Durability of a Cementitious Wasteform for Intermediate Level Waste

  • Peter J. McGlinn (a1), Daniel R.M. Brew (a1), Laurence P. Aldridge (a1), Timothy E. Payne (a1), Kylie P. Olufson (a1), Kathryn E. Prince (a1) and Ian J. Kelly (a1)...

Abstract

Cementitious material is the most commonly used encapsulation medium for low and intermediate level radioactive waste. This paper focuses on the aqueous durability of a Materials Testing Reactor (MTR) cementitious wasteform – a possible candidate for the proposed intermediate level waste management facility in Australia. A series of medium term (up to 92 months) durability tests, without leachate replacement, were conducted on samples of this wasteform.

The wasteform was made from cement, ground granulated blast furnace slag and a simulated waste liquor. The compressive strength (39 MPa) was typical of MTR cement wasteforms and well above that required for handling or storage. The wasteform was an inhomogeneous mixture containing calcite, a calcium silicate hydrate phase, hydrotalcite and unreacted slag particles. After leaching for 92 months the crystallinity of the calcium silicate hydrate phase increased.

The majority of the releases of Ca, Si, Al, Sr, S, Na and K was reached within 4 days of leaching, with the maxima ie. the highest concentrations in the leachates, occurring at 3 months for Ca, Al, Sr, S, Na and K, and at 1 month for Si. For the longer leach periods (6 months and 3 months respectively) there was a slight reduction in concentration in the leachates, and these levels were similar to those for the longest period of 92 months, suggesting steady-state conditions prevailing after 3 to 6 months of leaching. The highest releases of matrix elements were for Na (37%), K (40%) and S (16%). Releases for elements such as Ca, Na, Al and Sr were similar in magnitude to those reported by the UKAEA in earlier MTR studies.

After leaching for 92 months there was an alteration layer about 80 ∞m deep where calcium has been depleted. Na, K and Sr showed signs of diffusion towards the outer part of the cement samples.

Copyright

References

Hide All
1 Carter, P.B., UKAEA (Dounreay), Manual for process qualification of cemented MTR raffinate at the Dounreay cementation plant, Report No. WSSD(99)P24, unpublished technical note (2000).
2 Howard, C.G. and Lee, D.J., UKAEA (Winfrith), Immobilisation of MTR waste in cement (product evaluation), Final Report No. AEEW-R 2312 (1987).
3 International Organization for Standardization (ISO), Long-term leach testing of solidified waste forms, ISO 6961-1982 (E) (1982).
4 Brown, P.E., Inns, A.J. and Lindsay, M., UKAEA (Harwell), The equilibrium leach testing of cemented MTR waste forms, Report No. AERE R 13312 (1988).
5 Revertegat, E., Richet, C. and Gégout, P., Cement and Concrete Research, 22, pp. 259272 (1992).
6 Faucon, P., Jacquinot, J.F., Adenot, F., Virlet, J. and Petit, J.C., Materials Research Symposium Proceedings, 465, pp. 295302 (1997).

Durability of a Cementitious Wasteform for Intermediate Level Waste

  • Peter J. McGlinn (a1), Daniel R.M. Brew (a1), Laurence P. Aldridge (a1), Timothy E. Payne (a1), Kylie P. Olufson (a1), Kathryn E. Prince (a1) and Ian J. Kelly (a1)...

Metrics

Full text views

Total number of HTML views: 0
Total number of PDF views: 0 *
Loading metrics...

Abstract views

Total abstract views: 0 *
Loading metrics...

* Views captured on Cambridge Core between <date>. This data will be updated every 24 hours.

Usage data cannot currently be displayed