Oxidation Kinetics Of Mosi2 And Mosi2/Reinforcement Mixtures

Published online by Cambridge University Press:  26 February 2011

P. J. Meschter
P. J. Meschter*
Affiliation:
McDonnell Douglas Research Labs, P. O. Box 516, St. Louis, MO 63166
Get access

Abstract

An oxidation study of pure, dense MoSi 2 at 400-600°C and MoSi2/20 vol. % (TiB2, Al2O3, Nb) mixtures at 400–1200°C has been performed. Dense MoSi2 does not fail catastrophically (“pest”) in dry air, wet air, or oxygen, and oxidizes heavily only near 500°C. Heavy oxidation is related to the slow growth of a protective, amorphous SiO2 layer; a low rate of Mo removal as vapor species; and cracking of an initially protective Mo9O26-SiO2 layer. Pre-oxidation of MoSi2 at 1200°C prevents subsequent heavy oxidation at 500°C. MoSi2/TiB2 and MoSi2/A12O3 mixtures oxidize more slowly than MoSi2 for T < 600°C and more rapidly for T > 600°C. Protective oxides are formed on MoSi2/reinforcement mixtures except at 500°C, for which high-temperature pre-oxidation is again effective. MoSi2/Nb mixtures suffer severe mass losses upon oxidation at both 500 and 1200°C owing to rapid oxidation of the Nb and spalling of the product Nb2O5 Only the latter case poses problems for the application of MoSi2-matrix composites as high-temperature materials.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 213: Symposium Q – High-Temperature Ordered Intermetallic Alloys IV , 1990 , 1027
Copyright
Copyright © Materials Research Society 1991

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1. Fitzer, E., Herbst, H., and Schlichting, J., Werkst. Korros. 24, 274 (1973).Google Scholar
2. Schlichting, J., High Temp.-High Press. 10, 241 (1978).Google Scholar
3. Fitzer, E., in Warmfeste und Korrosionsbestandige Sinterwerkstoffe, 2. Plansee Seminar, Benesovsky, F., ed. (Springer, Vienna, 1966), p. 56.Google Scholar
4. Fitzer, E. and Reinmuth, K., in Hochtemperaturwerkstoffe. 6. Plansee Seminor, (Springer, Vienna, 1969), p. 767.Google Scholar
5. Berkowitz, J., Ingraham, M. G., and Chupka, W. A., J. Chem. Phys. 26, 842 (1957).Google Scholar
6. Belton, G. R. and Jordan, A. S., J. Phys. Chem. 69, 2065 (1965).CrossRefGoogle Scholar
7. Berkowitz-Mattuck, J. B., Blackburn, P. E., and Felten, E. J., Trans. TMS-AIME 233, 1093 (1965).Google Scholar
8. Fitzer, E., in 3. Plansee Seminar 1958 (Springer, Vienna, 1959), p. 175.Google Scholar
9. Vedula, K. and Lisy, F., in Metallic and Ceramic Matrix Composites: Processing, Modeling, and Mechanical Behavior, Bhagat, R. B., ed. (TMS, Warrendale, PA, 1990), p. 569.Google Scholar