árkai index’. A ‘crystalline’ solid is defined as a solid consisting of atoms, ions or molecules packed together in a periodic arrangement. A ‘crystallinity index’ is purported to be a measure of crystallinity, although there is uncertainty about what this means (see below). This report discusses briefly the nature of order, disorder and crystallinity in phyllosilicates and discusses why the use of a ‘crystallinity index’ should be avoided. If possible, it is suggested that indices be referred to using the name of the author who originally described the parameter, e.g. ‘Hinckley index’ or ‘Kübler index’, or in honor of a researcher who investigated the importance of the parameter extensively, e.g. ‘Árkai index’.