Triboemission And Wear Of Hydrogenated Carbon Films

Published online by Cambridge University Press:  15 February 2011

Keiji Nakayama
Keiji Nakayama*
Affiliation:
Mechanical Engineering Laboratory, Namiki 1–2, Tsukuba, Ibaraki 305, Japan
Get access

Abstract

It is suggested that perfluoropolyether lubricating oil coatings applied to the carbon overcoat film of magnetic recording layers become decomposed by electrons emitted from frictional surfaces. However, no work has at yet been reported as to triboemission of electrons from frictional carbon films.

This paper describes the behavior of triboemission of electrons and the friction coefficient during wear of sputtered hydrogenated carbon films (with various hydrogen contents on the glass substrate). The triboemission of electrons, together with friction coeficient, was measured in a frictional system of Al2O3 sliding on carbon films in a reduced dry air atmosphere. The worn surfaces of the carbon films were then observed using both a SEM and an AFM. The results showed that intense triboemission of electrons were observed during wear of hydrogenated carbon films. The electron emission intensity and friction coefficient transit from low to high with hydrogen content in the film. These results are discussed including physical properties of the carbon films such as internal stress and surface wettability.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 409: Symposium Q – Fracture-Instablility Dynamics, scaling and Ductile/Brittle Behavior , 1995 , 391
Copyright
Copyright © Materials Research Society 1996

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

[1] Mori, S. and Morares, W., Tribology Trans., 33, p. 325–332(1990).Google Scholar
[2] Vurens, G., Zehringer, R., Saperstein, D. and Jose, S., Surface Science Investigation in Tribology edited by Chung, Y., et al (ACS Symposium, 1992), 485, p.169–180.Google Scholar
[3] Ehl, M.J.Z and Faut, O.D., NASA TM, 101962, p.1–15(1989).Google Scholar
[4] Kasai, P.H., Tang, T. and Wheeler, P., Appl. Surf. Sci., 51, p.201–211(1991).Google Scholar
[5] Kasai, P.H., Adv. Info. Storage Syst., 4, p. 291–314(1992).Google Scholar
[6] Packansky, J. and Waltman, R.J., J. Phys. Chem., 95, p.1512–1518(1991).Google Scholar
[7] Strom, B.D., Bogy, D.B., Walmsey, R.G., Brandt, J. and Bhatia, C.S., IEEE Trans., 29, p.253–258(1993).Google Scholar
[8] Nakayama, K., Leiva, J.A. and Enomoto, Y., Tribology Int. in press.Google Scholar
[9] Nakayama, K., Suzuki, N. and Hashimoto, H., J. Appl. Phys., 25, p.303–308(1992).Google Scholar
[10] Nakayama, K. and Hashimoto, H., Tribology Trans., 35, p.643–650(1992).Google Scholar
[11] Nakayama, K. and Hashimoto, H., Tribology Trans., 38, p. 35–42(1995).Google Scholar
[12] Nakayama, K. and Hashimoto, H., Wear 185, p.183–188(1995).Google Scholar
[13] Nakayama, K., Wear, No.178, p.61–67(1994).Google Scholar
[14] Nakayama, K. and Hashimoto, H., Tribology Trans., 38, p.541–548.Google Scholar
[15] Nakayama, K. and Hashimoto, H., Tribology Int. in press.Google Scholar
[16] Nakayama, K., Hashimoto, H. and Fukuda, Y., Proceedings of the Japan Int. Tribology Conference, Nagoya, Oct. 29-Nov. 1, 1990, p. 1141–1146.Google Scholar