Transparent Graphene-Platinum Films for Advancing the Performance of Dye-Sensitized Solar Cells

Published online by Cambridge University Press:  02 September 2013

P. T. Shih ,
R. X. Dong ,
K. C. Ho  and
J. J. Lin
P. T. Shih
Affiliation:
Institute of Polymer Science and Engineering, National Taiwan University, Taipei 10617, Taiwan.
R. X. Dong
Affiliation:
Institute of Polymer Science and Engineering, National Taiwan University, Taipei 10617, Taiwan.
K. C. Ho*
Affiliation:
Institute of Polymer Science and Engineering, National Taiwan University, Taipei 10617, Taiwan. Department of Chemical Engineering, National Taiwan University, Taipei 10617, Taiwan.
J. J. Lin*
Affiliation:
Institute of Polymer Science and Engineering, National Taiwan University, Taipei 10617, Taiwan.
*
*Email: jiangjenlin@gmail.com
*Email: jiangjenlin@gmail.com
Get access

Abstract

Transparent films of platinum nanoparticles on graphene nanohybrids were synthesized in a two-step process. Reduction of homogeneously dispersed Pt precursor and graphene in water and solution coating/annealing afforded thin films with high catalytic performance as counter electrodes in dye-sensitized solar cells (DSSC). The requisite dispersant consisting of poly(oxyethylene)-(POE) segments and cyclic imide functionalities allowed the in-situ reduction of dihydrogen hexachloroplatinate by ethanol and the formation of nanohybrids of graphene-supported Pt nanoparticles at 4.0 nm diameter. Characterizations of polymeric dispersants by Fourier-transform infrared spectroscopy, thermogravimetric analysis, and nanohybrids by transmission electron microscope were performed. After screening various compositions of Pt/graphene, the nanohybrid film at the specific ratio of 5/1 by weight was fabricated into a counter electrode (CE) for DSSC by the solution casting method. The evaluation of cell performance demonstrated the most improved power conversion efficiency of 8.00%. This is significant achievement in comparison with 7.14% for the DSSC with the conventional platinum sputtered CE. Furthermore, the solution casting method allows the preparation of transparent CE films that are suitable for using as rear-illuminated DSSC. The approach was proven to be feasible by measuring the cell efficiency under rear light illumination. The power efficiency up to 7.01%, comparable to 8.00% by a normally front illumination, has been accomplished. In contrast, the rear illumination at merely 2.36% efficiency was obtained for the DSSC with sputtered platinum CE. Analyses of cyclic voltammetry, electrochemical impedance spectra were well correlated to the high efficiency of the performance caused by this nanohybrid film.

Keywords

Cdispersantphotovoltaic
Type
Articles
Information
MRS Online Proceedings Library (OPL) , Volume 1549: Symposium P – Carbon Functional Nanomaterials, Graphene and Related 2D-Layered Systems , 2013 , pp. 47 - 52
Copyright
Copyright © Materials Research Society 2013 

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

Preat, J.; Jacquemin, D.; Perpete, E. A. Environ. Sci. Technol. 2010, 44, 5666–5671.CrossRefGoogle Scholar
Zhang, Y.; Zou, G.; Doom, S. K.; Htoon, H.; Stan, L.; Hawley, M. E.; Sheehan, C. J.; Zhu, Y.; Jia, Q. ACS Nano 2009, 3, 2157–2162.CrossRefGoogle Scholar
Zhang, Y.; Zhang, L.; Kim, P.; Ge, M.; Li, Z.; Zhou, C. Nano Lett. xxxx, xx, xxx–xxx.Google Scholar
Si, Y.; Samulski, E. T. Chem. Mater. 2008, 20, 6792–6797.CrossRefGoogle Scholar
Wei, D.; Liu, Y.; Wang, Y.; Zhang, H.; Huang, L.; Yu, G. Nano Lett. 2009, 9, 1752–1758.CrossRefGoogle Scholar
Worsley, M. A.; Pauzauskie, P. J.; Olson, T. Y.; Biener, J.; Satcher, J. H.; Baumann, T. F. J. Am. Chem. Soc. 2010, 132, 14067–14069.CrossRefGoogle Scholar
Shan, C.; Yang, H.; Han, D.; Zhang, Q.; Ivaska, A.; Niu, L. Langmuir 2009, 25, 12030–12033.CrossRefGoogle Scholar