Environmental Effects on Localized Corrosion of a High-Level Nuclear Waste Container Material

Published online by Cambridge University Press:  28 February 2011

N. Sridhar ,
G. Cragnolino  and
W. Machowski
N. Sridhar
Affiliation:
Southwest Research Institute, Center for Nuclear Waste Regulatory Analyses, 6220 Culebra Rd., San Antonio, TX 78228–0510
G. Cragnolino
Affiliation:
Southwest Research Institute, Center for Nuclear Waste Regulatory Analyses, 6220 Culebra Rd., San Antonio, TX 78228–0510
W. Machowski
Affiliation:
Southwest Research Institute, Center for Nuclear Waste Regulatory Analyses, 6220 Culebra Rd., San Antonio, TX 78228–0510
Get access

Abstract

The effect of environmental variables on the localized corrosion behavior of alloy 825 is examined in this paper. Cyclic, potentiodynamic polarization tests based on a two-level, full factorial experimental design were conducted. An index incorporating both the visual and scanning electron microscope examinations of localized corrosion and the electrochemical parameters was used for the statistical analysis. The analysis showed that chloride is the single most important promoter of localized corrosion, while nitrate was the single most important inhibitor. Fluoride was a weak inhibitor, especially at low chloride levels. Sulfate was a weak promoter, especially at high chloride levels. Temperature did not have a significant effect within the chloride levels examined. Separate experiments indicated that silicon, added as metasilicate, did not have any significant effect on localized corrosion. The adverse effect of chloride was observed at concentrations as low as 100 ppm. Addition of H2O2 increased the corrosion potential of alloy 825 to a value above the repassivation potential observed in the 300 ppm chloride solution.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 212: Symposium P – Scientific Basis for Nuclear Waste Management XIV , 1990 , 269
Copyright
Copyright © Materials Research Society 1991

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1. Farmer, J. C., McCright, R. D., and Kass, J. N., Survey of Degradation Modes of Candidate Materials for High-Level Radioactive Waste Disposal Containers, LLNL Report, UCID-21362 Summary, 1988.Google Scholar
2. Glass, R. S., et al., Electrochemical Determination of the Corrosion Behavior of Candidate Alloys Proposed for Containment of High-Level Waste in Tuff, UCID-20174, June 1984.Google Scholar
3. Beavers, J. A., Thompson, N. G., and Harper, W. V., “Potentiodynamic Polarization Studies of Candidate Container Materials in Simulated Tuff Repository Environment,” Mat. Res. Soc. Symp. Proa, v. 176, Scientific Basis for Nuclear Waste Management XIII, p. 533, Materials Research Society, Pittsburgh, Pennsylvania, 1990.Google Scholar
4. Cragnolino, G. A. and Sridhar, N., Experimental Studies on Localized Corrosion of Container Materials for High-Level Nuclear Waste Disposal, Corrosion/91, Paper 35, NACE, Houston.Google Scholar
5. Mason, R. L., Gunst, R. F., and Hess, J. L., Statistical Design & Analysis of Experiments, John Wiley & Sons, 1989.Google Scholar
6. Szklarska-Smialowska, Z., Pitting Corrosion of Metals, NACE, Houston, 1986.Google Scholar
7. Fratesi, R., Corrosion, V. 41, No. 2, p. 114, 1985.CrossRefGoogle Scholar
8. Leckie, H. P. and Uhlig, H. H., J. of Electrochemistry, V. 113, No. 12, p. 1262, 1966.Google Scholar