Thermally Evaporated AgGaTe2 Thin Films For Low-Cost p-AgGaTe2/n-Si Heterojunction Solar Cells

Published online by Cambridge University Press:  11 February 2011

Krishna C. Mandal
Affiliation:
EIC Laboratories, Inc., 111 Downey Street, Norwood, MA 02062
Anton Smirnov
Affiliation:
EIC Laboratories, Inc., 111 Downey Street, Norwood, MA 02062
Utpal N. Roy
Affiliation:
Department of Physics, Fisk University, Nashville, TN 37208
Arnold Burger
Affiliation:
Department of Physics, Fisk University, Nashville, TN 37208
Get access

Abstract

High quality polycrystalline AgGaTe2 (AGT) thin films were deposited on H-terminated n-Si substrates by controlled thermal evaporation method at various substrate temperatures (300–500 K). X-ray diffraction (XRD) studies showed that all films were of chalcopyrite structure and while the films were deposited at 300 K had random grain orientation, the films deposited at higher substrate temperature (500 K) showed preferred (112) orientation. The composition of the films was thoroughly analyzed by energy dispersive x-ray analysis (EDAX) and by x-ray photoelectron spectroscopy (XPS) with and without argon ion etching. The ultraviolet-visible (UV-Vis) spectra showed the optical bandgap of 1.16 eV, with sharper band edge for the films deposited at higher temperature. The films were p-type and the resistivities of the as deposited at 300 and 500 K were 2.8 × 104 and 1.2 × 103 Ω. cm respectively. p-AgGaTe2/n-Si heterojunction solar cells, having an active area of 0.12 cm2 and without any antireflection coating, were fabricated. It was observed that the films deposited at 500 K produced junctions with improved photovoltaic properties. Under solar simulator AM1 illumination, the improved junctions exhibited an efficiency of 4.8% whereas the films deposited at 300 K showed an efficiency of 2.1%.

Type
Research Article
Copyright
Copyright © Materials Research Society 2003

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

[1] Rashkeev, S.N. and Lambrecht, W.R.L., Phys. Rev., B 63 (2001) 165212–1.Google Scholar
[2] Jackson, A.G., Ohmer, M.C., Leclair, S.R., Infrared Phys. Technol., 38 (1997) 233.Google Scholar
[3] Ohmer, M.C., Goldstein, J.T., Zelmon, D.E., Saxler, A.W., Hegde, S.M., Wolf, J.D., Schunemann, P.G., and Pollak, T.M., J. Appl. Phys., 86 (1999) 94.Google Scholar
[4] Qadri, S., Rek, Z., Webb, A., Skelton, E., Wolf, S.A., J. Appl. Phys., 54 (1983) 6897.Google Scholar
[5] Schunemann, P.G., Setzler, S.D., Pollak, T.M., Ohmer, M.C., Goldstein, J.T., and Zelmon, D.E., J. Crystal Growth, 211 (2000) 242.Google Scholar
[6] Burger, A., Ndap, J.-O., Cui, Y., Roy, U., Morgan, S., Chattopadhyay, K., Faris, K., Thibaud, S., Miles, R., Mateen, H., Goldstein, J.T., and Rawin, C.J., J. Crystal Growth, 225 (2001) 505.Google Scholar
[7] Melloch, M.R., Harmon, E.S., and Emery, K.A., IEEE Electron Device Lett., 12 (1991) 137.Google Scholar
[8] Tompa, G.S., Nelson, C.R., Sarcacino, M.A., Colter, P.C., Anderson, P.L., Wright, W.H., and Schimdt, J.L., Appl. Phys. Lett., 55 (1989) 62.Google Scholar
[9] Savadogo, O. and Mandal, K.C., J. Phys. D: Appl. Phys., 27 (1997) 1070.Google Scholar
[10] Das, S.R., Banerjee, A., and Chopra, K.L., Solid State Electron., 22 (1987) 65.Google Scholar
[11] Mandal, K.C., Ozanam, F., and Chazalviel, J.-N., Appl. Phys. Lett., 57 (1990) 2788.Google Scholar
[12] Mandal, K., Ozanam, F., Chazalviel, J.-N., J. Electroanal. Chem., 336 (1992) 153.Google Scholar
[13] Vincett, P.S., Barlow, W.A., and Roberts, G.G., J. Appl. Phys., 48 (1977) 3800.Google Scholar
[14] Anderson, R.L., IBM J. Res. Dev., 4 (283) 1960.Google Scholar