Dopant Diffusion in TiSi2

Published online by Cambridge University Press:  26 February 2011

F. M. d'Heurle ,
A. E. Michel ,
F. K. LeGoues ,
G. Scilla ,
J. T. Wetzel  and
P. Gas
F. M. d'Heurle
Affiliation:
IBM T. J. Watson Research Center, PO Box 218, Yorktown Heights, N.Y. 10598
A. E. Michel
Affiliation:
IBM T. J. Watson Research Center, PO Box 218, Yorktown Heights, N.Y. 10598
F. K. LeGoues
Affiliation:
IBM T. J. Watson Research Center, PO Box 218, Yorktown Heights, N.Y. 10598
G. Scilla
Affiliation:
IBM T. J. Watson Research Center, PO Box 218, Yorktown Heights, N.Y. 10598
J. T. Wetzel
Affiliation:
IBM T. J. Watson Research Center, PO Box 218, Yorktown Heights, N.Y. 10598
P. Gas
Affiliation:
E. R. A. 443, Département de Métallurgie, Université Saint Jerome, rue Henri Poincaré, 13397 Marseille, France.
Get access

Abstract

Dopant elements, B and Ga, P, As and Sb, and Ge as well, have been implanted into thick (350–400 nm) layers of TiSi2 prepared by Ti-Si reaction. Both B and Sb appear to be immobile, this behavior is thought to result from very small solid solubilities, rather than from very small diffusion coefficients. The other elements display about the same behavior, with detectable grain boundary diffusion at temperatures as low as 600°C, and lattice diffusion becoming considerable at 750°C, so that with the cooperation of both phenomena almost complete homogenisation of these relatively thick layers occurs in 30 minutes at 800°C. Germanium is used in lieu of a Si radioactive tracer because it can be analyzed by Secondary Ion Mass Spectroscopy. Its behavior is thought to imply that there is little equilibrium adsorption of the dopant elements at the Si/TiSi2 interface. The comparable values of the diffusion coefficients for the mobile elements confirm the anticipation that the dopants move as substitutional atoms on the Si sublattice. Results obtained with some samples implanted with both dopant and Ti indicate that in these silicon-saturated suicide layers the diffusion process is not significantly affected by small changes in stoichiometry.

Type
Articles
Information
MRS Online Proceedings Library (OPL) , Volume 77: Symposium D – Interfaces, Superlattices, and Thin Films , 1986 , 333
Copyright
Copyright © Materials Research Society 1987

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1 Eichinger, P., Frenzel, E. and Neppl, F., Symp. Proc. Mater. Res. Soc. 25, 165 (1984).Google Scholar
2 Van Ommen, A. H., van Houtum, H. J. W. and Theunissen, A. M., J. Appl. Phys. 60, 627 (1986).Google Scholar
3 Gas, P., Deline, V., d'Heurle, F. M., Michel, A. and Scilla, G., J. Appl. Pys. 60, 1634 (1986).Google Scholar
4 Inoue, S., Toyokura, N., Nakamura, T. and Ishikawa, H., J. Electrochem. Soc. 128, 2402 (1981).Google Scholar
5 Shone, Fu-chia, Saraswat, K. C. and Plummer, J. D., Proceedings of International Symposium on VLSI Technology (Taipei, Taiwan, May 1985) p. 147.Google Scholar
6 Standard Diffraction Powder Pattern #5–684.Google Scholar
7 Hansen, M. and Anderko, K., Constitution of Binary Alloys (McGraw Hill, New York, 1958) p. 778.Google Scholar
8 Standard Diffraction Powder Pattern # 29–1362.Google Scholar
9 Standard Diffraction Powder Pattern # 35–785.Google Scholar
10 Hung, L. S., Guylai, J., Mayer, J. W., Lau, S. S. and Nicolet, M.-A., J. Appl. Phys. 54, 5076(1983).CrossRefGoogle Scholar
11 Chu, W. K., Lau, S. S., Mayer, J. W., Müller, H. and Tu, K. N., Thin Solid Films 25, 393 (1975).Google Scholar
12 d'Heurle, F. M. and Gas, P., J. Mater. Res. 1, 205 (1986).Google Scholar
13 Goldschmidt, H. J., Interstitial Alloys (Butterworths, London 1967) p. 584.CrossRefGoogle Scholar