On the Role of Grain-Boundary Films in Optimizing the Mechanical Properties of Silicon Carbide Ceramics

Published online by Cambridge University Press:  21 March 2011

R. O. Ritchie ,
X.-F. Zhang  and
L. C. De Jonghe
R. O. Ritchie
Affiliation:
Materials Sciences Division, Lawrence Berkeley National Laboratory, and Department of Materials Science and Engineering, University of California, Berkeley, CA 94720 Department of Materials Science and Engineering, University of California, Berkeley, CA 94720
X.-F. Zhang
Affiliation:
Materials Sciences Division, Lawrence Berkeley National Laboratory, and Department of Materials Science and Engineering, University of California, Berkeley, CA 94720
L. C. De Jonghe
Affiliation:
Materials Sciences Division, Lawrence Berkeley National Laboratory, and Department of Materials Science and Engineering, University of California, Berkeley, CA 94720 Department of Materials Science and Engineering, University of California, Berkeley, CA 94720
Get access

Abstract

Through control of the grain-boundary structure, principally in the nature of the nanoscale intergranular films, a silicon carbide with a fracture toughness as high as 9.1 MPa.m1/2 has been developed by hot pressing β-SiC powder with aluminum, boron, and carbon additions (ABC-SiC). Central in this material development has been systematic transmission electron microscopy (TEM) and mechanical characterizations. In particular, atomic-resolution electron microscopy and nanoprobe composition quantification were combined in analyzing grain boundary structure and nanoscale structural features. Elongated SiC grains with 1 nm-wide amorphous intergranular films were believed to be responsible for the in situ toughening of this material, specifically by mechanisms of crack deflection and grain bridging. Two methods were found to be effective in modifying microstructure and optimizing mechanical performance. First, prescribed post-annealing treatments at temperatures between 1100 and 1500°C were seen to cause full crystallization of the amorphous intergranular films and to introduce uniformly dispersed nanoprecipitates within SiC matrix grains; in addition, lattice diffusion of aluminum at elevated temperatures was seen to alter grain-boundary composition. Second, adjusting the nominal content of sintering additives was also observed to change the grain morphology, the grain-boundary structure, and the phase composition of the ABC-SiC. In this regard, the roles of individual additives in developing boundary microstructures were identified; this was demonstrated to be critical in optimizing the mechanical properties, including fracture toughness and fatigue resistance at ambient and elevated temperatures, flexural strength, wear resistance, and creep resistance.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 818: Symposium M – Nanoparticles and Nanowire Building Blocks-Synthesis, Processing, Characterization and Theory , 2004 , N1.1.1
Copyright
Copyright © Materials Research Society 2004

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

1. Becher, P.F., J. Am. Ceram. Soc., 74, 255 (1991).Google Scholar
2. Cao, J.J., MoberlyChan, W.J., Jonghe, L.C. De, Gilbert, C.J., Ritchie, R.O., J. Am. Ceram. Soc. 79, 461 (1996).Google Scholar
3. Zhang, X.-F., Sixta, M.E., Jonghe, L.C. De, J. Am. Ceram. Soc. 83, 2813 (2000).Google Scholar
4. Zhang, X.-F., Yang, Q., Jonghe, L.C. De, Zhang, Z., J. Microsc. 207, 58 (2002).Google Scholar
5. Gilbert, C.J., Cao, J.J., Jonghe, L.C. De, Ritchie, R.O., J. Am. Ceram. Soc. 80, 2253 (1997).Google Scholar
6. Kleebe, H.-J., Cinibulk, M., Cannon, R.M., Rähle, M., J. Am. Ceram. Soc. 76, 1969 (1993).Google Scholar
7. Chiang, Y-M., Silverman, L.A., French, R.H., Cannon, R.M., J. Am. Ceram. Soc., 77, 1143 (1994).Google Scholar
8. Clarke, D.R., J. Am. Ceram. Soc. 70, 15 (1987).Google Scholar
9. Hamminger, R., Grathwohl, G., Thummler, F., J. Mater. Sci. 18, 3154 (1983).Google Scholar
10. Lane, J.E., Carter, C.H., Davis, R.F., J. Am. Ceram. Soc., 71, 281 (1988).Google Scholar
11. Zhang, X.-F., Sixta, M.E., Jonghe, L.C. De, J. Am. Ceram. Soc. 84, 813 (2001).Google Scholar
12. Cutler, I.B., Miller, P.D., Rafaniello, W., Park, H.K., Thompson, D.P., Jack, K.H., Nature 275, 434 (1978).Google Scholar
13. Zhang, X.-F., Sixta, M.E., Jonghe, L.C. De, J. Mater. Sci. 36, 5447 (2001).Google Scholar
14. Chen, D., Gilbert, C.J., Zhang, X.-F., Ritchie, R.O., Acta Mater, 48, 659 (2000).Google Scholar
15. Hansson, T., Miyashita, Y., Mutoh, Y., in Fracture Mechanics of Ceramics, edited by Bradt, R.C. (New York, NY: Plenum Press) 12, 187–201 (1996).Google Scholar
16. Ewart, L., Suresh, S., S., J. Mater. Sci. 27, 5181 (1992).Google Scholar
17. Ramamurty, U., Kim, A.S., Suresh, S., J. Am. Ceram. Soc. 76, 1953 (1993).Google Scholar
18. Sixta, M.E., Zhang, X.-F., Jonghe, L.C. De, J. Am. Ceram. Soc. 84, 2022 (2001).Google Scholar
19. Zhang, X.-F., Lee, G.Y., Chen, D., Ritchie, R.O., Jonghe, L.C. De, J. Am. Ceram. Soc., 86, 1370 (2003).Google Scholar
20. Zhang, X.-F., Yang, Q., Jonghe, L.C. De, Acta Mater., 51, 3849 (2003).Google Scholar
21. Yuan, R., Kruzic, J.J., Zhang, X.-F., Jonghe, L.C. De, Ritchie, R.O., Acta Mater., 51, 6477 (2003).Google Scholar
22. Sakai, T., Aikawa, T., J. Am. Ceram. Soc. 71, C–7 (1988).Google Scholar
23. Huang, J-L., Hurford, A.C., Cutler, R.A., Virkar, A.V., J. Mater. Sci. Lett. 21, 1448 (1986).Google Scholar