Anti-bacterial property of Hydrogen-free amorphous carbon coatings on Ar plasma-pretreated polytetrafluoroethylene (PTFE) with a-C:H:F interlayer

  • Hironari Umemoto (a1), Terumitsu Hasebe (a1) (a2), Rumiko Kasai (a3), Yukihiro Yoshimoto (a1), So Nagashima (a4), Atsushi Hotta (a1) and Tetsuya Suzuki (a1)...

Abstract

Amorphous carbon (a-C) films have a growing interest in the biological and medical field, as a coating material, due to their biocompatibility and antibacterial property. However, a-C films deposited directly on polymers often show adhesion failure.

In this paper, two types of a-C films, amorphous hydrogenated carbon (a-C:H) film and hydrogen-free a-C (H-free a-C) film were deposited on polytetrafluoroethylene (PTFE) using a plasma deposition method. Prior to a-C film coating, the PTFE substrates were treated with Ar and O2 plasma and an appropriate interlayer was chosen to enhance the adhesion strength. The effect of the plasma pretreatment on the chemical composition of the PTFE was investigated by X-ray photoelectron spectroscopy (XPS). A T-peel test was carried out to evaluate the adhesion strength of the a-C coated PTFE. In the T-peel test, Ar plasma pretreatment improved the adhesion strength more effectively than that of O2 plasma pretreatment, because of the substantial defluorination and oxygen bonding occurred by Ar plasma pretreatment. Moreover, H-free a-C film reduced the numbers of Escherichia coli (E. coli) colonies dramatically, compared with original PTFE and a-C:H coated PTFE. Consequently, H-free a-C film coating can be a promising method to inhibit the increase of bacteria.

Copyright

References

Hide All
[1] Sigler, M., Paul, T., Grabitz, R.G., Zeitschrift Fur Kardiologie 94/6 (2005) 383.
[2] Lammer, J., Stoffler, G., Petek, W.W., Hofler, H., Investigative Radiology 21/4 (1986) 329.
[3] Marciano, F.R., Bonetti, L.F., Mangolin, J.F., Da-Silva, N.S., Corat, E.J., Trava-Airoldi, V.J., Vacuum 85/6 (2011) 662.
[4] Ozeki, K., Hirakuri, K.K., Applied Surface Science 254/6 (2008) 1614.
[5] Hoshida, T., Tsubone, D., Takada, K., Kodama, H., Hasebe, T., Kamijo, A., Suzuki, T., Hotta, A., Surface & Coatings Technology 202/4–7 (2007) 1089.
[6] Wilson, D.J., Williams, R.L., Pond, R.C., Surface and Interface Analysis 31/5 (2001) 385.
[7] Zhou, H., Xu, L., Ogino, A., Nagatsu, M., Diamond and Related Materials 17/7–10 (2008) 1416.

Keywords

Anti-bacterial property of Hydrogen-free amorphous carbon coatings on Ar plasma-pretreated polytetrafluoroethylene (PTFE) with a-C:H:F interlayer

  • Hironari Umemoto (a1), Terumitsu Hasebe (a1) (a2), Rumiko Kasai (a3), Yukihiro Yoshimoto (a1), So Nagashima (a4), Atsushi Hotta (a1) and Tetsuya Suzuki (a1)...

Metrics

Full text views

Total number of HTML views: 0
Total number of PDF views: 0 *
Loading metrics...

Abstract views

Total abstract views: 0 *
Loading metrics...

* Views captured on Cambridge Core between <date>. This data will be updated every 24 hours.

Usage data cannot currently be displayed