Vapor Treatments of Spin-On Mesostructured Silica Films for the Enhancement of Structural Stability

  • Shunsuke Tanaka (a1), Norikazu Nishiyama (a1), Yasuyuki Egashira (a1), Yoshiaki Oku (a2) and Korekazu Ueyama (a1)...

Abstract

Organically functionalized mesoporous silica films were prepared by a novel synthesis procedure. The synthesis procedure involves a vapor infiltration technique for mesostructured silica films prepared through a spin-coating process. Organic-functional groups were incorporated into the mesochannel wall by the vapor infiltration treatment using organosiloxanes. The structural stability of spin-on mesostructured silica films is generally low, resulting in a structural shrinkage or a collapse of the mesostructure under calcination process. On the other hand, the treated films did not contract during calcination, indicating high structural stability. A contact angle of water on the treated film was large, showing high hydrophobicity. FTIR analysis suggested that the residual silanol groups were replaced with the organosilyl groups after vapor infiltration treatment. The increase in the film thickness was hardly observed under vapor infiltration, suggesting no deposition of organosiloxanes vapor on the surface of the film.

Copyright

References

Hide All
[1] Kresge, C.T., Leonowicz, M.E., Roth, W.J., Vartuli, J.C., and Beck, J. S., Nature, 359, 710 (1992).
[2] Beck, J.S., Vartuli, J.C., Roth, W.J.,Leonowicz, M.E., Kresge, C.T., Schmidtt, K.D., Chu, C.T.W., Olson, D.H., Sheppard, E.W., McCullen, S.B., Higgins, J.B., Schlenker, J.L., J. Am. Chem. Soc., 114, 10834 (1992).
[3] Yang, H., Coombs, N., Sokolov, I., and Ozin, G.A., Nature, 381, 589 (1996).
[4] Yang, H., Coombs, N., Dag, O., Sokolov, I., and Ozin, G.A., J. Mater. Chem., 7, 1755 (1997).
[5] Yang, H., Kuperman, A., Coombs, N., Mamich-Afara, S., and Ozin, G.A., Nature, 379, 703 (1996).
[6] Nishiyama, N.,Koide, A.,Egashira, Y., and Ueyama, K., Chem. Commun., 2499 (1998).
[7] Lu, Y., Ganguli, R., Drewien, C.A., Anderson, M.T., Brinker, C.J., Gong, W., Guo, Y., Soyez, H., Dunn, B., Huang, M.H., and Zink, J.I., Nature, 389, 364 (1997).
[8] Sellinger, A., Weiss, P.R., Nguyen, A., Lu, Y., Assink, R.A., Gong, W., and Brinker, C.J., Nature, 394, 256 (1998).
[9] Ogawa, M., J. Am. Chem. Soc., 116, 7941 (1994).
[10] Ogawa, M., Chem. Commun., 1149 (1996).
[11] Ogawa, M., Ishikawa, H., and Kikuchi, T., J. Mater. Chem., 8, 1783 (1998).
[12] Ogawa, M., and Masukawa, N., Micropor. Mesopor. Mater., 38, 35 (2000).
[13] Kundu, D., Zhou, H. S., and Honma, I., J. Mater. Sci. Lett., 17, 2089 (1998).
[14] Hozumi, A., Yokogawa, Y., Kameyama, T., Hiraku, K., Sugimura, H., Takai, O., and Okido, M., Adv. Mater., 12, 985 (2000).
[15] Nishiyama, N., Tanaka, S., Egashira, Y., Oku, Y., and Ueyama, K., Chem. Mater., 14, 4229 (2002).
[16] Nishiyama, N., Tanaka, S., Egashira, Y., Oku, Y., Kamisawa, A., and Ueyama, K., Proceeding of the MRS Symposium on Silicon Materials-Processing, Characterization and Reliability, Materials Research Society, 716, B5.2, 247 (2002).
[17] Oku, Y., Nishiyama, N., Tanaka, S., Ueyama, K., Hata, N., and Kikkawa, T., Proceeding of the MRS Symposium on Silicon Materials-Processing, Characterization and Reliability, Materials Research Society, 716, B12.6, 587 (2002).
[18] Hillhouse, H.W., Egmond, J. W. van, Tsapatsis, M., Hanson, J. C., and Larese, J. Z., Micropor. Mesopor. Mater., 44-45, 639 (2001).

Vapor Treatments of Spin-On Mesostructured Silica Films for the Enhancement of Structural Stability

  • Shunsuke Tanaka (a1), Norikazu Nishiyama (a1), Yasuyuki Egashira (a1), Yoshiaki Oku (a2) and Korekazu Ueyama (a1)...

Metrics

Full text views

Total number of HTML views: 0
Total number of PDF views: 0 *
Loading metrics...

Abstract views

Total abstract views: 0 *
Loading metrics...

* Views captured on Cambridge Core between <date>. This data will be updated every 24 hours.

Usage data cannot currently be displayed