Reinforcement/Matrix Interaction in Sic Fiber-Reinforced Ni3a1 Matrix Composites

Published online by Cambridge University Press:  26 February 2011

J.-M. Yang ,
W. H. Kao  and
C. T. Liu
J.-M. Yang
Affiliation:
Department of Materials Science and Engineering, University of California Los Angeles, CA 90024
W. H. Kao
Affiliation:
Materials Science Laboratory, The Aerospace Corporation, El Segundo, CA 90245
C. T. Liu
Affiliation:
Metals and Ceramics Division, Oak Ridge National Laboratory, Oak Ridge, TN 37831
Get access

Abstract

The interfacial reaction characteristics of two different types of SiC fibers with Ni3A1 (Ni-Al-Cr-Zr-B) matrix have been investigated. The microstructure and chemical compositions across the reaction zone have been analyzed quantitatively using microscopy and electron probe microanalysis. In both types of SiC/Ni3Al composites, it was found that Ni was the dominant diffusing species responsible for the overall reaction. The C-rich layer outside the SCS-6 fiber provided an incubation period, but could not stop the inward diffusion of Ni. It could, however, effectively stop the diffusion of Al, Zr and Cr. No significant increase in reaction zone thickness after exposure at temperatures below 900 °C for up to 100 hours was observed. When the C-rich layer was depleted, a rapid increase in reaction zone thickness and the formation of multilayer reaction products occurred. In the case of Sigma/Ni3A1 composite, extensive reaction between the fiber and the matrix occurred at all the temperatures studied. Diffusion barrier coating for both types of fibers is required to develop nickel aluminide matrix composites.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 133: Symposium H – High-Temperature Ordered Intermetallic Alloys III , 1988 , 453
Copyright
Copyright © Materials Research Society 1989

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1. Liu, C. T., MiCon 86: Optimization of Processing. Properties. and Service Performance Through Microstructure Control, ASTM STP 979, (ASTM, Philadelphia,1988), p. 222.Google Scholar
2. High Temperature Ordered Intermetallic Alloy I, Ed. by Koch, C.C., Liu, C.T., and Stoloff, N.S. (MRS, Pittsburgh, 1984).Google Scholar
3. High Temperature Ordered Intermetallic Alloy II, Ed. by Stoloff, N.S., Koch, C.C., Liu, C.T., and Izumi, O. (MRS, Pittsburgh, 1987).Google Scholar
4. Baker, I. and Munroe, P.R., J. of Metals, 40, 28 (1988).Google Scholar
5. Aoki, K., and Izumi, O., J. Japan Inst. Met, 43, 38 (1979).Google Scholar
6. Liu, C.T., White, C.L. and Horton, J. A., Acta. Met. 23, 213 (1985).CrossRefGoogle Scholar
7. Huang, S.C., Taub, A. I., and Chang, K. M., Acta Met., 32, 1703 (1984).CrossRefGoogle Scholar
8. Taub, A. I., Huang, S. C., and Chang, K. M., Met. Trans., 15A, 399 (1984).CrossRefGoogle Scholar
9. Yang, J,-M., Kao, W. H., and Liu, C. T., Development of Nickel Aluminide Matrix Composites, to be published in Materials Science and Engineering, 1988 Google Scholar
10. Nieh, T. G., Stephens, J.J., Wadsworth, J. and Liu, C.T., Proceeding of the International Conference on Composite Interface, 1988, in press.Google Scholar
11. Povirk, G. L., Horton, J. A., McKamey, C. G., Tiegs, T. N. and Nutt, S. R., Acta Met., in press.Google Scholar
12. Bose, A., Moore, B., German, R. M., and Stoloff, N. S., J. Metals, 40, 14 (1988).Google Scholar
13. Bose, A., Moore, B., Stoloff, N. S., and German, R. M., in Proc. Conference on P/M Aerospace Materials, Luzern, Switzerland, Nov. 1987, in pressGoogle Scholar
14. Fuchs, G. E., and Kao, W. H., Proc. 1988 P/M Conference, Orlando, FL, Oct., 1988, in pressGoogle Scholar
15. Nourbakhsh, S., Liang, S. L., and Margolin, H., to be published in Advanced Materials and Manufacturing Processes, in press.Google Scholar
16. Yang, J.-M., Kao, W. H., and Liu, C. T., submitted to Met. Trans., 1988 Google Scholar
17. Comie, J. A., NASA-CR-135301, 1977.Google Scholar