Synthesis and characterization of partially and fully stabilized zirconia fibers made from an inorganic precursor

Published online by Cambridge University Press:  31 January 2011

A. Hartridge ,
M. D. Taylor  and
A. K. Bhattacharya
A. Hartridge
Affiliation:
Warwick Process Technology Group, Department of Engineering, University of Warwick, Coventry CV4 7AL, United Kingdom
M. D. Taylor
Affiliation:
Warwick Process Technology Group, Department of Engineering, University of Warwick, Coventry CV4 7AL, United Kingdom
A. K. Bhattacharya*
Affiliation:
Warwick Process Technology Group, Department of Engineering, University of Warwick, Coventry CV4 7AL, United Kingdom
*
a)Address all correspondence to this author.
Get access

Abstract

Continuous high-quality fibers of yttria-doped zirconia with 4 and 8 mol% yttria were blow spun using an inorganic sol precursor. The fibers were heated and analyzed using scanning electron microscopy, x-ray diffraction, differential thermal/thermogravimetric analysis, and surface area/porosity by nitrogen adsorption. The fibers were of a single-phase cubic structure after crystallization at 529 °C and typically 3.3–5.5 or 7.5–11.5 μm in diameter depending on the composition. Samples of fibers were heated to various temperatures and their friability index and creep properties analyzed using the bend stress relaxation technique and compared to other fibers of similar composition prepared by different solution techniques and commercially available fibers.

Type
Articles
Information
Journal of Materials Research , Volume 16 , Issue 8 , August 2001 , pp. 2384 - 2390
Copyright
Copyright © Materials Research Society 2001

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1Pullar, R.C., Taylor, M.D., and Bhattacharya, A.K., J. Eur. Ceram. Soc. 21, 19 (2000).CrossRefGoogle Scholar
2Bhattacharya, A.K., Hartridge, A., Mallick, K.K., and Taylor, M.D., J. Mater. Sci. 31, 5583 (1996).CrossRefGoogle Scholar
3Pullar, R.C., Taylor, M.D., and Bhattacharya, A.K., J. Mater. Sci. 33, 3229 (1998).CrossRefGoogle Scholar
4Hartridge, A., Mallick, K.K., Taylor, M.D., and Bhattacharya, A.K., Mater. Sci. Lett. 15, 1654 (1996).Google Scholar
5Pullar, R.C., Taylor, M.D., and Bhattacharya, A.K., J. Eur. Ceram. Soc. 18, 1759 (1998).CrossRefGoogle Scholar
6Naumann, A.W. and Gortsena, F.P., Union Carbide Corp., German Offen. 2007209 (Cl.C01b) (1990), U.S. Priority (1969).Google Scholar
7Morton, M.J., Birchall, J.D., and Cassidy, J.E., Patent, U.K. Speci-fication 1360197 (17 July 1974).Google Scholar
8Shozo, H., Kozo, T., Yasuaki, A., and Akio, F., Sumitomo, Japan Kokai 74134928 (Cl.42 E0) (1974), Appl. 7351398 (1973).Google Scholar
9Garvie, R.C., Hannink, R.H., and Pascoe, R.T., Nature 258, 703 (1975).CrossRefGoogle Scholar
10Marshall, D.B., Lange, F.F., and Morgan, P.D., J. Am. Ceram. Soc. 70, C–188 (1987).Google Scholar
11Yogo, T., J. Mater. Sci. 25, 2394 (1990).CrossRefGoogle Scholar
12Chatterjee, G.De.A. and Ganguli, D., J. Mater. Sci. Lett.9, 845 (1990).Google Scholar
13Abe, Y., Kudo, T., Tomioka, H., Gunji, T., Nagao, Y., and Misono, T., J. Mater. Sci. 33, 1867 (1998).CrossRefGoogle Scholar
14Clauss, B., Gruh, A., and Oppermann, W., Adv. Mater. 8, 143 (1996).CrossRefGoogle Scholar
15Fine Ceramic Fibres, edited by Bunsell, A.R. and Berger, M.H. (Marcel Dekker, New York, 1999), Chapter 2, p. 76.Google Scholar
16Brinker, C.J. and Assink, R.A., J. Non-Cryst. Solids 111, 48 (1989).CrossRefGoogle Scholar
17Fine Ceramic Fibres, edited by Bunsell, A.R. and Berger, M.H. (Marcel Dekker, New York, 1999), Chapter 2, p. 45.Google Scholar
18Tsubakino, H., Hamamoto, R., and Nozato, R., J. Mater. Sci. 26, 5521 (1991).CrossRefGoogle Scholar
19Hughes, A.E., Interfacial Phenomena in Y2O3-ZrO2 based ceramics, Science of Ceramic Interfaces II, edited by Novotny, J. (Elsevier, New York, 1994).Google Scholar
20 20. Badwal, S.P.D., Drennan, J., Hannink, R.H.J., and Hughes, A.E., Influence of Interfaces on the Properties and Performance of Zirconia Based Advanced Ceramics (Trans Tech Publications, Uetikon-Zuerich, Switzerland, 1995), Key Eng. Mater. 111–112, 109 (1995).Google Scholar
21Taylor, M.D. and Bhattacharya, A.K., J. Mater. Sci. 34, 1277 (1999).CrossRefGoogle Scholar
22Brook, R.J., Proc. Br. Ceram. Soc. 32, 7 (1982).Google Scholar
23Karst, K.A. and Sowman, H.G., U.S. Patent 4,047, 965 (1977).Google Scholar
24Norscher, G.N. and DiCarlo, J.A., J. Am. Ceram. Soc. 75, 136 (1992).CrossRefGoogle Scholar
25Ong, C.L., Wang, J., Ng, S.C., and Gan, L.M., J. Am. Ceram. Soc. 81, 2624 (1998).CrossRefGoogle Scholar
26Miller, , Metallurgy of the Rarer Metals, Zirconium, 2nd ed. (But-terworths Scientific Publications, London, United Kingdom, 1957), p. 91.Google Scholar