Kaolinite:NaCl intercalates with basal layer dimensions of 0.95 and 1.25 nm have been prepared by direct reaction of saturated aqueous NaCl solution with well-crystallized source clay KGa-1. The intercalates and their thermal decomposition products have been studied by XRD, solid-state 23Na, 27Al, and 29Si MAS NMR, and FTIR. Intercalate yield is enhanced by dry grinding of kaolinite with NaCl prior to intercalation. The layered structure survives dehydroxylation of the kaolinite at 500°–600°C and persists to above 800°C with a resultant tetrahedral aluminosilicate framework. Excess NaCl can be readily removed by rinsing with water, producing an XRD “amorphous” material. Upon heating at 900°C this material converts to a well-crystallized framework aluminosilicate closely related to low-carnegieite, NaAlSiO4, some 350°C below its stability field. Reaction mechanisms are discussed and structural models proposed for each of these novel materials.

The long-term impermeability of clay barriers in waste disposal facilities and hydraulic structures is of critical importance to environmental, agricultural, and industrial concerns. Changes in the oxidation state of Fe in the constituent clays of compacted clay barriers may degrade the hydraulic conductivity of these structures because other properties related to hydraulic conductivity, such as swelling, gel microstructure, and particle size, are greatly altered by the oxidation state. Two Na-saturated smectites (SWa-1 and API 25) were reduced by sodium dithionite (Na2S2O4), both in suspension and in situ after consolidation, to examine the effects of structural Fe reduction on hydraulic conductivity. Results indicated that the hydraulic conductivity depended on both the oxidation state and the consolidation history of the clay. The hydraulic conductivity of clay reduced in suspension before consolidation was lower than that of oxidized clay. Initially reduced smectite, thus, may be compactable to a less-permeable material with higher bulk density. But reduction of smectite in situ after consolidation increased the hydraulic conductivity and its variability. The oxidized state of clay liners should, therefore, be preserved.

X-ray diffraction patterns were obtained from rock fragments, < 1 μm randomly oriented freeze-dried powders, and < 1 μm oriented aggregates for 11 mixed-layered illite/smectite samples (K-bentonites) that cover the range from 14 to 100 percent expandable. In all cases, 00l and hkl comparisons show no evidence of laboratory induced artifacts. Either the laboratory procedures caused no disaggregation of fundamental illite particles, or, if they did, fundamental particle reaggregation during sample preparation duplicated the one and three-dimensional structures of the illite/smectite in the original, untreated rock.

Demodulation of the 20l, 13l reflections into a two-dimensional band shape occurred with increasing percent expandable layers in illite/smectite. This result strongly supports the contention that turbostratic displacements occur at the expandable interfaces between fundamental particles, and are limited to those sites.

A comparison of the quantities measured by powder X-ray diffraction and high resolution transmission electron microscope (TEM) lattice fringe image techniques for disordered crystals suggests that meaningful comparisons between the two methods can be made only if a sufficient number of images are recorded to define the statistical parameters of the disorder.

A series of reduced-charge (RC) hectorites were prepared by multiple heat (250°C) treatments of Mg-saturated hectorites (SHCa-1 ). Cation exchange capacity (CEC) measurements and alkylammonium exchange indicated that a decrease in layer charge occurred with each Mg-250 treatment. Chemical analyses showed that decreases in structural Li and increases in structural Mg contents coincided with charge reduction. Fluorescence measurements of adsorbed quinoline indicated that the hectorite surface was acidified during charge reduction; hydroxyl group deprotonation is a possible source for the acidity. Fourier transform infrared spectra (FTIR) indicated that the Mg-250 treatment induced the loss of structural Li and shifted the SiO stretch band to a position similar to that in talc. The relative intensities of the OH and SiO stretch bands in FTIR spectra suggest that some of the hydroxyl groups in hectorite were lost, possibly by deprotonation. However, thermogravimetric data (TG) reveal no significant difference in the hydroxyl contents of the hectorites.

The FTIR spectra, CEC, layer charge, chemical, and TG data all supported the view that Mg substitution for octahedral Li occurred which resulted in a more “talc-like” structure. Charge reduction in smectites is evidently a general phenomenon and can be induced by heat treatment with the proper exchangeable cation. The ability to reduce the charge of hectorites makes it possible to prepare a series of clays which vary in charge but lack structural Fe. Such RC smectites should be suitable for expandable clay mineral studies which utilize spectroscopic techniques that are sensitive to Fe content.

