Effect of Pre-Oxidation on The Oxidation Behavior of Ti-2Al-2.5Zr Alloy at 300°C in An Alkaline Steam

  • X. T. Zu (a1) (a2), Y. L. Li (a3), G.T. Zeng (a1), X. Q. Huang (a3), Z.G. Wang (a1), L. B. Lin (a1) and X. D. Feng (a1)...

Abstract

The long-term oxidation behavior on a Ti-2Al-2.5Zr alloy with and without pre-oxidation oxidized at 300 in an alkaline steam for about 13000h were studied. Some of the samples were subjected to 400°C deionized water steam at a pressure of 10MPa for 72 hours for pre-oxidation. A comparison study has been carried out between the pre-oxidized and without pre-oxidized Ti-2Al-2.5Zr to determine the influence of pre-oxidation upon the properties of oxidation resistance. The result analysis showed that the oxide scales on the Ti-2Al-2.5Zr alloy consisted of Al2TiO5, TiO2, Ti3O5, Ti2O3, Al2O3 and TiO. The oxidation kinetics showed that the weight gains of the pre-oxidized samples were much less than that of the without pre-oxidized samples. The AES results showed that the whole thickness of the pre-oxidized sample thinner than that of the without pre-oxidized one, in contrast the pattern for the stable oxide scale was reversed, i.e. the pre-oxidized sample was much thicker. It is thought that pre-oxidation is an effective method to enhance the oxidation resistance of Ti-2Al-2.5Zr.

Copyright

References

Hide All
1. Ju, D., Zhentao, Y., Guanjun, Y., Rare Met 21, 88 (1997).
2. Zu, X. T., Wang, Z. G., Feng, X. D., et al., Surf. Coat. Technol., 140(2), 161 (2001).
3. Raynaud, P., Nardou, F., Billy, M., J. Chim. Phys., 76(6), 595 (1984).
4. Milosev, I., M. Metikos-Hukovic, Strehblow, H. H., Biomaterials 21, 2103 (2000).
5. Daychkov, V. I., Billy, M., J. Chim. Phys., 88, 233 (1991).
6. Langlade, C., Vannes, A. B., Krafft, J. M., Martin, J. R., Surf. Coat. Technol., 100–101, 383(1998).
7. Bloyce, A., Qi, P. Y., Dong, H., Bell, T., Surf. Coat. Technol., 107, 125 (1998).
8. Yerokhin, A. L., Nie, X., Leyland, A., Matthews, A., Surf. Coat. Technol., 130, 195 (2000).
9. Nie, X., Leyland, A., Matthews, A., Surf. Coat. Technol., 133–134, 331 (2000).

Metrics

Full text views

Total number of HTML views: 0
Total number of PDF views: 0 *
Loading metrics...

Abstract views

Total abstract views: 0 *
Loading metrics...

* Views captured on Cambridge Core between <date>. This data will be updated every 24 hours.

Usage data cannot currently be displayed