Amorphous Bi2Sr2CaCu2O8 (Bi-2212) was crystallized under uniaxial loads (up to 1500 N) at temperatures up to 890 °C to induce texture. Well-textured samples (19 mm in diameter and 0.15 mm thick) were obtained for samples heated to 890 °C and quenched. Heated (10 °C/min) and quenched samples at 550, 750, 850, and 870 °C demonstrate that the crystallization path is Bi2Sr2CuO6 (Bi-2201) (550 °C) to Bi-2212 (850 °C), with texturing occurring during grain growth (T > 850 °C). Comparison of samples crystallized under load and no load demonstrates that the texturing is a result of the plane stress biasing the normal anisotropic grain growth normal to the applied stress direction.