Hydrothermal tobelitic phyllosilicates modeled as ISII (R3) ordering with a minimum of 2–3% and a maximum of 6–8% interstratified smectite occur in veins and as replacement of fossils in hydrothermally altered black shale. These heavy metal-rich phyllosilicate veins formed during a Mesozoic-aged, regional-scale hydrothermal event that affected an area which encompasses the Mercur Au district (Wilson and Parry, 1990a, 1990b). Associated minerals include kaolinite, quartz, chlorite, Fe-oxides, I/S (R1, 45% smectite), and pyrite. N and O contents of NH4 phyllosilicates determined by microprobe analysis range from 0.19 to 1.78 and 48.6 to 52.9 elemental wt. %, respectively. Infrared absorption analysis indicates N occurs as NH4+. Very high O analyses are probably caused by contamination with kaolinite. A representative structural formula for the tobelitic material is [(NH4)0.36K0.36Na0.03]-(Al1.91Mg0.13Fe0.03)(Si3.21Al0.79)O10(OH1.88F0.12).

Correlation plots of data from microprobe analyses indicate an atypically high correlation between interlayer charge and octahedral layer charge and no correlation between (K+Na) and N. More typical correlations between N and (K+Na) and between interlayer charge and tetrahedral layer charge are obtained if 2–8% of a beidellitic smectite are factored out of the analyses. This amount of smectite is consistent with modeling of X-ray diffraction data using the computer program NEWMOD (Reynolds, 1985).

Possible sources of NH4 are from introduction by hydrothermal fluids or from thermal degradation of organic matter prevalent within the host rocks during low-grade metamorphism. The occurrence of NH4 phyllosilicate veins in unoxidized shale and the limited occurrence of NH4 phyllosilicates within the host shales suggests a hydrothermal source for the NH4.

The rehydration and rehydroxylation properties of homoionic rectorites (saturated with Ca2+, Mg2+, Na+, or K+) were further investigated. The rehydration properties of the rectorite were characterized as follows: (1) basal spacings of rehydrated materials after heating above 500°C changed to 22.5 Å for H2O-complexes, 26.85 Å for ethylene glycol-complexes, and 27.65 Å for glycerol-complexes; (2) rehydrated Ca- and Mg-materials exhibited single layer hydrates at <50% RH, and rehydrated K-material showed double layer hydrates at 80% RH; (3) IR absorption spectra due to rehydrated H2O and OH exhibited the same or very close absorption intensities and frequencies to each other; (4) DTA-TGA curves of rehydrated materials indicated that the amount of rehydrated H2O approached about 4.2 wt. %, and about one-half of OH was rehydroxylated after heating at 800°C; and (5) interlayer cations of expandable layer components became non-exchangeable after heating above 500°C. These results suggest the following rehydration mechanism of rectorite: the interlayer cations migrate into the hexagonal holes of the SiO4 network by thermal dehydration. The cations migrated below 400°C easily return to the interlayer space and their original hydrated configurations have been recovered completely on rehydration. However, those migrated above 500°C are fixed to the hexagonal holes but water molecules are regained in the interlayer space. Consequently, electrostatic effects of interlayer cations on formation of water molecule layers are considerably reduced.

Products resulting from the reaction of toluene with Cu(II)-montmorillonite were analyzed using GC/MS, HPLC/MS, GPC, and FTIR methods. Numerous oligomers of toluene were observed, extending at least as high as the resolution limit (1500 g/mol) of the GPC column. The FTIR spectrum of the nonvolatile components of the extract was very similar to that of liquid toluene. GC/MS data on the volatile components revealed dimers, trimers, and a multitude of transmethylated products. Oligomerization proceeded via both ring-ring (i.e., polyphenyl) and ring-methyl linkages. The primary trans-methylated products were tert-butylbenzene and isopropylxylene, indicating a competition between ringand side-chain methylations. The side-chain substitutions cannot be explained in terms of the aromatic radical cation intermediate which typically forms in arene/clay reactions. A consideration of alkylbenzene reactions observed in various other media suggests that the present transmethylation reactions occur via a benzyl cation intermediate.

In the copper deposit of Salobo 3A (Brazil), nontronite-like clay samples were found at the bottom of the weathering blanket. Samples were fractionated first by sedimentation and then by a HGMS method. From XRD data, it was found that the samples are essentially smectite with kaolinite in very small quantities. The average structural formula of the smectite, presented in the traditional manner, is:

Chemical analyses show that the smectite samples contain a population of clay particles whose chemistry ranges between a nontronite end-member and an Al-Mg beidellite end-member.

