Processing of Bi–Sr–Ca–Cu–O glasses using platinum and alumina crucibles

Published online by Cambridge University Press:  31 January 2011

T.G. Holesinger ,
D.J. Miller ,
S. Fleshler  and
L.S. Chumbley
T.G. Holesinger
Affiliation:
Materials Science Division and Science and Technology Center for Superconductivity, Argonne National Laboratory, Argonne, Illinois 60439
D.J. Miller
Affiliation:
Materials Science Division and Science and Technology Center for Superconductivity, Argonne National Laboratory, Argonne, Illinois 60439
S. Fleshler
Affiliation:
Materials Science Division and Science and Technology Center for Superconductivity, Argonne National Laboratory, Argonne, Illinois 60439
L.S. Chumbley
Affiliation:
Ames Laboratory and Iowa State University, Ames, Iowa 50011
Get access

Abstract

Reactions with alumina and platinum crucibles were studied during the preparation of Bi2Sr2Ca1Cu2Oy “2212” glasses. In particular, reactions with Al2O3 are of interest since alumina is a potential substrate material in applications of this superconductor. Glasses processed using alumina crucibles were completely homogeneous and free of secondary phases although the material contained 2.26 at. % Al in solution. After heat treatments, Al was found in the form of SrCaAlOy particles located primarily along grain boundaries of the 2212 superconducting phase. Platinum contamination was minimal (<0.02 at. %) and no Pt-containing secondary phases were found in amorphous or annealed samples. Glasses made with Pt crucibles were found to contain small amounts of CaO, Sr14−xCaxCu24O41, and 2201 as second phases. Differential thermal analysis (DTA) suggested that the crystallization processes were essentially the same for all samples although the small amount of Al seemed to slow the kinetics leading to the formation of 2212. Neither Al nor Pt was detected within the 2212 phase. The measured superconducting compositions in each annealed sample were nearly the same with identical transition temperatures of 88 K. Overall differences in stoichiometry were accommodated by changes in the number and composition of the secondary phases present.

Type
Articles
Information
Journal of Materials Research , Volume 7 , Issue 8 , August 1992 , pp. 2035 - 2039
Copyright
Copyright © Materials Research Society 1992

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

1.Michel, C., Hervieu, M., Boiel, M. M., Grandin, A., Deslandes, F., Provost, J., and Raveau, B., Z. Phys. B 68, 421 (1987).CrossRefGoogle Scholar
2.Maeda, H., Tanaka, Y., Fukutomi, M., and Asano, T., Jpn. J. Appl. Phys. Lett. 27, L209 (1988).CrossRefGoogle Scholar
3.Hinks, D. G., Soderholm, L., Capone, D. W., II, Dabrowski, B., Mitchell, A. W., and Shi, D., Appl. Phys. Lett. 53, 423–425 (1988).CrossRefGoogle Scholar
4.Nassau, K., Miller, A. E., Gyorgy, E. M., and Siegrist, T., J. Mater. Res. 4, 1330–1338 (1989).CrossRefGoogle Scholar
5.DeGuire, M. R., Bansal, N. P., and Kim, C. J., J. Am. Ceram. Soc. 73, 1165–1171 (1990).CrossRefGoogle Scholar
6.Holesinger, T. G., Miller, D. J., and Chumbley, L. S., J. Mater. Res. 7, 1658–1671 (1992).CrossRefGoogle Scholar
7.Komatsu, T., Sato, R., Hirose, C., Matusita, K., and Yamashita, T., Jpn. J. Appl. Phys. 27, L2293–2295 (1988).CrossRefGoogle Scholar
8.Vandervoort, K. G., Griffith, G., Claus, H., and Crabtree, G. W., Rev. Sci. Instrum. 62, 2271–2275 (1991).CrossRefGoogle Scholar
9.Siegrist, T., Schneemeyer, L. F., Sunshine, S. A., Waszczak, J. V., and Roth, R. S., Mater. Res. Bull. XXIII, 1429–1438 (1988).CrossRefGoogle Scholar
10.Rawson, H., Inorganic Glass-Forming Systems (Academic Press, New York, 1967), p. 9.Google Scholar