High-temperature stability of epitaxial, non-isostructural Mo/NbN superlattices

Published online by Cambridge University Press:  31 January 2011

C. Engström ,
A. Madan ,
J. Birch ,
M. Nastasi ,
L. Hultman  and
S. A. Barnett
C. Engström
Affiliation:
Advanced Coating Technology Group and Department of Materials Science and Engineering, Northwestern University, Evanston, Illinois, and Physics Department, Linköping University, Sweden
A. Madan
Affiliation:
Advanced Coating Technology Group and Department of Materials Science and Engineering, Northwestern University, Evanston, Illinois
J. Birch
Affiliation:
Physics Department, Linköping University, Sweden
M. Nastasi
Affiliation:
Los Alamos National Laboratory, Los Alamos, New Mexico
L. Hultman
Affiliation:
Physics Department, Linköping University, Sweden
S. A. Barnett
Affiliation:
Advanced Coating Technology Group and Department of Materials Science and Engineering, Northwestern University, Evanston, Illinois
Get access

Abstract

The effect of 1000 °C vacuum annealing on the structure and hardness of epitaxial Mo/NbN superlattice thin films was studied. The intensity of superlattice satellite peaks, measured by x-ray diffraction, decreased during annealing while new peaks corresponding to a MoNbN ternary phase appeared. The results are consistent with the Mo–Nb–N phase diagram, which shows no mutual solubility between Mo, NbN, and MoNbN. Even after 3-h anneals and a loss of most of the superlattice peak intensity, the room-temperature hardness was the same as for as-deposited superlattices. The retained hardness suggests that a residual nanocomposite structure is retained even after the formation of the ternary structure.

Type
Articles
Information
Journal of Materials Research , Volume 15 , Issue 2 , February 2000 , pp. 554 - 559
Copyright
Copyright © Materials Research Society 2000

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1.Sproul, W.D., J. Vac. Sci. Technol. A4, 2874 (1986).CrossRefGoogle Scholar
2.Barnett, S.A., in Physics of Thin Films, edited by Francombe, M. and Vossen, J.A. (Academic Press, New York, 1993).Google Scholar
3.Engström, C., Birch, J., Hultman, L., Lavoie, C., Cabral, C., Jordan-Sweet, J.L., and Carlsson, J.R.A, J. Vac. Sci. Technol. A 17, 2920 (1999).CrossRefGoogle Scholar
4.Madan, A., Chu, Xi, and Barnett, S.A., Appl. Phys. Lett. 68, 2198 (1996).CrossRefGoogle Scholar
5.Madan, A., Wang, Y-Y., Barnett, S.A., Engström, C., Ljungcrantz, H., Hultman, L., and Grimsditch, M., J. Appl. Phys. 84, 776 (1998).CrossRefGoogle Scholar
6.Villars, P., Prince, A., and Okamoto, H., Handbook of Ternary Alloy Phase Diagrams (ASM International, Materials Park, OH, 1995).Google Scholar
7.Mirkarimi, P.B., Shinn, M., Hultman, L., and Barnett, S.A., J. Vac. Sci. Technol. A 10, 75 (1992).CrossRefGoogle Scholar
8.Birch, J., Sundgren, J-E., and Fewster, P., J. Appl. Phys. 78, 6562 (1995).CrossRefGoogle Scholar
9.Ljungcrantz, H., Odén, M., Hultman, L., Greene, J.E., and Sundgren, J-E., J. Appl. Phys. 80, 6725 (1996).CrossRefGoogle Scholar
10.Oliver, W.C. and Pharr, G.M., J. Mater. Res. 7, 1564 (1992).CrossRefGoogle Scholar
11. Powder Diffraction File No. 33–0928 (JCPDS International Center for Diffraction Data 1997).Google Scholar
12.Engström, C., Hultman, L., Madan, A., Barnett, S.A., Nastasi, M. and Lavoie, C. (unpublished).Google Scholar