Li-insertion Behavior in NanocrystallineTiO2-(MoO3)z Core-Shell Materials

Published online by Cambridge University Press:  18 March 2011

Gregory J. Moore
Affiliation:
Argonne National Laboratory Argonne, IL 60439, U.S.A.
Dominique Guyomard
Affiliation:
Institut des Matériaux Jean Rouxel, CNRS – University of NantesBP 32229 – 44322 Nantes Cedex 3 –, France
Scott H. Elder
Affiliation:
Pacific Northwest National Laboratory Richland, WA 99352, U.S.A.
Get access

Abstract

A fundamental study of the Li insertion behavior of a series of materials consisting of a TiO2 core having MoO3 on the surface has been carried out in order to determine the influence of the shell. These TiO2-(MoO3)z materials, where (z) denotes the fraction of coverage from a partial to a double layer, range in diameter from 40-100 Å. Calculations have been done on their theoretical lithium capacity using a maximum of Li0.5TiO2 for the core, and Li1.5MoO3 at the TiO2/MoO3 interface, and they have been compared to that found experimentally. The reversible Li-insertion capacity was shown to increase from 0.34 per Ti for the pure TiO2 sample, to 0.91 Li per transition metal when the MoO3 coverage increased to one monolayer. There was only one plateau observed in the electrochemical scans for the samples showing that they function as a single-phase material making them interesting for electrodes. The redox voltage of the TiO2/Li0.5TiO2 biphasic transformation increased 60 mV from the pure TiO2 to the sample containing one monolayer of MoO3. This effect was interpreted as due to a change in TiO2 surface charge coming from an inductive effect of Ti-O-Mo bonds.

Type
Research Article
Copyright
Copyright © Materials Research Society 2001

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1. Huang, S. Y.et al., J. Electrochem. Soc., 142, L142 (1995).Google Scholar
2. Cav, R.J., Murphy, D.W., Zahurak, S., Santoro, A. and Roth, R.S., J. Solid State Chem., 53, 64 (1984).Google Scholar
3. Zachau-Christiansen, B., West, K., Jacobsen, T., Skaarup, S., Solid State Ionics, 53–56, 364 (1992).Google Scholar
4. Ohzuku, T., Takehara, Z. and Yashizawa, S., Electrochimica Acta, 24, 219 (1979).Google Scholar
5. Bonino, F., Busani, L., Lazzari, M., Manstretta, M., Rivolta, B. and Scrosati, B., J. Power Sources, 6, 261 (1981).Google Scholar
6. Ohzuku, T., Kodama, T. and Hirai, T., J. Power Sources, 14, 153 (1985).Google Scholar
7. Macklin, W.J. and Neat, R.J., Solid State Ionics, 53–56, 694 (1992).Google Scholar
8. Kavan, L., Attia, A., Lenzmann, F., Elder, S.H. and Gratzel, M., J.Electrochem. Soc., 147, 2897 (2000).Google Scholar
9. Elder, S.H., Cot, F.M., Su, Y., Heald, S.M., Tyryshkin, A.M., Bowman, M.K., Gao, Y., Joly, A.G., Balmer, M.L., Kolwaite, A.C., Magrini, K.A. and Blake, D.M., J.Am.Chem. Soc., 122, 5138 (2000).Google Scholar
10. Julien, C., Nazri, G.A., Guesdon, J.P., Gorenstein, A., Khefla, A. and Hussain, O.M., Solid State Ionics, 73, 319 (1994).Google Scholar
11. Boschen, I. and Krebs, B., Acta. Cryst., B30, 1795 (1974).Google Scholar
12. Oswald, H.R., Gunter, J.R. and Dubler, E., J. Solid State Chem., 5, 354 (1975).Google Scholar
13. Padhi, A.K., Nanjundaswamy, K.S., Masquelier, C., Okada, S., and Goodenough, J.B., J.Electrochem Soc., 144, 1609 (1997).Google Scholar