Characterization of Laser Induced Backside Damage for Gettering Purposes

Published online by Cambridge University Press:  15 February 2011

G.E.J. Eggermont ,
D.F. Allison ,
S.A. Gee ,
K.N. Ritz ,
R.J. Falster  and
J.F. Gibbons
G.E.J. Eggermont
Affiliation:
Philips Research Laboratories Sunnyvale Signetics Corp., 811 E. Arques Ave., Sunnyvale, CA, 94086, USA
D.F. Allison
Affiliation:
Philips Research Laboratories Sunnyvale Signetics Corp., 811 E. Arques Ave., Sunnyvale, CA, 94086, USA
S.A. Gee
Affiliation:
Philips Research Laboratories Sunnyvale Signetics Corp., 811 E. Arques Ave., Sunnyvale, CA, 94086, USA
K.N. Ritz
Affiliation:
Philips Research Laboratories Sunnyvale Signetics Corp., 811 E. Arques Ave., Sunnyvale, CA, 94086, USA
R.J. Falster
Affiliation:
Quantronix Corp., 225 Engineers Road, Smithtown, N.Y., 11787, USA
J.F. Gibbons
Affiliation:
Stanford Electronic Laboratories, Stanford, CA, 94305, USA
Get access

Abstract

A characterization of Q-switched Nd-YAG laser induced backside damage in various stages of a bipolar process is presented. TEM-analysis shows the occurence of microcracks, low angle boundaries and dislocations in as-irradiated wafers, of which the microcracks anneal out during an initial oxidation at 1050°C. The other damage is very stable and remains even after a heat treatment at 1200°C. This is quite in contrast with mechanically or Ar implantation induced backside damage, which anneal out completely at such high temperatures. Side effects of laser induced backside damage such as surface roughness and influence on wafer strength are found to be of no consequence within a limited range of laser pulse energy densities where the gettering efficiency is found to be very promising.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 4: Symposium A – Laser and Electron-Beam Interactions with Solids , 1981 , 615
Copyright
Copyright © Materials Research Society 1982

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1. Pearce, C.W., Zaleckas, V.J., J. Electrochem. Soc. 126, 1436 (1979).Google Scholar
2. Pearce, C.W., McMahon, R.G., J. Vac. Sci. and Techn. 14, 40 (1977).Google Scholar
3. Hayafuji, Y., Yanada, T., Aoki, Y., J. Electrochem. Soc. 128, 1975 (1981).Google Scholar
4. Eggermont, G.E.J., Linssen, A.J., unpublished results.Google Scholar
5. Dale, J.R., Gee, S.A., to be published.Google Scholar