Thermal Stability and Wetting Properties of Cr–O–C Coatingssynthesized by Plasma Immersion Ion Processing

Published online by Cambridge University Press:  31 January 2011

Xiao-Ming He
Affiliation:
Los Alamos National Laboratory, Los Alamos, New Mexico 87545
Marko Hakovirta
Affiliation:
Los Alamos National Laboratory, Los Alamos, New Mexico 87545
Kevin C. Walter
Affiliation:
Los Alamos National Laboratory, Los Alamos, New Mexico 87545
Mitchell Trkula
Affiliation:
Los Alamos National Laboratory, Los Alamos, New Mexico 87545
Michael Nastasi
Affiliation:
Los Alamos National Laboratory, Los Alamos, New Mexico 87545
Get access

Abstract

Microcrystalline Cr-O-C films, synthesized by the plasma immersion ion processing technique, were annealed in vacuum and air at 700 °C for different times so their thermal stability could be evaluated. The study showed that annealing does not greatly change the chemical composition of the Cr–O–C films but induces a transformation ofthe film structure from the mixed phases of Cr2O3, CrO2, and CrC1.13O0.12 to the dualphases of Cr3C2, and Cr2O3. In addition, the annealed Cr–O–C films exhibit excellentnonwetting qualities to liquid aluminum despite the presence of pin holes. The contactangle of resolidified molten aluminum against the Cr–O–C films was found to be ashigh as 120–150°. The aluminum contact angle was found not to vary with thermal aging of the Cr–O–C films. The Cr–O–C films showed high hardness (16–24 GPa) and good wear resistance as compared to the steel substrates (H13 and 304 stainless steels)used in this study.

Type
Articles
Copyright
Copyright © Materials Research Society 2002

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

Handbook of Thin Film Process Technology, Rej, D.J. (Institute of Physics, Philadelphia, PA, 1996), Chap. E2.3.Google Scholar
Nastasi, M., He, X-M., Walter, K.C., Hakovirta, M., and Trkula, M., Surface & Coatings Technology 136, 162 (2001).CrossRefGoogle Scholar
Tuszewski, M., Henins, I., Nastasi, M., Scarborough, W.K., Walter, K.C., and Lee, D.H., IEEE Trans. Plasma Sci. 26, 1653 (1998).CrossRefGoogle Scholar
Handbook of Modern Ion Beam Materials Analysis, Tesmer, J.R. and Nastasi, M., (Materials Research Society, Pittsburgh, PA, 1995) Chaps. 6 and 7.Google Scholar
Doolittle, L.R., Nucl. Instrum. Meth. B9, 344 (1985).CrossRefGoogle Scholar
Doolittle, L.R., Nucl. Instrum. Meth. B 15, 227 (1986).CrossRefGoogle Scholar
He, X-M., Baker, N., Kehler, B.A., Walter, K.C., Nastasi, M., and Nakamura, Y., Vac. Sci. Technol. A 18, 30 (2000).CrossRefGoogle Scholar
Chemical Thermodynamics of Materials, Lupis, C.H.P. (North-Holland, Amsterdam, The Netherlands, 1983), Chap. XIII, p. 374.Google Scholar