Characterisation of Extended Defects in Si and Si1−x Gex Alloys: The Influence of Transition Metal Contamination

Published online by Cambridge University Press:  25 February 2011

V. Higgs  and
E.C. Lightowlers
V. Higgs
Affiliation:
Physics Department, King's College, London, Strand, London WC2R 2LS, UK
E.C. Lightowlers
Affiliation:
Physics Department, King's College, London, Strand, London WC2R 2LS, UK
Get access

Abstract

Photoluminescence (PL) spectroscopy, cathodoluminescence (CL) spectroscopy and imaging, transmission electron microscopy (TEM), and preferential defect etching and optical microscopy have been used to characterise dislocations in plastically deformed Si and in Si1−x Gex alloys. The PL spectra from plastically deformed Si produced under clean conditions, contained no dislocation related luminescence features. However, after deliberated Cu contamination and annealing, the PL spectra were dominated by the four main D-bands (D1-D4). CL spectroscopy and imaging revealed that the D3 and D4 bands originate on the slip lines, whereas D1 and D2 are dominant between the slip lines. Pseudomorphic Si1−x Gex layers grown by molecular beam epitaxy (MBE) and forced to relax by Cu contamination and annealing have also been examined. Both the PL and CL spectra were dominated by the D1-D4 bands, and monochromatic CL imaging showed that the D3 and D4 bands originate at the misfit dislocations with the location of the Dl and D2 bands being much less well defined. PL spectra from Si1−x Gex capping layers, grown by MBE on linearly compositionally graded buffer layers, were dominated by bound exciton luminescence features, identical with those observed in bulk grown alloys, and showed relatively weak D-band features. PL spectra obtained after chemical step etching, and CL spectra obtained with different beam energies, showed that the D-bands originated in the buffer layers which contained high densities of misfit dislocations. Well defined monochromatic CL images of the misfit dislocations could only be obtained using a narrow band pass filter centred on the D4 band. No D-band luminescence was observed from Si1−x Gex layers grown by high temperature chemical vapour deposition (CVD). However, after deliberate contamination with Ni, the D-bands became the dominant features and CL imaging clearly showed that the D4 band originates at the misfit dislocations and the D2 band predominantly between the misfit dislocations.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 263: Symposium F – Mechanisms of Heteroepitaxial Growth , 1992 , 305
Copyright
Copyright © Materials Research Society 1992

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1. Sauer, R., Weber, J., Stolz, J., Weber, E. R., Kiisters, K.H. and Alexander, H., Appl. Phys. A36, 1 (1985).Google Scholar
2. Weber, J. and Alonso, M.I., in “Defect Control in Semiconductors”, Proc. Int. Conf. on the Science and Technology of Defect Control in Semiconductors, Yokahama, 1989, edited by Sumino, K. (North Holland, Amsterdam, 1990), Vol. 2, p. 1453.Google Scholar
3. Lelikov, Yu. S., Rebane, Yu. T. and Shreter, Yu. G., Inst. Phys. Conf. Ser. No. 104, 119 (1989).Google Scholar
4. Higgs, V., Lightowlers, E.C., Norman, C.E. and Kightley, P., Mat. Sci. Forum 83–87, 1309 (1992).Google Scholar
5. Weronek, K., Weber, J., Hopner, A., Ernst, F., Buchner, R., Stefaniak, M. and Alexander, H., Mat. Sci. Forum 83–87, 1315 (1992).Google Scholar
6. Lelikov, Yu., Rebane, Yu., Ravimov, S., Tarhin, D., Sitnikoda, A. and Shreter, Yu., Mat. Sci. Forum 83–87, 1321 (1992).Google Scholar
7. Higgs, V., Goulding, M.R., Brinklow, A. and Kightley, P., Appl. Phys. Lett. 60, 1369 (1992).Google Scholar
8. Higgs, V., Norman, C.E., Lightowlers, E.C. and Kightley, P., Proc. 20th Int. Conf. on the Physics of Semiconductors, edited by Anastassakis, E.M. and Joanopoulos, J.D. World Scientific, Singapore, 1990), Vol. 1, p. 706.Google Scholar
9. Radzimski, Z.J., Zhou, T.Q., Buckowski, A., Rozgonyi, G. A., Finn, D., Hellwig, L.G. and Ross, J.A., Appl. Phys. Lett. 60, 1096 (1992).Google Scholar
10. Peaker, A.R., Kaniewska, M., Kaniewski, J., Evans, J.H., Hamilton, B. and Lorimer, G., Electrochem. Soc. Proc. Vol 91–9, 125 (1991).Google Scholar
11. Davies, G., Higgs, V., Kubiak, R.A.A., Powell, A., Whall, T.E. and Parker, E.H.C., MRS Symp. Proc. 220, 321 (1991).Google Scholar
12. Higgs, V., Kightley, P., Goodhew, P.J. and Augustus, P.D., Appl. Phys. Lett. 59, 829 (1991).Google Scholar
13. Fitzgerald, E.A., Xie, Y.H., Green, M.L., Brasen, D., Kortan, A.R., Michel, J., Mii, Y.J., and Weir, B.E., Appl. Phys. Lett. 59, 811 (1991).Google Scholar
14. Weber, J. and Alonso, M.I., Phys. Rev. B40, 5683 (1989).Google Scholar
15. Tajima, M., Takeno, H., and Abe, T., Mat. Sci. Forum 83–87, 1327 (1992).Google Scholar
16. Chew, N.G., Cullis, A.G., Warwick, C.A., Robbins, D.J., Hardman, R.W. and Gasson, D.B., Inst. Phys. Conf. Ser. No. 76, 129 (1985).Google Scholar
17. Graham, R.J., Spence, J.C.H. and Alexander, H., Mat. Res. Soc. Proc. Vol. 82, 235 (1987).Google Scholar
18. Yacobi, B.G. and Holt, D.B., Cathodoluminescence Microscopy of Inorganic Solids (Plenum Press, New York, 1990) p. 58.Google Scholar