Superplastic Deformation and Viscous Flow in an Zr-Based Metallic Glass at 410°C

Published online by Cambridge University Press:  10 February 2011

T. G. Nieh
Affiliation:
Lawrence Livermore National Laboratory, Box 808, Livermore CA 94551, niehl@llnl.gov
J. G. Wang
Affiliation:
Lawrence Livermore National Laboratory, Box 808, Livermore CA 94551, niehl@llnl.gov
J. Wadsworth
Affiliation:
Lawrence Livermore National Laboratory, Box 808, Livermore CA 94551, niehl@llnl.gov
T. Mukai
Affiliation:
Osaka Municipal Technical Research Institute, Osaka 536, Japan
C. T. Liu
Affiliation:
Oak Ridge National Laboratory, P.O. Box 2008, Oak Ridge TN 37831
Get access

Abstract

The thermal properties of an amorphous alloy (composition in at.%: Zr-10Al-5Ti-17.9Cu-14.6Ni), and particularly the glass transition and crystallization temperature as a function of heating rate, were characterized using Differential Scanning Calorimetry (DSC). X-ray diffraction analyses and Transmission Electron Microscopy were also conducted on samples heat-treated at different temperatures for comparison with the DSC results. Superplasticity in the alloy was studied at 410°C, a temperature within the supercooled liquid region. Both single strain rate and strain rate cycling tests in tension were carried out to investigate the deformation behavior of the alloy in the supercooled liquid region. The experimental results indicated that the alloy did not behave like a Newtonian fluid.

Type
Research Article
Copyright
Copyright © Materials Research Society 1999

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

1. Klement, W., Willens, R., and Duwez, P., Nature, 187 (1960) 869.Google Scholar
2. Johnson, W.L., in Metal Handbook 10th Edition, Vol.10, p. 804, ASM International, Metals Park, OH, 1988.Google Scholar
3. Hashimoto, K., in Current Topics in Amorphous Materials: Physics and Technology, p. 167, edited by Sakurai, Y. et al, Elsevier Science Publishers B.V., 1993.Google Scholar
4. Kawamura, Y., Nakamura, T., and Inoue, A., Scr. Mater., 39 (1998) 301.Google Scholar
5. Morris, D.G., in Proc. 5th Int'l Conf. on Rapidly Quenched Metals, p. 1775, edited by Steeb, S. and Warlimont, H., Elsevier Science Publishers B.V., 1985.Google Scholar
6. Argon, A.S., Acta Metall., 27 (1979) 47.Google Scholar
7. Mulder, A.L., Derksen, R.J.A., Drijver, J.W., and Radelaar, S., in Proc. 4th International Conf. on Rapidly Quenched Metals, p. 1345, edited by Masumoto, T. and Suzuki, K., Japan Institute of Metals, Sendai, Japan, 1982.Google Scholar
8. Homer, C. and Eberhardt, A., Scr. Metall., 14 (1980) 1331.Google Scholar
9. Zelenskiy, V.A., Tikhonov, A.S., and Kobylkin, A.N., Russian Metallurgy, 4 (1985) 152.Google Scholar
10. Busch, R., Bakke, E., and Johnson, W.L., Acta Mater., 46 (1998) 4725.Google Scholar
11. Khonik, V.A. and Zelenskiy, V.A., Phys. Met. Metall., 67 (1989) 196.Google Scholar
12. Inoue, A., Kim, Y.H., and Masumoto, T., Mater. Trans., JIM, 33 (1992) 487.Google Scholar
13. Inoue, A. and Satome, Y., Metals, 3 (1993) 51.Google Scholar
14. Kawamura, Y., Kato, H., Inoue, A., and Masumoto, T., Appl. Phys. Lett., 67 (1995) 2008.Google Scholar
15. Nieh, T.G., Wang, J.N., Hsiung, L.M., Wadsworth, J., and Sikka, V., Scr. Mater., 37 (1997) 733.Google Scholar
16. Lin, X.H., Johnson, W.L., and Rhim, W.K., Mater. Trans. JIM, 38(5) (1997) 473.Google Scholar
17. Kawamura, Y., Shibata, T., Inoue, A., and Masumoto, T., Appl. Phys. Lett., 69 (1996) 1208.Google Scholar
18. Maddin, R. and Masumoto, T., Mater. Sci. Eng., 9 (1972) 153.Google Scholar
19. Kim, Y.H., Hiraga, K., Inoue, A., Masumoto, T., and Jo, H.H., Mater. Trans. JIM, 35(5) (1994) 293.Google Scholar
20. Kim, Y.H., Inoue, A., and Masumoto, T., Mater. Trans. JIM, 31 (1990) 747.Google Scholar