High Spatial Resolution X-Ray Analysis in a SEM

Published online by Cambridge University Press:  11 March 2014

Steve Chapman*
Affiliation:
Protrain, 23 Foxglove Close, Buckingham MK18 1FU, United Kingdom
Ron Rasch
Affiliation:
Centre for Microscopy & Microanalysis, The University of Queensland, Brisbane St Lucia, QLD 4072, Australia

Abstract

Type
Microanalysis
Copyright
Copyright © Microscopy Society of America 2014 

Introduction

For many years energy-dispersive X-ray analysis has been carried out on scanning and transmission electron microscopes. The spatial resolution of analysis is the major difference between the two techniques, as shown in Figure 1. Working with a thin section in the transmission electron microscope (TEM), it is possible to obtain X-ray information from a region almost the same diameter as the incident electron beam. However the TEM suffers from having a sample totally surrounded by X-ray emitting materials. Careful masking of the system is required in order to ensure that X rays from these materials do not contribute to the X-ray spectrum from the region of interest. An analysis conducted in the scanning electron microscope (SEM) suffers from a high level of beam spread within the specimen, resulting in information from emission areas that are many micrometers in diameter and many micrometers deep. Whilst most SEM manufacturers have transmission imaging attachments, these often suffer the same problems as a TEM. They too are surrounded by materials that emit X rays that may interfere with the desired X-ray signal.

Figure 1 Schematic comparison of the X-ray excitation regions of a TEM thin specimen with a SEM bulk specimen.

Thin-Film X-Ray Holder

Using a physical arrangement similar to a Faraday cup, Protrain has developed a thin-film specimen holder that allows high spatial resolution X-ray analysis in any model of SEM. The specimen sits in an aluminium holder directly above a 3 mm deep hole that is coated with carbon (Figure 2). The majority of electrons passing through the specimen are lost within the hole, as in a Faraday cup, and those that are backscattered are small in number because of the low backscatter coefficient of the carbon coating. The carbon coating has a secondary role in that it masks the aluminium holder reducing the aluminium systems peak in the background [Reference Thomas and Auchterlonie1,Reference Ziegler2].

Figure 2 Schematic of the thin-film holder machined from a conventional SEM stub.

There are other advantages to carrying out thin-film X-ray analysis in the SEM. In the SEM specimen chamber there is more space and therefore less possibility of interference fromX rays generated in chamber materials. Using this technique the major contributor to artifactual X rays could be backscattered electrons (BSEs) hitting the bottom of the final lens, but this may be masked if a BSE detector or low-atomic-number shield is in place. When using the SEM in this mode, imaging is possible by secondary electrons (SE) and BSEs as well as through the use of X-ray maps [Reference Friel and Lyman3]. Often BSE imaging is preferred when X-ray analysis is performed so that the electron image resolution is closer to the X-ray map resolution.

Results

Tests of the thin-film holder in a SEM with a tungsten-hairpin source reveal useful X-ray map information at magnifications up to 100,000×, where an apparent map resolution better than 100 nm may be discerned. In the example shown in Figures 3 and 4,a LaB6 source was used to demonstrate this level of X-ray map. In field-emission SEMs we have produced X-ray maps at magnifications up to 500,000×. For example, thin-film analysis of polymer interfaces was carried out recently in the SEM at much higher spatial resolution than would be possible with a bulk-specimen interface [Reference Vandi, Truss, Veidt, Rasch, Heitzmann and Paton4]. Another point that may interest some scientists is that the holder also may be used in a dedicated electron probe that employs wavelength-dispersive X-ray spectrometers to produce X-ray maps with greater elemental sensitivity.

Figure 3a Secondary electron image of a Ti-Nb-oxide particle contaminated with Fe acquired with the thin-film X-ray holder.

Figure 3b Fe Kα X-ray map acquired from the Ti-Nb-oxide particle shown in 3a.

Figure 4 Global spectrum from the area examined in Figures 3a and 3b. The horizontal scale denotes the energies of emitted X rays generated with a beam energy of 25 keV. Note the low background level.

