Biaxially Textured Buffer Layers on Large-Area Polycrystalline Substrates

Published online by Cambridge University Press:  10 February 2011

J. Dzick ,
S. Sievers ,
J. Hoffmann ,
K. Thiele ,
F. Garcia-Moreno ,
A. Usoskin ,
C. Jooss  and
H. C. Freyhardt
J. Dzick
Affiliation:
Institut fuer Materialphysik, Windausweg 2, 37073 Goettingen, Germany kabelmetal electro GmbH, Kabelkamp 20, 30179 Hannover, Germany
S. Sievers
Affiliation:
Institut fuer Materialphysik, Windausweg 2, 37073 Goettingen, Germany kabelmetal electro GmbH, Kabelkamp 20, 30179 Hannover, Germany
J. Hoffmann
Affiliation:
Institut fuer Materialphysik, Windausweg 2, 37073 Goettingen, Germany
K. Thiele
Affiliation:
Institut fuer Materialphysik, Windausweg 2, 37073 Goettingen, Germany
F. Garcia-Moreno
Affiliation:
Institut fuer Materialphysik, Windausweg 2, 37073 Goettingen, Germany Zentrum fuer Funktionswerkstoffe gGmbH, Windausweg 2, 37073 Goettingen, Germany
A. Usoskin
Affiliation:
Zentrum fuer Funktionswerkstoffe gGmbH, Windausweg 2, 37073 Goettingen, Germany
C. Jooss
Affiliation:
Institut fuer Materialphysik, Windausweg 2, 37073 Goettingen, Germany
H. C. Freyhardt
Affiliation:
Institut fuer Materialphysik, Windausweg 2, 37073 Goettingen, Germany Zentrum fuer Funktionswerkstoffe gGmbH, Windausweg 2, 37073 Goettingen, Germany
Get access

Abstract

Biaxially textured yttria stabilized zirconia (YSZ) buffer layers were deposited on long polycrystalline metallic tapes by an ion-beam-assisted deposition process (IBAD) to serve as templates for high-current carrying Y1Ba2Cu3O7-x (YBCO) films. YSZ was deposited by a dualionbeam equipment with two 11 cm Kaufman ion sources. The coating of large-area technical substrates, large in comparison with the ion sources, requires substrate movements to render YSZ films of homogeneous texture quality. These movements can hinder cooling of the metallic tapes in the absence of a thermal contact. Therefore, the temperature of those small-heat-capacity substrates could rise to above 100 °C within minutes, causing a decrease of the in-plane alignment of YSZ. The investigation of the temperature dependence of the IBAD process reveals that the best results of the in-plane alignment could be obtained by room temperature deposition. Applying high tape velocities hinder a rise of the deposition temperature to above 90 °C. Therefore, it is possible to deposit YSZ films on metal tapes (up to 60 mm × 1000 mm) with in-plane textures down to 15° full width at half maximum (FWHM), which allow their coating with highcurrent-carrying YBCO films.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 585: Symposium L – Fundamental Mechanisms of Low-Energy-Beam Modified Surface , 1999 , 55
Copyright
Copyright © Materials Research Society 2000

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

[1] Goyal, A. et al., Appl. Phys. Lett. 69, p. 1795 (1996)Google Scholar
[2] lijima, Y., Tanabe, N., Ikeno, Y., and Kohno, O., Physica C 185, p. 1959 (1991)Google Scholar
[3] Simon, T., Ph. D. Thesis, University of Goettingen (1995)Google Scholar
[4] Wiesmann, J., Dzick, J., Hoffmann, J., Heinemann, K., and Freyhardt, H.C., Inst. Phys. Conf. Ser. No 158, p. 997 (1997)Google Scholar
[5] Hoffmann, J., Dzick, J., Wiesmann, J., Heinemann, K., Garcia-Moreno, F., and Freyhardt, H. C., J. Mater. Res. 12, p. 593 (1997)Google Scholar
[6] Dzick, J., Wiesmann, J., Hoffmann, J., Heinemann, K., Usoskin, A., Garcia-Moreno, F., Isaev, A., and Freyhardt, H.C., Inst. Phys. Conf. Ser. No 158, p. 1001 (1997)Google Scholar
[7] Dzick, J., Wiesmann, J., Hoffmann, J., Heinemann, K., F. Garcia-Moreno, Isaev, A., Freyhardt, H.C., and Lechner, W., IEEE Trans. on Appl. Supercond. Vol. 9, No. 2, p. 2248 (1999)Google Scholar
[8] Aston, G., Kaufman, H.R., and Wilbur, P.J., AIAA Journal Vol 16, No. 5, p. 516 (1978)Google Scholar
[9] Freyhardt, H.C., Hoffmann, J., Wiesmann, J., Dzick, J., Heinemann, K., Isaev, A., Usoskin, A., and Garcia-Moreno, F., Applied Superconductivity Vol. 4, p. 435 (1998)Google Scholar
[10] Wiesmann, J., Dzick, J., Hoffmann, J., Heinemann, K., and Freyhardt, H.C., J. Mater. Res. 11, p. 3149 (1998)Google Scholar
[11] Usoskin, A., García-Moreno, F., Dzick, J., Hoffmann, J., Sievers, S., and Freyhardt, H.C., Large-area HTS conductors obtained by novel PLD technique on metallic substrates, Contribution to Eucas '99, in press (2000)Google Scholar