Tungsten nitride thin films prepared by MOCVD

Published online by Cambridge University Press:  31 January 2011

Hsin-Tien Chiu  and
Shiow-Huey Chuang
Hsin-Tien Chiu
Affiliation:
Department of Applied Chemistry, National Chiao Tung University, Hsinchu, Taiwan 30050, Republic of China
Shiow-Huey Chuang
Affiliation:
Department of Applied Chemistry, National Chiao Tung University, Hsinchu, Taiwan 30050, Republic of China
Get access

Abstract

Polycrystalline tungsten nitride thin films were grown by low pressure metallo-organic chemical vapor deposition (MOCVD) using (tBuN)2W(NHtBu)2 as the single-source precursor. Deposition of uniform thin films on glass and silicon substrates was carried out at temperatures 723–923 K in a cold-wall reactor, while the precursor was vaporized at 333–363 K. The growth rates were 2–10 nm/min depending on the condition employed. Bulk elemental composition of the thin films, studied by wavelength dispersive spectroscopy (WDS), is best described as WNx (x = 0.7–1.8). The N/W ratio decreased with increasing temperature of deposition. X-ray diffraction (XRD) studies showed that the films have cubic structures with the lattice parameter a = 0.414–0.418 nm. The lattice parameter decreased with decreasing N/W ratio. Stoichiometric WN thin films showed an average lattice parameter a of 0.4154 nm. X-ray photoelectron spectroscopy (XPS) showed that binding energies of the W4f7/2, W4f5/2, and N1s electrons were 33.0, 35.0, and 397.3 eV, respectively. Elemental distribution within the films, studied by secondary ion mass spectroscopy (SIMS) and Auger spectroscopy depth profilings, was uniform. The SIMS depth profiling also indicated that C and O concentrations were low in the film. Volatile products trapped at 77 K were analyzed by gas chromatography–mass spectroscopy (GC–MS) and nuclear magnetic resonance (NMR). Isobutylene, acetonitrile, hydrogen cyanide, and ammonia were detected in the condensable mixtures. Possible reaction pathways were proposed to speculate the origin of these molecules.

Type
Articles
Information
Journal of Materials Research , Volume 8 , Issue 6 , June 1993 , pp. 1353 - 1360
Copyright
Copyright © Materials Research Society 1993

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1Boher, P., Houdy, P., Kaikati, P., and Ijzendoorn, L. J. Van, J. Vac. Sci. Technol. A8, 846 (1990).CrossRefGoogle Scholar
2Deneuville, A., Benyahya, M., Brunei, M., Oberlin, J. C., Torres, J., Bourhila, N., Paleau, J., and Canut, B., Appl. Surf. Sci. 38, 179 (1989).CrossRefGoogle Scholar
3Lalinsky, T., Kuzmik, J., Gregusova, D., Mozolova, Z., Breza, J., Fecisko, M., and Seidl, P., J. Mater. Sci.: Mater. Electron. 3, 157 (1992).Google Scholar
4Lee, J.S., Park, C.S., Yang, J.W., Kang, J.Y., and Ma, D.S., J. Appl. Phys. 67, 1134 (1990).CrossRefGoogle Scholar
5Kim, Y.T. and Min, S-K., Appl. Phys. Lett. 53, 929 (1991).CrossRefGoogle Scholar
6Kilbane, F.M. and Habig, P.S., J. Vac. Sci. Technol. 12, 107 (1975).CrossRefGoogle Scholar
7Matsumoto, O., Shiiato, Y., and Hayakawa, Y., J. Electiochem.Google Scholar
8Iwama, S., Hayakawa, K., and Arizumi, T., J. Cryst. Growth 66, 189 (1984).CrossRefGoogle Scholar
9Volpe, L. and Boudart, M., J. Solid State Chem. 59, 332 (1985).CrossRefGoogle Scholar
10Landingham, R. L. and Austin, J. H., J. Less-Comm. Met. 18, 229 (1969).CrossRefGoogle Scholar
11Nakajima, T., Watanabe, K., and Watanabe, N., J. Electrochem. Soc. 134, 3175 (1987).CrossRefGoogle Scholar
12Chiu, H-T. and Chang, W-P., Mater, J.. Sci. Lett. 11, 96 (1992).CrossRefGoogle Scholar
13Winter, C. H., Sheridan, P. H., Lewkebandara, T. S., Heeg, M. J., and Proscia, J.W., J. Am. Chem. Soc. 114, 1095 (1992).CrossRefGoogle Scholar
14Preliminary results were communicated; Chiu, H-T. and Chuang, S-H., in Chemical Vapor Deposition of Refractory Metals and Ceramics II, edited by Besmann, T. M., Gallois, B. M., and Warren, J. W. (Mater. Res. Soc. Symp. Proc. 250, Pittsburgh, PA, 1992), p. 317.Google Scholar
15Nugent, W. A. and Harlow, R.L., Inorg. Chem. 19, 777 (1980).CrossRefGoogle Scholar
16Powder Diffraction File, JCPDS (International Center for Diffraction Data, Swarthmore, PA, 1982), File No. 25–1257.Google Scholar
17Colton, R.J. and Rabalais, J.W., Inorg. Chem. 15, 236 (1976).CrossRefGoogle Scholar
18Ingrey, S., Johnson, M.B., Streater, R.W., and Sproule, G.I., J. Vac. Sci. Technol. 20, 968 (1982)CrossRefGoogle Scholar
19Currie, A.L. and Howard, K.E., J. Mater. Sci. 27, 2739 (1992).CrossRefGoogle Scholar
20Lyutaya, M. D., Poroshk. Metall. (Kiev) 3, 60 (1979).Google Scholar
21Bent, B. E., Nuzzo, R. G., and Dubois, L. H., J. Am. Chem. Soc. 111, 1634 (1989).CrossRefGoogle Scholar
22Fix, R.M., Gordon, R.G., and Hoffman, D.M., Chem. Mater. 2, 235 (1990).CrossRefGoogle Scholar
23Rutherford, N.M., Larson, C.E., and Jackson, R.L., in Chemical Perspectives of Microelectronic Materials, edited by Gross, M. E., Jasinski, J., and Yates, J. T. Jr, (Mater. Res. Soc. Symp. Proc. 131, Pittsburgh, PA, 1989), p. 439.Google Scholar
24Laine, R. M. and Hirschon, A. S., in Transformation of Organometallics into Common and Exotic Materials: Design and Activation, edited by Laine, R. M. (Martinus Nijhoff, Dordrecht, The Netherlands, 1988), p. 21.CrossRefGoogle Scholar
25Fix, R. M., Gordon, R. G., and Hoffman, D. M., J. Am. Chem. Soc. 112, 7833 (1990).CrossRefGoogle Scholar
26Fix, R. M., Gordon, R. G., and Hoffman, D. M., Chem. Mater. 3, 1138 (1991).CrossRefGoogle Scholar
27Gordon, R.G., Riaz, U., and Hoffman, D.M., J. Mater. Res. 7, 1679 (1992).CrossRefGoogle Scholar
28Lu, J-P. and Raj, R., J. Mater. Res. 6, 1913 (1991).CrossRefGoogle Scholar
29Gebeyehu, Z., Weller, F., Neumiiller, B., and Dehnicke, K., Z. Anorg. Allg. Chem. 593, 99 (1991).CrossRefGoogle Scholar