Low friction coatings of diamond-like carbon with silicon prepared by plasma-assisted chemical vapor deposition

Published online by Cambridge University Press:  31 January 2011

K. Oguri  and
T. Arai
K. Oguri
Affiliation:
Toyota Central Research & Development Laboratories, Inc., 41-1, Aza Yokomichi, Oaza Nagakute, Nagakute-cho, Aichi-gun, Aichi-ken, 480-11, Japan
T. Arai
Affiliation:
Toyota Central Research & Development Laboratories, Inc., 41-1, Aza Yokomichi, Oaza Nagakute, Nagakute-cho, Aichi-gun, Aichi-ken, 480-11, Japan
Get access

Abstract

Amorphous carbon-silicon (a–C–Si) coatings with smooth surface and adhesion to steel substrate were deposited at 550°C by a dc glow discharge method from reactant gases of CH4, SiCl4, H2, and Ar at a deposition rate of 1–3 μm h−1. Diamond-like carbon was detected by laser Raman spectroscopy in the coatings with high hardness of Hv 2000 and more than 70 at. % carbon. Ball-on-disk type and Ohgoshi-type apparatuses were used to measure the tribological properties. Ball-on-disk tests revealed that the a–C–Si coatings showed a friction coefficient as low as 0.04 against steel with no lubricant in an ambient atmosphere of 70% relative humidity, which was one-third that of an i–C coating. The wear rate of the steel ball against the coated disk was an order and three orders of magnitude smaller than that against i–C coated and uncoated disks, respectively. Both types of tests showed that the wear rate of the a–C–Si coating itself was also very small.

Type
Diamond and Diamond-Like Materials
Information
Journal of Materials Research , Volume 5 , Issue 11 , November 1990 , pp. 2567 - 2571
Copyright
Copyright © Materials Research Society 1990

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1Weissmantel, C., Bewilogua, K., Breuer, K., Dietrich, D., Ebersbach, U., Erler, H-J., Rau, B., and Reisse, G., Thin Solid Films 96, 31 (1982).Google Scholar
2Dimigen, H., Hübsch, H., and Memming, R., Appl. Phys. Lett. 50, 1056 (1987).Google Scholar
3Braun, M., Nucl. Instrum. Methods B 39, 544 (1989).CrossRefGoogle Scholar
4Hioki, T., Itoh, Y., Hibi, S., and Kawamoto, J., submitted to Thin Solid Films.Google Scholar
5Enke, K., Dimigen, H., and Hübsch, H., Appl. Phys. Lett. 36, 291 (1980).Google Scholar
6Memming, R., Tolle, H. J., and Wierenga, P. E., Thin Solid Films 143, 31 (1986).CrossRefGoogle Scholar
7Imanura, A., Tsukamoto, T., Shibuki, K., and Takatsu, S., Surface and Coatings Technology 36, 161 (1988).CrossRefGoogle Scholar
8Oguri, K. and Arai, T., Thin Solid Films 186, L29 (1990).CrossRefGoogle Scholar
9Arai, T., Fujita, H., and Oguri, K., Thin Solid Films 165, 139 (1988).CrossRefGoogle Scholar
10Oguri, K. and Arai, T., Proc. 2nd Jpn. Symp. Plasma Chem., Nagoya, 1989, Organizing Committee of Japanese Symposium on Plasma Chemistry, 1989, p. 197.Google Scholar
11Hintermann, H. E., J. Vac. Sci. Technol. B2, 816 (1984).Google Scholar