Additive Sintering Process in Aluminum Nitride Ceramics

Published online by Cambridge University Press:  25 February 2011

H. Makihara  and
N. Kamehara
H. Makihara
Affiliation:
FUJITSU LABORATORIES LTD., 10-1 Morinosato-Wakamiya, Atsugi, Kanagawa, 243-01, Japan
N. Kamehara
Affiliation:
FUJITSU LABORATORIES LTD., 10-1 Morinosato-Wakamiya, Atsugi, Kanagawa, 243-01, Japan
Get access

Abstract

Calcium compounds and yttrium compounds are frequently used as additives to densify AlN ceramics[l,2]. They react with oxygen impurities, such as A1203 in the raw AlN powder and in aluminate forms. A phase diagram is helpful in deciding the amount of additives to add, but the AlN sintering process doesn't come to equilibrium. We investigated the differences between sintering AlN with CaCO3 and with Y2O3.

With CaCO3 added, the calcium-aluminate liquid phase evaporates from the sintered AlN body at high sintering temperatures. The AlN thermal conductivity doesn't increase above a sintering temperature of 1700°C because residual oxygen substitutes into the AlN grains. With Y2O3 added, AlN sinters below 1850°C, as predicted by a phase diagram. With a large amount of Y2O3 added, 5 wt%, thermal conductivity doesn't depend on residual oxygen. This is because yttrium doesn't evaporate from the sintered AlN body and residual oxygen substitutes into AlN grains at an early stage of the AlN sintering.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 249: Symposium Q – Synthesis and Processing of Ceramics: Scientific Issues , 1991 , 437
Copyright
Copyright © Materials Research Society 1992

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

[1] Komeya, K., Tsuge, A., Inoue, H., and Ohta, H., J. Mat. Sci. Let. 1, 325 (1982).CrossRefGoogle Scholar
[2] Komeya, K. and Inoue, H., Trans. J. Brit. Ceram. Soc., 70, 107 (1971)Google Scholar
[3] Slack, G.A. and McNelly, T.F., J. Cryst. Growth 42, 560 (1977).Google Scholar
[4] Kuramoto, N., Taniguchi, H., and Aso, I., Proc. 1986 Electronic Component Conference IEEE Trans. Comp. Hybrids, Manuf. Technol., 8, 424 (1986).Google Scholar
[5] Udagawa, E., Makihara, H., Kamehara, N., and Niwa, K., J. Mat. Sci. Let. 9, 116 (1989).Google Scholar
[6] Ueno, F. and Horiguchi, A., 1st European Ceramic Society Conference, Maastricht, Netherlands, 1989.Google Scholar
[7] Nurse, R.W., Welch, J.H., and Majumdar, A.J., Trans. Brit. Ceram. Soc., 64, 416 (1965).Google Scholar
[8] Noguchi, T. and Mizuno, M., Kogyo zasshi, 70, 839 (1967).Google Scholar
[9] Slack, G.A., J. Phys. Chem. Solids, 34, 321 (1973).Google Scholar