Discussion

When carrying out thin-specimen analysis in the SEM, the analytical approach needs to be considered. Most important is that it should be realized that most SEM EDS software comes with some sort of standardless quantitative procedure. Although not as accurate as analysis using standards, this procedure is quick and in common use. It performs a matrix correction procedure (be it ZAF, ϕ(ρz), or XPP [Reference Goldstein, Newbury, Echlin, Joy, Romig, Lyman, Fiori and Lifshin5]) to turn element X-ray peaks into a composition for the sample. In many situations, unless a thin-foil routine is provided, this SEM software will assume that the specimen is a bulk material. If applied to a thin section, the bulk matrix correction will not be appropriate and will most likely overcorrect the atomic number correction, the X-ray absorption correction, and the fluorescence correction. This leads to erroneous values for most elements. If a quantitative analysis is required, it must be treated in the same way that analysis in the TEM is performed: either (a) to ratio elemental peak intensities from the unknown and a standard before employing a modified matrix correction procedure, or (b) through the simpler Cliff-Lorimer ratio technique where X-ray intensities from pairs of elements in the unknown specimen are ratioed to each other [Reference Williams and Carter6]. Others have reported using commercial TEM thin-foil standardless analysis software for thin-specimen SEM analysis and found it to produce accurate results [Reference Halvarsson, Jonsson and Canovic7]. In all cases care must be taken to ensure that analysis is not performed near a supporting grid bar.

The advantages of carrying out thin-section analytical work in the SEM are numerous. As stated previously the thin sample significantly reduces the interaction volume and therefore increases the analytical spatial resolution over normal thick-specimen SEM analysis. Thin-section analysis is traditionally done in a TEM, but we have noticed a significant increase in X-ray count rate by moving the same specimen from the TEM to the SEM. Results will vary from lab to lab and from specimen to specimen; however it is not unusual to see an order of magnitude increase in X-ray intensity when going from TEM to SEM with the same specimen. The source of this increase in X-ray yield is twofold. First, the inner-shell ionization cross section of the specimen atoms is dependent on the accelerating voltage and, for most commonly measured X-rays, the voltages typically used in SEM analysis (10–30 kV) produce more ionizations and therefore more X-rays than voltages used in typical TEM analysis (100–300 kV). An overvoltage of 2–3 is usually desirable, where overvoltage is the ratio of incident beam energy to critical ionization energy. This produces the maximum number of ionizations in most analytical situations [Reference Goldstein, Newbury, Echlin, Joy, Romig, Lyman, Fiori and Lifshin5,Reference Campos, Vasconcellos, Trincavelli and Segui8]. Secondly, the probability of an electron scattering from a specimen atom is inversely proportional to the potential of the incident electron [Reference Goldstein, Newbury, Echlin, Joy, Romig, Lyman, Fiori and Lifshin5]. So electrons scatter less at the higher voltages used by TEMs, and more pass directly through the specimen. At SEM accelerating voltages, the electron beam scatters more, producing multiple ionizations in the specimen material, as shown by the two Monte Carlo plots (Figure 5) of electrons passing through a thin iron specimen at 20 kV and 200 kV. These two effects together simply say that more of the beam interacts with more of the specimen at SEM voltages than at TEM voltages.

Figure 5 Monte Carlo simulations of electrons traveling through (a) 50 nm thick iron film at 20 keV and (b) the same film at 200 keV.

Further Possibilities

The scanning microscope may enable observation of a thin-film specimen in other advantageous modes. First, provided the specimen is mounted grid side down 100 percent of a specimen may be viewed without grid bar intervention. Secondly, SEM images of the material in inverted signal mode, particularly with stained biological material, will display an image very similar to that from a TEM in bright-field (BF) mode. Two common imaging modes in the TEM are BF mode and dark field (DF) mode, both of which are dominated by elastic scattering. In the SEM the elastically scattered signal is the BSE image, and that produces contrast similar to the TEM DF image. If a conventionally stained biological thin section is imaged in the SEM in BSE mode and then software is used to invert the contrast, the image obtained looks like a conventional biological TEM BF image.

