Low Temperature PECVD Silicon Oxide For Devices And Circuits On Flexible Substrates

Published online by Cambridge University Press:  15 February 2011

Mark Meitine  and
Andrei Sazonov
Mark Meitine
Affiliation:
Electrical and Computer Engineering Department, University of Waterloo, 200 University Ave West, Waterloo, Ontario, N2L3G1, Canada
Andrei Sazonov
Affiliation:
Electrical and Computer Engineering Department, University of Waterloo, 200 University Ave West, Waterloo, Ontario, N2L3G1, Canada
Get access

Abstract

The aim of this research is to develop low temperature gate dielectric/passivation layer for μc-Si and poly-Si based devices and circuits compatible with plastic substrates.

The PECVD silicon oxide films were fabricated from mixture of silane and nitrous oxide at 250 °C, 120 °C and 75 °C. Helium, argon and nitrogen were used as diluent gases to optimize density, stress, uniformity, and electronic properties.

Chemical composition and bonding in the films were studied by FTIR spectroscopy. The absorption peak at 1075-1080 cm-1 observed in the spectrum of each film corresponds to SiO2 stretching mode. No presence of SiH stretching or NH-stretching vibrations was found in the FTIR spectra of the samples.

Film uniformity was varied from 1.44 % to 5.60 % for 3“×3” area. Four wafers were processed at the same time. The deposited films have compressive stress varied from 0.063 GPa to 0.117 GPa. Respective film density is in the range from 1.63 g/cm3 to 1.77 g/cm3.

The electronic properties were studied on MOS capacitors with 200 nm thick SiOx. The dielectric permittivity was in the range between 2.03 and 3.57. The dielectric breakdown at 9 MV/cm was observed for the films deposited at 120 °C. The films deposited at higher temperatures are characterized by lower leakage current density, which was 3.7.10-10 A/cm2 for the sample deposited at 250 °C, 9.10-9 A/cm2 for 120 °C, and 2.2.10-8 A/cm2 for 75 °C at 5 MV/cm.

The a-Si:H based TFTs were fabricated using low temperature oxide as gate dielectric. TFTs demonstrate threshold voltage (3.02 – 4.12 V) and mobility (0.12 – 0.59 cm2/Vs) comparing with those using silicon nitride.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 769: Symposium H – Flexible Electronics - Materials and Device Technology , 2003 , H6.6
Copyright
Copyright © Materials Research Society 2003

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

1. Gleskova, H., Wagner, S., Gasparik, V., and Kovac, P., J.Electrochem.Soc. 148, G370 (2001)Google Scholar
2. Stryahilev, D., Sazonov, A., and Nathan, A., J.Vac.Sci.Technol. A 20, 2231 (2002)Google Scholar
3. Smith, P.M., Carey, P.G. and Sigmon, T.W., Appl.Phys.Lett. 70, 324 (1997)Google Scholar
4. Lucovsky, G. and Phillips, J.C. in Flat-Panel Displays and Sensors - Principles, Materials and Processes, edited by Chalamala, B.R., Friend, R.H., Jackson, T.N., and Libsch, F.R. (Mater. Res. Soc. Proc. 558, Warrendale, PA, 2000) pp.135–140 Google Scholar
5. Hsieh, S.W., Chang, C.Y., and Hsu, S.C., J.Appl.Phys. 74, 2638 (1993)Google Scholar
6. Lucovsky, G. and Tsu, D.V., J.Vac.Sci.Technol. A 5, 2231 (1987)Google Scholar
7. Bulkin, P., Hofrichter, A., Heitz, T., Huc, J., Drevillon, B., and Benattar, J.J., J.Vac.Sci.Technol. A 20, 338 (2002)Google Scholar
8. Revesz, A.G., Anwand, W., Brauer, G., Hughes, H.L., and Skorupa, W., Appl.Surf.Sci. 194, 101 (2002)Google Scholar
9. Martinu, L. and Poitras, D., J.Vac.Sci.Technol. A 18, 2619 (2000)Google Scholar
10. Pereyra, I. and Alayo, M.I., J.Non-Cryst Solids 212, 225 (1997)Google Scholar
11. Han, S.S., Ceiler, M., Bidstrup, S.A., and Kohl, P., IEEE Trans.Comp.Pack.Manufac.Technol. A 17, 174 (1994)Google Scholar
12. Lucovsky, G., Yang, J., Chao, S.S., Tyler, J.E., and Czubatyj, W., Phys.Rev. B 28, 3225 (1983)Google Scholar
13. Powell, M.J., IEEE Trans.Elec.Devices, 36, 2753 (1989)Google Scholar
14. Sazonov, A., Stryahilev, D., Nathan, A., and Bogomolova, L.D., J.Non-Cryst.Solids 299-302, 1360 (2002)Google Scholar