Equilibrium Defects and Concentrations in Nickel Aluminide

Published online by Cambridge University Press:  10 February 2011

Bin Bai  and
Gary S. Collins
Bin Bai
Affiliation:
Department of Physics, Washington State University, Pullman, WA 99164–2814
Gary S. Collins
Affiliation:
Department of Physics, Washington State University, Pullman, WA 99164–2814
Get access

Abstract

Perturbed angular correlation of gamma rays was applied to determine properties of equilibrium defects in B2 NiAl near the stoichiometric composition. Point defects were detected through quadrupole interactions they induce at In probe atoms on the Al sublattice. Well-resolved signals were observed for probe atoms having zero, one or two Ni-vacancies (VNi) in the first neighbor shell. The fractions of probes in different sites are analyzed using a thermodynamic model to determine defect properties as follows. The equilibrium high-temperature defect is determined to be the triple defect combination (two VNi and one Ni-antisite atom) through the variation of the vacancy concentration with composition and not, for example, the Schottky vacancy pair. The binding enthalpy of VNi with a probe atom was determined to be in the range 0.18–0.24 eV. Site fractions were measured for three samples having 50.03, 50.14 and 50.91 at.% Ni at temperatures up to 1300 C. Vacancy concentrations were deduced from the site fractions and binding enthalpy. The equilibrium constant for formation of the triple defect was determined as a function of temperature from the vacancy concentrations and sample compositions. The formation enthalpy was found to be in the range 1.65–1.83 eV, depending on the binding enthalpy. The formation entropy was found to be -3.2(4) kB. The large, negative value of the formation entropy probably cannot be explained in terms of a binding entropy, and we speculate that triple defects harden the B2 lattice, perhaps by disrupting the well-known 1/3 <111> ‘soft mode’ lattice instability in B2 and bcc materials.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 552: Symposium KK – High-Temperature Ordered Intermetallic Alloys VIII , 1998 , KK8.7.1
Copyright
Copyright © Materials Research Society 1999

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1. Collins, Gary S., Shropshire, Steven L. and Fan, Jiawen, Hyperfine Interactions 62, 1 (1990).CrossRefGoogle Scholar
2. Recknagel, E., Schatz, G. and Wichert, Th., in Hyperfine Interactions or Radioactive Nuclei, Ed. Christiansen, J. (Springer, Berlin, 1983) p. 133.CrossRefGoogle Scholar
3. Pleiter, F. and Hohenemser, C., Phys. Rev. B25, 106 (1982).CrossRefGoogle Scholar
4. Another argument is that an InNi probe should be even an even higher-energy defect than the normally unobserved AlNj antisite atom due to the larger volume of the In probe atom.Google Scholar
5. Fan, Jiawen and Collins, Gary S., Hyperfine Interactions 60, 655 (1990)CrossRefGoogle Scholar
6. Collins, Gary S., Fan, Jiawen and Bai, Bin, in Structural Intermetallics 1997, Eds. Nathal, M.V., Darolia, R., Liu, C.T., Martin, P.L., Miracle, D.B., Wagner, R. and Yamaguchi, M. (The Minerals, Metals and Materials Society, 1997) p. 43.Google Scholar
7. Fan, Jiawen, Ph.D. dissertation, Washington State University, 1992 (unpublished).Google Scholar
8. Bai, Bin and Collins, Gary S., Mat. Res. Soc. Symp. Proc. 527, 203 (1998).CrossRefGoogle Scholar
9. Taylor, A. and Doyle, N. J., J. Appl. Cryst. 5, 201 (1972); the other potential elementary defects being VAl and AlNi.CrossRefGoogle Scholar
10. Bai, Bin, Ph.D. dissertation, Washington State University, 1998 (unpublished).Google Scholar
11. Bai, Bin, Collins, Gary S., Nieuwenhuis, Harmen Thys, Wei, Mingzhong, and Evenson, William E., Mat. Res. Soc. Symp. Proc. 527, 209 (1998).CrossRefGoogle Scholar
12. In earlier papers, for example ref. 6, we concluded using incorrect arguments that the Schottky vacancy pair was the equilibrium defect combination in NiAl instead of the triple defect.Google Scholar
13. Signals above 1520 K were strongly disturbed by motional relaxation that made site fractions difficult to determine accurately (cf. Fig. 1 and ref. 11).Google Scholar
14. Collins, Gary S., Peng, Luke S.-J. and Wei, Mingzhong, these proceedings.Google Scholar