Using electro-deoxidation to synthesize niobium sponge from solid Nb2O5 in alkali–alkaline-earth metal chloride melts

Published online by Cambridge University Press:  31 January 2011

X.Y. Yan  and
D.J. Fray
X.Y. Yan
Affiliation:
Department of Materials Science and Metallurgy, University of Cambridge, Pembroke Street, Cambridge CB2 3QZ, United Kingdom
D.J. Fray
Affiliation:
Department of Materials Science and Metallurgy, University of Cambridge, Pembroke Street, Cambridge CB2 3QZ, United Kingdom
Get access

Abstract

The method of electro-deoxidation was applied to reduce solid Nb2O5 directly to niobium metal, in the form of sponge, in the eutectic CaCl2–NaCl and BaCl2–NaCl systems, respectively. The direct electrochemical reduction of solid Nb2O5 was achieved by electrolysis in the chloride melts at temperatures between 850 and 950 °C and at a controlled potential of 3.1 V, well below the decomposition potentials of the melts used. The obtained results demonstrated that the method is applicable for preparing niobium sponges directly from solid Nb2O5 under the present experimental conditions. The niobium sponge prepared was proven to possess as remarkable superconducting properties. The parameters affecting the rate and the extent of electro-deoxidation were investigated experimentally, including initial particle sizes of the starting Nb2O5 powders, compaction pressure, sintering temperature and times, electrolysis temperature and duration, and electrolyte systems. The mechanism by which the Nb2O5 pellets were electro-deoxidized to the niobium sponges was also discussed on the basis of the present experimental observations.

Type
Articles
Information
Journal of Materials Research , Volume 18 , Issue 2 , February 2003 , pp. 346 - 356
Copyright
Copyright © Materials Research Society 2003

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

Suzuki, O.R., Aizawa, M., and Ono, K., J. Alloys Compd. 288, 173 (1999).CrossRefGoogle Scholar
Padamsee, H., J. Less-Common Met. 139, 167 (1988).CrossRefGoogle Scholar
Handbook of Applied Superconductivity, edited by Seeber, B. (Institute of Physics Publishing, London, U.K., 1998), pp. 1165–1734.CrossRefGoogle Scholar
Laverick, C., J. Less-Common Met. 139, 107 (1988).CrossRefGoogle Scholar
Olzi, E. and Matacotta, F.C., J. Less-Common Met. 139, 123 (1988).CrossRefGoogle Scholar
Lyakishev, N.P., Tulin, N.A., and Pilner, Yu. L., Niobium in Steel and Alloys (Companhia Brasileira de Metalurgia e Mineracao-CBMM, Soa Paulo, Brazil, 1984).Google Scholar
Wilhelm, H.A., Schmidt, F.A., and Ellis, T.G., J. Met. 1303 (Dec 1966).Google Scholar
Kamat, G.R. and Gupta, C.K., Metall. Trans. 2, 2817 (1971).CrossRefGoogle Scholar
Carlson, O.N., in Encyclopedia of Materials Science and Engineering, edited by Bever, M.B. (Pergamon Press, New York, 1986), p. 3205.Google Scholar
Fray, D.J., Farthing, T.W., and Chen, Z., Inter. Patent No. PCT/GB99/ 01781 (first filing date: 05 June 1998).Google Scholar
Chen, G.Z., Fray, D.J., and Farthing, T.W., Nature (London) 407, 361 (2000).CrossRefGoogle Scholar
Chen, G.Z. and Fray, D.J., in Progress in Molten Salt Chemistry, edited by Berg, R.W., Hjuler, H.A. (Elsevier, Paris, France, 2000), p. 157.Google Scholar
Chen, G.Z. and Fray, D.J., Light Met. 1147 (2001).Google Scholar
Fray, D.J. and Chen, G.Z., in Proceedings of the 4th International Conference on Materials Engineering for Resources (The Society of Materials Engineering for Resources of Japan, Akita, Japan, 2001), p. 1.Google Scholar
Fray, D.J., J. Met. 26 (Oct 2001).Google Scholar
Glowacki, B.A., Yan, X.Y., Fray, D.J., Chen, G., Majoros, M., Shi, Y., Physica C (in press).Google Scholar
Yan, X.Y. and Fray, D.J., Light Met. 5 (2002).Google Scholar
Yan, X.Y. and Fray, D.J., Metall. Mater. Trans. B (in press).Google Scholar
Yan, X.Y. and Fray, D.J. (submitted for publication).Google Scholar
Outokumpu, H.S.C., Chemistry for Windows, version 4.0 (Outokumpu Research Oy Information Service, Pori, Finland, 1999).Google Scholar
Rao, Y.K., Stoichiometry and Thermodynamics of Metallurgical Processes (Cambridge University Press, London, U.K., 1985), p. 883.Google Scholar
Okabe, T.H., Park, I., Jacob, K.T., and Waseda, Y., J. Alloys Compd. 288, 200 (1999).CrossRefGoogle Scholar
Park, I., Okabe, T.H., Waseda, Y., Yu, H.S., and Lee, O.Y., Mater. Trans. 42, 850 (2001).CrossRefGoogle Scholar
Roberge, R., in Superconductor Materials Science, edited by Foner, S. and Schwartz, B.B. (Plenum Press, New York, 1981), p. 442.Google Scholar
Chartrand, P. and Pelton, A.D., Metall. Mater. Trans. A 32A, 1361 (2001).Google Scholar
Chartrand, P. and Pelton, A.D., Can. Met. Q. 40, 13 (2000).CrossRefGoogle Scholar
Levin, E.M. and Mc, H.F.Murdie, Phase Diagrams for Ceramists-Supplement (The American Ceramic Society, Westerville, OH, 1975).Google Scholar
Boghosian, S., Godo, A.A., Mediaas, H., Ravlo, W., and Ostvold, T., Acta Chem. Scand. 45, 145 (1991).CrossRefGoogle Scholar
Halbritter, J., IEEE Trans. Magn. MAG–21, 858 (1985).CrossRefGoogle Scholar
Halbritter, J., J. Less-Common Met. 139, 133 (1988).CrossRefGoogle Scholar
Kirchheim, R., Acta Metall. 27, 869 (1979).CrossRefGoogle Scholar
Bard, A.J. and Faulkner, L.R., Electrochemical Methods, 2nd ed. (John Wiley & Sons, New York, 2001), pp. 423–425.Google Scholar
Delahay, P., New Instrumental Methods in Electrochemistry (Interscience Publishers, New York, 1954), pp. 218–219, 283–284.Google Scholar
Szekely, J., Evans, J.W., and Sohn, H.Y., Gas-Solid Reactions (Academic Press, New York, 1976), pp. 73–78.Google Scholar
Hulm, J.K. and Matthias, B.T., in Superconductor Materials Science, edited by Foner, S., Schwartz, B.B. (Plenum Press, New York, 1981), p. 28.Google Scholar