New Perovskite Oxide (Tl1/2Na1/2)TiO3

  • Yue Jin Shan (a1), Tetsuro Nakamura (a1), Mayuko Miyata (a1), Kazuhisa Kobashi (a2), Yoshiyuki Inaguma (a2) and Mitsuru Itoh (a2)...

Abstract

New perovskite-type oxide (Tl1/2Na1/2)TiO3 was synthesized by a cubic-anvil-type high pressure apparatus at 5.5 GPa and 1273 K for 30 sec. The perovskite-phase was found to have a tetragonal symmetry with space group P4/mmm. The lattice parameters a and c are 0.3811 nm and 0.3826 nm, respectively. An insulating skin covered the sample, but real resistivity is smaller and shows a metallic behavior.

Copyright

References

Hide All
[1] Inaguma, Y., Shon, J.H., Kim, I.S., Itoh, M. and Nakamura, T., J. Phys. Soc. Jpn., 61, p. 3831 (1992).
[2] Sun, P.H., Nakamura, T., Shan, Y.J., Inaguma, Y. and Itoh, M., Ferroelectrics, 200, p. 93 (1997).
[3] Shan, Y.J., Nakamurra, T., Inaguma, Y. and Itoh, M., Solid State lonics., 108, p. 123 (1998).
[4] Kim, Y.-I. and lzumi, F., J. Ceram. Soc. Jpn., 102, p. 401 (1994).
[5] Hoppe, R. and Werding, G., Z.anorg.allg. Chem., 307, p. 174 (1961).
[6] Hoppe, R. and Rohrborn, H.J., Z.anorg.allg. Chem., 327, p. 199 (1964).

Related content

Powered by UNSILO

New Perovskite Oxide (Tl1/2Na1/2)TiO3

  • Yue Jin Shan (a1), Tetsuro Nakamura (a1), Mayuko Miyata (a1), Kazuhisa Kobashi (a2), Yoshiyuki Inaguma (a2) and Mitsuru Itoh (a2)...

Metrics

Full text views

Total number of HTML views: 0
Total number of PDF views: 0 *
Loading metrics...

Abstract views

Total abstract views: 0 *
Loading metrics...

* Views captured on Cambridge Core between <date>. This data will be updated every 24 hours.

Usage data cannot currently be displayed.