Spectroscopic studies by FTIR, Mössbauer, and ESR show that the three major octahedral cations (Al, Fe, Mg) are present in each octahedral sheet of the smectite, forming a solid solution, and that the chemical trends of the smectite clay detected at a “macroscopic” scale (associated clay particles) can also be observed at the unit cell scale.

This paper aims at characterizing the morphology, texture, and microstructure of three hydrated kaolin rich clays (f < 0.2 μm) from volcanic soils. These clays represent a weathering sequence in which CEC, halloysite content with respect to kaolinite, as well as smectite content in the halloysite-smectite mixed-layer clays decrease with increased weathering. The clay samples were made homoionic (K+ or Mg2+) and hydrated under a low suction pressure (3.2 kPa). After replacing water by a resin, ultrathin sections were cut and examined by TEM. Particle shape varies with increased weathering, as follows: spheroids → tubes → platelets. Higher aggregation and dispersion are observed by TEM after Mg2+ and K+ saturation, respectively, at two levels of the clay-water system organization: intraparticle and interparticle. The microstructure variations induced by the nature of the exchangeable cation become less pronounced with decreasing layer charge of the 2:1 layers. They are thus related here to the presence of smectite layers localized in the halloysite habitus, mostly at the particle periphery. These results show that small amounts of smectite largely affect the organization of clays rich in kaolins at a high water content, and that K+ behaves here as a dispersing ion.

NMR spectra of PF1-1 Floridan palygorskite strongly suggest that Al3+ occurs only in octahedral coordination. X-ray microanalysis of the palygorskite fibers indicate a chemical composition defined by the atomic ratios: Mg/Si = 0.34, Al/Si = 0.27, and Fe/Si = 0.04. Considering the NMR and CEC data in this report along with the previously published results of IR and Mössbauer spectroscopic studies, the following structural formula is proposed for PF1-1 palygorskite:

$${\rm{(M{g_{2.12}}A{l_{1.68}}F{e^{3 + }}_{0.24}{\square _{0.96}})S{i_8}{O_{20}}{(OH)_2}{(O{H_2})_4}}}$$

The influence of tartaric acid and pH on chemical composition, morphology, surface area, and porosity of short-range ordered Al precipitation products was studied. Samples were prepared (1) at pH 8.0 and at the tartaric acid/Al molar ratios (R) ranging from 0 to 0.25 and (2) at R = 0.1 and in the pH range of 4.7 to 10.0. In Al precipitation products formed at pH 8.0, the organic C content increased from 8 g/kg (R = 0.01) to 93 g/kg (R = 0.25), whereas the Al content decreased from 363 g/kg (R = 0.01) to 271 g/kg (R = 0.25). The specific surface of the materials was particularly high (>400 m2/g) when samples were prepared at R < 0.1, but drastically decreased when samples were prepared at R > 0.1 (e.g., 78.6 m2/g at R = 0.25). When the C content was relatively high (>45 g/kg), aggregation between the particles was promoted, and the specific surface, thus, decreased. Electron optical observations showed that such samples were strongly aggregated. In the materials prepared at R = 0.1, but at different initial pH values, the C content decreased from 90 g/kg (pH = 4.7) to 25 g/kg (pH = 10.0). As a consequence, the lower the initial pH, the lower was the specific surface of the Al precipitation products. Tartaric acid plays an important role in both Pertubation of crystallization of Al hydroxides and promotion of aggregation of the reaction products. The two processes counteract in influencing the specific surface and pore volume of Al hydroxides.

Heating treatments greatly affected the specific surface and porosity of Al precipitation products. The specific surface and porosity of the samples generally increased by increasing the temperature up to 400°C and then decreased. Small amounts of C still remained after heating some samples for 12 hr at 600°C.

A new approach is described to computer simulate cation distribution in octahedral sheets of dioctahedral 2:1 layer silicates with vacant trans-octahedra. This approach makes use of the information on cation distribution at the one-dimensional level provided by integrated IR optical densities for the region of OH-stretching frequencies. By using this program it is possible to show that (1) the Mössbauer spectrum of glauconite B. Patom conforms to the structural model composed of celandonite-like and illite-like domains whose dimensions are limited by approximately 2 or 4 unit cells; (2) non-equivalency of “left” and “right” cis-positions (with fixed b-direction) with respect to R2+ and R3+ occupancy is a characteristic feature of a celadonite-like domain.