Chemical Processing of Nanostructured Materials

Published online by Cambridge University Press:  21 March 2011

R. N. Das
R. N. Das*
Affiliation:
Department of Metallurgical Engineering and Materials Science, Indian Institute of Technology, Bombay, Powai, Mumbai-400076, India
Get access

Abstract

Nanocrystalline ( particle diameter less than 50 nm) ceramic powders have been prepared by the rapid evaporation of precursor solutions containing the respective metal nitrates/ hydroxides, triethanolamine (TEA) and sucrose in stoichiometric amounts. Complete evaporation of the solutions yields a fluffy dried precursor mass. Heat-treatment of the precursor mass at low external temperatures (450-700 °C) resulted in the desired nanocrystalline oxides. The oxide system studied are: barium titanate (BaTiO3), lanthanum modified lead zirconate-titanate (PLZT), Nickel ferrite (NiFe2O4) and Calcium Tungstate (CaWO4).

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 676: Symposium Y – Synthesis, Functional Properties and Applications of Nanostructures , 2001 , Y3.10
Copyright
Copyright © Materials Research Society 2001

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1. Das, R. N., Ray, J. C. and Pramanik, P., J. Mater. Res. 15, 2273 (2000).Google Scholar
2. Kodogawa, Y. and Ikeda, T. ; Chem. Express, 2, 309 (1987).Google Scholar
3. Das, R N. and Pramanik, P., Nanostructured Materials 8, 1371 (1998).Google Scholar
4. Anderton, D. J., Sale, F. R. ; Powder Metallurgy, 1, 8 (1979).Google Scholar
5. Pathak, A., Mukhopadhayay, D. and Pramanik, P.; Mat. Res. Bull., 27, 155 (1992).Google Scholar
6. Pechini, M. P., US Patent 3, 330, 697 (1967).Google Scholar
7. Anderton, D. J. and Sale, F. R. ; Powder Metallurgy, 1, 14 (1979)Google Scholar
8. Pramanik, P. Bull. Mat. Sci., 18[6], 819 (1995)Google Scholar
9. Baythoun, M. S. and Sale, F. R. ; J. Mater. Sci. 17, 2757 (1982).Google Scholar
10. Lessing, P. A. ; Ceramic Bulletin, 68, 1002 (1989).Google Scholar
11. Ravindranathan, P. and Patil, K. C. ; Am. Ceram. Soc. Bull., 66, 668 (1987).Google Scholar
12. Suresh, K., Kumar, N. R. S. and Patil, K. C. ; Adv. Mater., 30, 148 (1991).Google Scholar
13. Chick, L. A., Paderson, L. R., Maupin, G. D., Bates, J. L., Thomas, L. E. and Exarhos, G. J. ; Mater. Lett., 10, 6 (1990).Google Scholar
14. Klug, M. P. and Alexander, L. E., X-ray diffraction procedure for polycrystalline and amorphous materials-Wiley, New York, 1974, p634.Google Scholar