Electron microscope study of Synroc before and after exposure to aqueous solutions

Published online by Cambridge University Press:  31 January 2011

Gregory R. Lumpkin ,
Katherine L. Smith  and
Mark G. Blackford
Gregory R. Lumpkin
Affiliation:
Australian Nuclear Science and Technology Organisation, Lucas Heights Research Laboratories, PMB 1, Menai 2234, Australia
Katherine L. Smith
Affiliation:
Australian Nuclear Science and Technology Organisation, Lucas Heights Research Laboratories, PMB 1, Menai 2234, Australia
Mark G. Blackford
Affiliation:
Australian Nuclear Science and Technology Organisation, Lucas Heights Research Laboratories, PMB 1, Menai 2234, Australia
Get access

Abstract

A well-characterized Synroc was subjected to durability tests in de-ionized water at 70 °C and 150 °C, and silicate and bicarbonate solutions at 70 °C, to study the effect of temperature and solution composition on the mechanisms of aqueous alteration. SEM and TEM were used before and after durability experiments to characterize the primary and secondary phases in and on the Synroc samples, and to describe changes in morphology and chemistry. Leachant compositions after durability testing were analyzed using ICP/OES and ICP/MS and have been reported elsewhere.8 After durability testing, titaniferous surface layers were observed primarily on perovskite, the most soluble Synroc phase. Electron microscopy demonstrates that the surface layer formed at 70 °C is an amorphous Ti–O film and is fine grained anatase at 150 °C. Congruent dissolution is the major mechanism of perovskite alteration. However, at 150 °C, selective loss of Ca and Sr may occur locally. A number of additional secondary phases were identified, including Al–oxide/hydroxide, Fe–oxide, REE-bearing Ti–oxides, and several silicate phases. The abundance and composition of the secondary phases are related to solution composition and temperature.

Type
Articles
Information
Journal of Materials Research , Volume 6 , Issue 10 , October 1991 , pp. 2218 - 2233
Copyright
Copyright © Materials Research Society 1991

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

1.Ringwood, A. E., Kesson, S. E., Reeve, K. D., Levins, D. M., and Ramm, E. J., in Radioactive Waste Forms for the Future, edited by Lutze, W. and Ewing, R. C. (North-Holland, Amsterdam, 1988), p. 233.Google Scholar
2.Fielding, P. E. and White, T. J., J. Mater. Res. 2, 387 (1987).CrossRefGoogle Scholar
3.Buykx, W. J., Levins, D. M., R.St.Smart, C., Smith, K. L., Stevens, G. T., Watson, K. G., Weedon, D., and White, T. J., J. Am. Ceram. Soc. 73, 1201 (1990).CrossRefGoogle Scholar
4.Reeve, K. D., Levins, D. M., Seatonberry, B. W., Ryan, R. K., Hart, K. P., and Stevens, G. T., Fabrication and Study of Synroc Containing Radioactive Waste Elements, Australian Atomic Energy Commission, Final Report to NERDDP on Project 498 (1987).Google Scholar
5.Solomah, A. G. and Matzke, Hj., in Scientific Basis for Nuclear Waste Management XII, edited by Lutze, W. and Ewing, R. C. (Mater. Res. Soc. Symp. Proc. 127, Pittsburgh, PA, 1989), p. 241.Google Scholar
6.Kastrissios, T., Stephenson, M., Turner, P. S., and White, T. J., J. Am. Ceram. Soc. 70, C144 (1987).CrossRefGoogle Scholar
7.Pham, D. K., Chemical Durability of Perovskite (CaTiO3) and Thermodynamic Factors Affecting Synroc Dissolution, Ph.D. Dissertation, Griffith University, Brisbane, Qld., Australia (1989).Google Scholar
8.Smith, K. L., Hart, K. P., Lumpkin, G. R., McGlinn, P., Lam, P., and Blackford, M. G., in Scientific Basis for Nuclear Waste Management XIV (Mater. Res. Soc. Symp. Proc. 212, Pittsburgh, PA, 1991), p. 167.Google Scholar
9. MCC, MCC-1P Static Leach Test Method, Materials Characterization Center, Battelle Northwest Laboratory, Richland, WA (1983).Google Scholar
10. MCC, MCC-2S Agitated Powder Leach Test Method, Materials Characterization Center, Battelle Northwest Laboratory, Richland, WA (1984).Google Scholar
11.Cooper, J. A., Cousens, D. R., Lewis, R. A., Myhra, S., Segall, R. L., R. St. Smart, C., Turner, P. S., and White, T. J., J. Am. Ceram. Soc. 68, 64 (1985).CrossRefGoogle Scholar
12.Murakami, T., Nucl. Chem. Waste Management 5, 269 (1985).CrossRefGoogle Scholar
13.Kesson, S. E. and White, T. J., Proc. R. Soc. London, A 405, 73 (1986).Google Scholar
14.Pham, D. K., Neall, F. B., Myhra, S., Smart, R. St. C., and Turner, P. S., in Scientific Basis for Nuclear Waste Management XII, edited by Lutze, W. and Ewing, R. C. (Mater. Res. Soc. Symp. Proc. 127, Pittsburgh, PA, 1989), p. 231.Google Scholar
15.Wambeke, L.Van, Neues Jahrb. Mineral. Abh. 112, 117 (1970).Google Scholar
16.Lumpkin, G. R. and Ewing, R. C., in Scientific Basis for Nuclear Waste Management VIII, edited by Jantzen, C. M., Stone, J. A., and Ewing, R. C. (Mater. Res. Soc. Symp. Proc. 44, Pittsburgh, PA, 1985), p. 647.Google Scholar
17.Myhra, S., Delogu, P., Giorgi, R., and Riviere, J. C., J. Mater. Sci. 23, 1514 (1988).CrossRefGoogle Scholar
18.Myhra, S., Smart, R. St. C., and Turner, P. S., Scanning Microscopy 2, 715 (1988).Google Scholar
19.Myhra, S., Bishop, H. E., Riviere, J. C., and Stephenson, M., J. Mater. Sci. 22, 3217 (1987).CrossRefGoogle Scholar
20.Myhra, S., Pham, D. K., Smart, R.St. C., and Turner, P. S., in Scientific Basis for Nuclear Waste Management XIII, edited by Oversby, V. M. and Brown, P. W. (Mater. Res. Soc. Symp. Proc. 176, Pittsburgh, PA, 1990), p. 249.Google Scholar
21.Myhra, S., Smart, R. St. C., Turner, P. S., and Neall, F. B., Scientific and Technical Evaluation of the Synroc Fabrication Program, Griffith University, Final Report to NERDDP on Project 883142 (1986).Google Scholar
22.De Gennes, P. G., Lafore, P., and Millot, J. P., J. Phys. Chem. Solids 11, 105 (1959).CrossRefGoogle Scholar
23.Matzke, Hj., Ray, I. L. F., Seatonberry, B. W., Thiele, H., Trisoglio, C., Walker, C. T., and White, T. J., J. Am. Ceram. Soc. 73, 370 (1990).CrossRefGoogle Scholar
24.Ball, C. J., Buykx, W. J., Dickson, F. J., Hawkins, K., Levins, D. M., Smart, R. St. C., Smith, K. L., Stevens, G. T., Watson, K. G., Weedon, D., and White, T. J., J. Am. Ceram. Soc. 72, 404 (1989).CrossRefGoogle Scholar