23 April 2024: We are investigating problems with ecommerce on Cambridge Core. We apologise for any inconvenience and hope to have full functionality restored shortly.
We use cookies to distinguish you from other users and to provide you with a better experience on our websites. Close this message to accept cookies or find out how to manage your cookie settings.
To save this undefined to your undefined account, please select one or more formats and confirm that you agree to abide by our usage policies. If this is the first time you used this feature, you will be asked to authorise Cambridge Core to connect with your undefined account.
Find out more about saving content to .
To save this article to your Kindle, first ensure coreplatform@cambridge.org is added to your Approved Personal Document E-mail List under your Personal Document Settings on the Manage Your Content and Devices page of your Amazon account. Then enter the ‘name’ part of your Kindle email address below.
Find out more about saving to your Kindle.
Note you can select to save to either the @free.kindle.com or @kindle.com variations. ‘@free.kindle.com’ emails are free but can only be saved to your device when it is connected to wi-fi. ‘@kindle.com’ emails can be delivered even when you are not connected to wi-fi, but note that service fees apply.
The low electron affinity of a-C:H is related to that of diamond surfaces and is studied using a chemical bonding model. The electron field emission from hydrogenated amorphous carbon (a-C:H) and nitrogen modified a-C:H showing low turn on fields are described. Nitrogen improves the field emission, apparently by raising the Fermi level.