Silicon carbide fiber-reinforced alumina extrusion

Published online by Cambridge University Press:  03 March 2011

S. Blackburn*
Affiliation:
Interdiscipilinary Research Centre, in Materials for High Performance Applications, The University of Birmingham, Edgbaston, Birmingham, B15 2TT. United Kingdom
H. Böhm
Affiliation:
Interdiscipilinary Research Centre, in Materials for High Performance Applications, The University of Birmingham, Edgbaston, Birmingham, B15 2TT. United Kingdom
*
a)Also a member of the School of Chemical Engineering.
Get access

Abstract

Silicon carbide fiber-reinforced alumina bodies have been produced by ram extrusion. The Al2O3 powder and SiC fiber were milled together to give a dry dispersion of up to 30 vol % fiber which was subsequently mixed to a paste by high shear kneading using hydroxypropylmethylcellulose solutions as the binder phase. Extruded bodies with green densities ranging between 56 and 63% full theoretical density were achieved. The paste flow behavior was characterized using physically based equations which show that for any given moisture content the pressure drop and the constituent paste parameters are all systematically reduced as the fiber loading is increased. This observation can be explained almost completely by combining packing theory with the paste rheology data. Fiber interactions within the paste and the die system appear not to greatly influence the rheological character of the material. It is shown statistically that the fibers are homogeneously dispersed throughout the paste mass after extrusion. Image analysis has been used to aid in macrodefect analysis, and it is shown that the optimum concentration of fiber was 20 vol % with a quantity of binder sufficient to give an initial yield stress of 2 MPa.

Type
Articles
Copyright
Copyright © Materials Research Society 1995

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1Coyle, J. W., Guyot, M. H., and Jamet, J.F., Ceram. Eng. Sci. Proc. 7 (78), 947 (1986).Google Scholar
2Nieto, M. I., Miranzo, P., Moya, J. S., and de Aza, S., Euro. Ceram. 2, DGK, 1431 (1991).Google Scholar
3Homeny, J., Vaughn, W. L., and Ferber, M. K., Am. Ceram. Soc. Bull. 67, 333 (1987).Google Scholar
4Hanney, M. J. and Morrell, R., Proc. Br. Ceram. Soc. 32, 277 (1982).Google Scholar
5Alford, N. McN., Birchall, J. D., and Kendall, K., Nature (London) 333, 51 (1987).Google Scholar
6Benbow, J. J., Lawson, T. A., Oxley, E. W., and Bridgwater, J., Am. Ceram. Soc. Bull. 68(10), 1821 (1989).Google Scholar
7Blackburn, S., Proc. Br. Ceram. Soc. 50, 9 (1993).Google Scholar
8Blackburn, S. and Lawson, T. A., J. Am. Ceram. Soc. 75(4), 953 (1992).CrossRefGoogle Scholar
9Willson, M. C., Edrees, H. J., and Kerr, A., Proc. Br. Ceram. Soc. 50, 83 (1993).Google Scholar
10Benbow, J. J., Oxley, E. W., and Bridgwater, J., Chem. Eng. Sci. 42, 2151 (1987).Google Scholar
11Böhm, H. and Blackburn, S., Br. Ceram. Trans. 93, (5), 169 (1994).Google Scholar
12Edirisinghe, M. J. and Evans, J. R. G., Proc. Br. Ceram. SOC. 38, 67 (1986).Google Scholar
13Clarke, B., Trans. Inst. Chem. Eng. 45, 551 (1967).Google Scholar
14Taso, I. and Danforth, S. C., J. Am. Ceram. Soc. 76(12), 2977 (1993).Google Scholar
15Stedman, J. and Evans, J. R. G., J. Mater. Sci. 25, 1833 (1990).CrossRefGoogle Scholar
16Blackburn, S. and Böhm, H., J. Mater. Sci. 29, 4157 (1994).CrossRefGoogle Scholar
17Benbow, J. J., Ouchiyama, N., and Bridgwater, J., Chem. Eng. Comm. 62, 203 (1987).Google Scholar
18Milewski, J. V., Ceram. Eng. Sci. Proc. 12 (78), 1095 (1991).Google Scholar
19Karlsson, K. and Spring, L., J. Mater. Sci. 5, 340 (1970).CrossRefGoogle Scholar