Mechanical Behavior of Energetic Materials During High Acceleration in An Ultracentrifuge

Published online by Cambridge University Press:  15 February 2011

M. Yvonne D. Lanzerotti  and
J. Sharma
M. Yvonne D. Lanzerotti
Affiliation:
U. S. Army Armament Research, Development and Engineering Center, Picatinny Arsenal, NJ 07806-5000
J. Sharma
Affiliation:
Naval SurfaceWarfare Center, White Oak, Silver Spring, MD 20903
Get access

Abstract

The mechanical behavior of explosives subjected to high acceleration (high g) has been studied in an ultracentrifuge. The experiments reported here reveal new information on the mechanical behavior of such materials and the influence of grain size on the fracture process. Through measurement and analysis of fracture surfaces, we have found that predominately intergranular failure occurs when the shear or tensile strength of the explosive is exceeded. We have found that the mechanical strength of melt-cast polycrystalline TNT varies inversely with crystal size. That is, if the sample consists of large, homogeneous crystals, these are found to separate from the sample at lower g-levels due to the larger mass-to-binding surface area ratio of the crystals. Conversely, smaller original crystallites are found to separate at higher g-levets due to the smaller mass-to-binding surface area ratio. Our results show that single crystals of TNT fracture under a higher g-level at crystal defects. We have also found that the fracture acceleration of Octol decreases with increasing percent TNT and decreasing percent HMX. Hexanitrostilbene (HNS) has been shown by other investigators to be an effective additive to prevent growth of large TNT grains. We have found that the fracture acceleration increases when HNS is added to Octol.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 362: Symposium J – Grain-Size and Mechanical Properties--Fundamentals and Applications , 1994 , 131
Copyright
Copyright © Materials Research Society 1995

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

1. Lanzerotti, Y. D. and Sharma, J., App. Phys. Lett.39(1981)455.Google Scholar
2. Lanzerotti, Y. D., “Fracture Phenomena of Energetic Materials During High Acceleration”, in Proceedings of the Symposium on Thermomechanical Properties of Energetic Materials and Their Effects on Munitions Survivability, Volume II, p. 1, 1985.Google Scholar
3.. Lanzerotti, Y. D. and Pinto, J. J., “Chemical Reaction of Energetic Materials During High Acceleration”, in: Shock Waves in Condensed Matter, ed. Gupta, Y. M. (1986, Plenum Press, New York, NJ) p. 908.Google Scholar
4. Lanzerotti, Y. D., Pinto, J., Wolfe, A., Thomson, D. J., “Fracture Surface Topography of TNT, Composition B and Octol”, in Tenth Symposium (International) on Detonation, in press.Google Scholar
5. Borman, S., “Advanced Energetic Materials Emerge for Military and Space Applications” in Chemical and Engineering News, V.72, Number 3, p. 18 (17 Janaury 1994).Google Scholar
6. Costain, T. S. and Motto, R. V., Picatinny Arsenal Technical Report 4587, Picatinny Arsenal (now U. S.Army Armament Research, Development and Engineering Command), Picatinny Arsenal, NJ, 1973.Google Scholar
7.. Properties of Explosives of Military Interest, U. S. Army Materiel Command Handbook, AMCP 706–177, 1971.Google Scholar
8.. HMX, MIL- 11–4544B (PA), 27 February 1974.Google Scholar
8.. PICMaterial Specification for Sedimentation Cast Octol, 1986.Google Scholar
10.. SOP No. 1510–1900-F, Holston Defense Corporation, 1989.Google Scholar
11. Philp, D. K. and Thorpe, B. W., J. Crystal Growth 35(1976)133.Google Scholar
12. Parry, M. A. and B. W. Thorpe 35(1979)541.Google Scholar
13. Trevino, S. F., Portnoy, S., Choi, C. S., U. S.Army Armament Research and Development Command Memorandum Report ARLCD-MR-79001, September 1979.Google Scholar
14. Parry, M. A. and Thorpe, B. W., Influence of HNS on the Microstructure and Properties of Cast TNT, MRL-R-812, 1981.Google Scholar
15.. Soderberg, J. L., Back, J. S., Hakansson, C. L., Method of Producing Fine-Crystalline Cast Charges with Unoriented Crystalline Structure of 2,4,6-Trinitrotoluene or Explosive Compositions Containing 2,4,6-Trinitrotoluene, U. S. Patent 3,620,857, 1971.Google Scholar