Laser Cladding with a Ni-Fe-Cr-Al Alloy

Published online by Cambridge University Press:  25 February 2011

K. Mohammed Jasim  and
D.R.F. West
K. Mohammed Jasim
Affiliation:
On leave from Scientific, Research Council, Baghdad, Iraq
D.R.F. West
Affiliation:
Department of Materials, Imperial College, London
Get access

Abstract

An investigation is reported of the laser surface.cladding of an alloy of nominal composition Ni-4Fe-30Cr-6A1 (wt%) on a mild steel substrate, using a continuous powder feed of the elemental powder mixture into the melt pool. The effect of laser processing conditions has been investigated in relation to clad dimensions, bonding, dilution level, hardness and microstructural features. A 2 kW CW C02laser was used working at 1.6 kW power and 2.5 mm beam diameter at different traverse speeds ranging from 1.8 to 25 mm/s: clad layers were produced in the range of 0.15-3 mm thick. Fine microstructures were obtained (corresponding to the rapid solidification rates). Good metallurgical bonding was observed between the clad layer and substrate within the range of specific energies, 50-130 J/mm2. For all the conditions studied, no cracking was observed in single tracks; low specific energy conditions gave little porosity.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 129: Symposium B – Laser and Particle-Beam Modification of Chemical Processes on Surfaces , 1988 , 139
Copyright
Copyright © Materials Research Society 1989

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1. Ayers, J.D., Thin Solid Films 84, 323 (1981)Google Scholar
2. Jasim, K. Mohammed, West, D.R.F., Steen, W.M. and Rawlings, R.D., presented at the 1988 TMS Full-Meeting, Chicago, Illinios, Sept. 25-29 (unpublished).Google Scholar
3. Jasim, K. Mohammed and D.R.F. West, to be published in J. Mat. Sci. Letts.Google Scholar
4. Grot, A.S. and Martyn, J.K., Ceram. Bull. 60, 807 (1981)Google Scholar
5. Vogan, T.W., Hsu, L. and Stetson, A.R., Thin Solid Films 84, 75 (1981)CrossRefGoogle Scholar
6. Smeggil, J.G., Funkenbusch, A.W. and Bornsteln, N.S., Thin Solid Films 119, 327 (1984)Google Scholar
7. Liu, C.A., Humphries, J.H. and Kratenat, R.C., Thin Solid Films 107, 269 (1983)Google Scholar
8. Bruck, G.J., J. of Metals 39, 10 (1987)Google Scholar
9. Steen, W.M., presented at ECLAT' 88, Bad Nauheim, W. Germany, 1988 (published).Google Scholar
10. Raynor, G.V. and Rivlin, V.G., Phase equilibria in iron ternary alloys, Institute of Metals, London, 1988.Google Scholar