Incorporation of Excess Arsenic in GaAs and AlGaAs Epilayers Grown at Low Substrate Temperatures by Molecular Beam Epitaxy

Published online by Cambridge University Press:  15 February 2011

M. R. Melloch ,
N. Otsuka ,
K. Mahalingam ,
A. C. Warrew ,
J. M. Woodall  and
P. D. Kirchner
M. R. Melloch
Affiliation:
School of Electrical Engineering, Purdue University, West Lafayette, IN 47907
N. Otsuka
Affiliation:
School of Materials Engineering, Purdue University, West Lafayette, IN 47907
K. Mahalingam
Affiliation:
School of Materials Engineering, Purdue University, West Lafayette, IN 47907
A. C. Warrew
Affiliation:
IBM Research Division, P.O. Box 218, Yorktown Heights, NY 10598
J. M. Woodall
Affiliation:
IBM Research Division, P.O. Box 218, Yorktown Heights, NY 10598
P. D. Kirchner
Affiliation:
IBM Research Division, P.O. Box 218, Yorktown Heights, NY 10598
Get access

Abstract

Excess arsenic can be incorporated in GaAs and AIGaAs epilayers by growing at low substrate temperatures (LT-GaAs and LT-AIGaAs) by molecular beam epitaxy (MBE). Upon annealing these epilayers, the excess As precipitates forming GaAs:As and AIGaAs:As. Using transmission electron microscopy (TEM), we have measured the densities and sizes of the As precipitates and thereby determined the amount of excess As incorporated in these epilayers. The volume fraction of excess As as a function of inverse substrate growth temperature follows an Arrhenius-type behavior with an activation energy of 0.87 eV. The sizes of the As precipitates increase and the densities decrease with increase anneal temperatures; for Si-doped GaAs:As this results in n-type material when the densities become small enough that the depletion regions around the As precipitates no longer overlap. Also investigated is the formation of As precipitates at GaAs/AIGaAs heterojunctions and superlattices, and our attempts to tailor the As precipitate distribution.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 241 , 1991 , 113
Copyright
Copyright © Materials Research Society 1992

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

[1]Cho, A.Y., in The Technology and Physics of Molecular Beam Epitaxy, edited by Parker, E.H.C. (Plenum, New York, 1985) pp. 2–3.Google Scholar
[2]Kaminska, M., Liliental-Weber, Z., Weber, E.R., George, T., Kortright, J.B., Smith, F.W., Tsaur, B-Y., and Calawa, A.R., Appl. Phys. Lett. 54, 1881(1989).Google Scholar
[3]Matyi, R.J., Melloch, M.R., and Woodall, J.M., submitted to Appl. Phys. Lett.Google Scholar
[4]Wie, C.R., Xie, K., Look, D.C., Evans, K.R., and Stutz, C.E., Proc. 6th Conf. on Semiinsulating Materials, 71(1990).Google Scholar
[5]Wie, C.R., Xie, K., Bardin, T.T., Pronko, J.G., Look, D.C., Evans, K.R., and Stutz, C.E., Material Res. Symp. Proc. 198, 383 (1990).Google Scholar
[6]Kaminska, M., Weber, E.R., Liliental-Weber, Z., Leon, R., and Rek, Z.U., J. Vac. Sci. Technol. B7 (4), 710(1989).Google Scholar
[7]Melloch, M.R., Workshop on Low Temperature GaAs Buffer Layers, San Francisco, CA, April 20, 1990.Google Scholar
[8]Ballingall, J.M., Workshop on Low Temperature GaAs Buffer Layers, San Francisco, CA, April 20, 1990.Google Scholar
[9]Liliental-Weber, Z., Workshop on Low Temperature GaAs Buffer Layers, San Francisco, CA, April 20, 1990.Google Scholar
[10]Melloch, M.R., Otsuka, N., Woodall, J.M., Warren, A.C., and Freeouf, J.L., Appl. Phys. Lett. 57, 1531(1990).Google Scholar
[11]Mahalingam, K., Otsuka, N., Melloch, M.R., Woodall, J.M., and Warren, A.C., Journal of Vac. Sci. and Technol. B9, 2328(1991).Google Scholar
[12]Melloch, M.R., Mahalingam, K., Otsuka, N., Woodall, J.M., and Warren, A.C., Journal of Crystal Growth 111, 39(1991).Google Scholar
[13]Puechner, R.A., Johnson, D.A., Shiralagi, K.T., Gerber, D.S., Droopad, R., and Maracus, G.N., Journal of Crystal Growth 111, 43(1991).Google Scholar
[14]Warren, A.C., Woodall, J.M., Freeouf, J.L., Grischkowsky, D., Mclnturff, D.T., Melloch, M.R., and Otsuka, N., Appl. Phys. Lett. 57, 1331 (1990).Google Scholar
[15]Warren, A.C., Burroughes, J.H., Woodall, J.M., Mclnturff, D.T., Hodgson, R.T., and Melloch, M.R., IEEE Elec. Dev. Lett. 12, 527(1991).Google Scholar
[16]Mclnturff, D.T., Woodall, J.M., Warren, A.C., Braslau, N., Pettit, G.D., and Melloch, M.R., ”Photoemission Spectroscopy of GaAs:As PiN Photodiodes,” to appear in Appl. Phys. Lett. 60, (1992).Google Scholar
[17]Schaff, W.J., Workshop on Low Temperature GaAs Buffer Layers, San Francisco, CA, April 20, 1990.Google Scholar
[18]Mahalingam, K., Otsuka, N., Melloch, M.R., Woodall, J.M., and Warren, A.C., Eleventh Annual Molecular Beam Epitaxy Workshop, Sept. 16–18, 1991, Austin, TX, and to appear in the Journal of Vac. Sci. and Technol. B10, March/April 1992.Google Scholar
[19]Singh, J. and Bajaj, K.K., J. Vac. Sci. Technol. B3, 520(1985).Google Scholar
[20]Voorhees, P.W., J. of Statistical Physics 38, 231 (1985).Google Scholar