This work reports the growth of crystalline SrHf
x
Ti1−x
O3 (SHTO) films on Ge (001) substrates by atomic layer deposition. Samples were prepared with different Hf content x to explore if strain, from tensile (x = 0) to compressive (x = 1), affected film crystallization temperature and how composition affected properties. Amorphous films grew at 225 °C and crystallized into epitaxial layers at annealing temperatures that varied monotonically with composition from ~530 °C (x = 0) to ~660 °C (x = 1). Transmission electron microscopy revealed abrupt interfaces. Electrical measurements revealed 0.1 A/cm2 leakage current at 1 MV/cm for x = 0.55.