Further, a biological thin specimen is flat and lacks topography, so the SE image contrast is now dominated by the BSE-sourced SEs of type 2 (SE II) [Reference Goldstein, Newbury, Echlin, Joy, Romig, Lyman, Fiori and Lifshin5]. This image also can be inverted to produce an image similar to the conventional TEM BF. Figure 6 shows a typical example is shown below of stained mouse islet sections, imaged in the SEM with SE mode; the contrast was inverted. The major advantage of this technique is that 100 percent of the specimen is available for investigation when the accelerating voltage is adjusted to minimize the grid bar signal.

Figure 6 Stained mouse pancreatic islets of Langerhans cells imaged in the SEM in SE mode (contrast inverted). The material was high-pressure frozen, freeze substituted, fixed, and stained with uranyl acetate. The section is 60 nm thick.

Conclusions

Simply by thinking in a new dimension when examining specimens in a SEM opens up a number of new areas for investigation. Changing the style of the specimen and the way it is mounted in the microscope may offer even more information to researchers. This article describes the advantages of examining TEM thin specimens in the SEM.

Acknowledgments

The authors would like to thank David Joy for the use of his Monte Carlo modelling software, and also the facilities of the Australian Microscopy & Microanalysis Research Facility, Centre for Microscopy and Microanalysis, The University of Queensland. Ron Rasch would like to thank Graeme Auchterlonie for his friendly support and insightful advice about electron scattering. We are both appreciative of help from Charles Lyman.

References

[1]Thomas, CE and Auchterlonie, GJ, “Improved Low Background Analytical SEM Holders for Thin Sections,” 13th Australian Conference of Electron Microscopy, Gold Coast, February 7–14, 1994, p. 202, 7–14.Google Scholar
[2]Ziegler, A, Microsc Microanal 13(Suppl 3) (2007) 176.Google Scholar
[3]Friel, JJ and Lyman, CE, Microsc Microanal 12 (2006) 2.Google Scholar
[4]Vandi, L-J, Truss, R, Veidt, M, Rasch, R, Heitzmann, MT, and Paton, R, J Phys Chem C 117(33) (2013) 16933.CrossRefGoogle Scholar
[5]Goldstein, JI, Newbury, DE, Echlin, P, Joy, DC, Romig, A, Lyman, CE, Fiori, C, and Lifshin, E, Scanning Electron Microscopy and X-ray Microanalysis, 2nd Ed., Plenum Press, New York and London, 1992, p. 69.Google Scholar
[6]Williams, DB and Carter, C Barry, Transmission Electron Microscopy, Plenum Press, New York and London, 1996.Google Scholar
[7]Halvarsson, M, Jonsson, T, and Canovic, S, Journal of Physics: Conference Series 126 (2008) 597.Google Scholar
[8]Campos, CS, Vasconcellos, MAZ, Trincavelli, JC, andSegui, S, J Phys B–At Mol Opt 40 (2007) 3825.CrossRefGoogle Scholar
Figure 0

Figure 1 Schematic comparison of the X-ray excitation regions of a TEM thin specimen with a SEM bulk specimen.

Figure 1

Figure 2 Schematic of the thin-film holder machined from a conventional SEM stub.

Figure 2

Figure 3a Secondary electron image of a Ti-Nb-oxide particle contaminated with Fe acquired with the thin-film X-ray holder.

Figure 3

Figure 3b Fe Kα X-ray map acquired from the Ti-Nb-oxide particle shown in 3a.

Figure 4

Figure 4 Global spectrum from the area examined in Figures 3a and 3b. The horizontal scale denotes the energies of emitted X rays generated with a beam energy of 25 keV. Note the low background level.

Figure 5

Figure 5 Monte Carlo simulations of electrons traveling through (a) 50 nm thick iron film at 20 keV and (b) the same film at 200 keV.

Figure 6

Figure 6 Stained mouse pancreatic islets of Langerhans cells imaged in the SEM in SE mode (contrast inverted). The material was high-pressure frozen, freeze substituted, fixed, and stained with uranyl acetate. The section is 60 nm thick.