Ionic Conduction Mechanisms in CaF2 and CaF2-Al2O3 Nanocomposite Films on Al2O3 Substrates

Published online by Cambridge University Press:  21 February 2011

F. A. Modine ,
D. Lubben  and
J. B. Bates
F. A. Modine
Affiliation:
Solid State Division, Oak Ridge National Laboratory, Oak Ridge, Tennessee 37831-6030
D. Lubben
Affiliation:
Solid State Division, Oak Ridge National Laboratory, Oak Ridge, Tennessee 37831-6030
J. B. Bates
Affiliation:
Solid State Division, Oak Ridge National Laboratory, Oak Ridge, Tennessee 37831-6030
Get access

Abstract

Thin films of pure CaF2 and nanocomposite mixtures of Al2O3 with CaF2 were sublimated on Al2O3 substrates. Interdigital electrodes allowed in situ measurements of the electrical conduction of films as a function of thickness, deposition rate, composition, time, and temperature. The electrical conductivity in pure CaF2 adjacent to an Al2O3 interface sometimes exceeded the bulk CaF2 conductivity (i.e., value at more than 50 nm distance) by as much as a factor of 6700 at 200°C. The high conductivity is characterized by an activation energy of 0.6 ± 0.1 eV, which is significantly lower than the activation energy of about 1.0 eV for conduction in the bulk. However, this high conductivity is thermally unstable and diminishes in time. A high but stable conductivity was obtained in CaF2 films containing about 10 mole percent Al2O3 as a dispersed second phase. At 200°C, a 2-phase film gave a factor of 360 enhancement over the measured bulk CaF2 conductivity and a factor of 7 improvement over the best previously reported conductivity for CaF2-Al203 composite materials. The origin of enhanced conduction in CaF2 is attributed to ion transport along dislocations. Dislocations anneal with a characteristic log of time dependence that is recognizable in the annealing behavior of the electrical conductivity. Presumably, the addition of a dispersed second phase of Al2O3 to CaF2 serves both to generate and to pin dislocations; the electrical conductance is thereby enhanced and stabilized.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 318: Symposium Ca – Interface Control of Electrical, Chemical, and Mechanical Properties , 1993 , 439
Copyright
Copyright © Materials Research Society 1994

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1 Dudney, N. J., Annu. Rev. Mater. Sci. 19, 103 (1989).Google Scholar
2 Chang, M. R-W., Shaki, K., and Wagner, J. B. Jr., J. Electrochem. Soc. 131, 1213 (1984).Google Scholar
3 Nakamura, O. and Goodenough, J. B., Solid State Ionics 7, 119 (1982).CrossRefGoogle Scholar
4 Slade, R. C. T. and Thompson, J. M., Solid State Ionics 26, 287 (1988).Google Scholar
5 Phipps, J. B., Johnson, D. L., and Whitmore, D. H., Solid State Ionics 5, 393 (1981).Google Scholar
6 Phipps, J. B. and Whitmore, D. H., Solid State Ionics 9/10, 123 (1983).Google Scholar
7 Maier, J., J. Electrochem. Soc. 134, 1524 (1987); J. Phys. Chem. Solids 46, 309 (1985).CrossRefGoogle Scholar
8 J. Maier Phys. Status Solidi (a) 112, 115 (1989).Google Scholar
9 Dudney, N. J., J. Am. Ceram. Soc. 70, 65 (1987).CrossRefGoogle Scholar
10 Mühlherr, S., Läuger, K., Schreck, E., Dansfeld, K., and Nicoloso, N., Solid State Ionics 28–30, 1495 (1988).CrossRefGoogle Scholar
11 Schreck, E., Läuger, K., and Dansfeld, K., Z. Phys. B 62, 331 (1986).Google Scholar
12 Wen, T. L., Huggins, R. A., Rabenau, A., and Weppner, W., Rev. Chim. Min. 20, 643 (1983).Google Scholar
13 Vaidehi, N., R, Akila, Shukla, A. K., and Jacob, K. T., Mat. Res. Bull. 21, 909 (1986).Google Scholar
14 Khandkar, A., Tare, V. B., and Wagner, J. B. Jr., Rev. Chim. Min. 23, 274 (1986).Google Scholar
15 Ure, R. W. Jr., J. Chem. Phys. 26, 1363 (1957).CrossRefGoogle Scholar
16 Bollman, W., Görlich, P., Hauk, W., and Mothes, H., Phys. Status Solidi A 2, 157 (1970); W. Bollman and H. Henniger, ibid., A 11, 367 (1972).Google Scholar
17 Mogilevskii, B. M., Romanov, V. N., Reiterov, V. M., Trofimova, L. M., and Chudnovskii, A. F., Sov. Phys. Solid State 15, 728 (1973).Google Scholar
18 Jacobs, P. W. M. and Ong, S. H., J. Phys. 12, C7 331 (1976).Google Scholar
19 Kliewer, K. L. and Kohler, J. S., Phys. Rev. 140, 1226 (1963); 140, 1241 (1963); K. L. Kliewer, J. Phys. Chem. Solids. 27, 705 (1966).Google Scholar
20 Dudney, N. J., J. Am. Ceram. Soc. 68, 538 (1985).Google Scholar
21 Johnston, W. G., Phys. Rev. 98, 1777 (1955).Google Scholar
22 Mott, N. F., Phil. Mag. 43, 1151 (1952); 44, 742 (1953).Google Scholar
23 Kingery, W. D., Bowen, H. K., and Ulman, D. R., Introduction to Ceramics, 2nd Edition, (John Wiley & Sons, New York, 1976), p. 729.Google Scholar