Investigation of TiN/TiSi2 Bilayer Thin Films on Si (100) Substrate

Published online by Cambridge University Press:  15 February 2011

Y. Shor  and
J. Pelleg
Y. Shor
Affiliation:
Department of Materials Engineering, Ben - Gurion University of the Negev, Beer-Sheva, Israel.
J. Pelleg
Affiliation:
Department of Materials Engineering, Ben - Gurion University of the Negev, Beer-Sheva, Israel.
Get access

Abstract

In this work the conditions of forming a bi – layer structure of TiN/TiSi2 thin film on Si (100) substrate is investigated. Two methods of producing this structure were used: a) Deposition of Ti on Si (100), followed by reactive sputtering to obtain TiN on top of this layer and b) codeposition of Ti and Si on Si (100) and then deposition of TiN by reactive sputtering. The reactive sputtering was carried out in a mixture of N2/Ar with 20% N2. This amount is believed to be optimal for obtaining good quality and stoichiometric TiN films. Annealing is essential to form TiSi2 and it was performed either in the sputtering chamber immediately after the deposition or by rapid thermal annealing (RTA). The structure of the specimens was analyzed by X-ray diffraction using step scanning, Auger electron spectroscopy (AES) and transmission electron microscopy (TEM). TEM analysis was done on cross sectional specimens and also electron diffraction results were recorded. Resistivity measurements were performed by four – point probe method. The influence of TiN on the silicide formation was established. The results indicate that in the presence of TiN the phase TiSi2 was obtained, but in its absence Ti5 Si3 is formed under the same conditions of deposition and annealing. The stress distribution was investigated by Hall – Williamson curves and it was found that TiN stabilizes the silicide film and no peeling was observed. The effectiveness of TiN as diffusion barrier against Al and Si penetration was tested at 500°C/lh. It was found, that under these conditions, the TIN/TiSi2 structure is about the same, as before the heat treatment. No Al penetration is observed.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 402: Symposium H – Silicide Thin Films-Fabrication, Properties and Applications , 1995 , 107
Copyright
Copyright © Materials Research Society 1996

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

1. Chittipeddi, S., Dziuba, C. M. et al., J. of electronic materials V. 22 (7), p. 785–791 (1993).Google Scholar
2. Nassiopoulos, A. G. et al., J. Appl. Phys. 72 (10), p. 4660–4668 (1992).Google Scholar
3. Lee, Cheol - Jin and Sung, Yang - Kwon, J. of electronic materials. V.22, 7 (1993).Google Scholar
4. Dawson, P. T., Stazyk, S. A. J., J. Vac. Sci. Technol. 20 (4), p. 966–967 (1982).Google Scholar
5. Shiller, S. et al, Thin Solid Films. 111, p. 259 (1984).Google Scholar
6. Sproul, W. D., Thin Solid Films. 107, p. 141–147 (1983).Google Scholar
7. Perry, A. J., Chollet, L., J. Vac. Sci. Technol. A4 (6), p. 2801–2807 (1986).Google Scholar
8. Hopfe, S. et al., Solid State Phenomena V. 19 – 20, p. 611–616 ( 1991).Google Scholar
9. Ku, Y. N. et al., Appl. Phys. Lett. 50 (22), p. 1598–1600 (1987).Google Scholar
10. Murarka, S. P., Silicides For VLSI Applications, Academic Press, New York, 1983, pp. 30, 51, 130, 200.Google Scholar
11. Murarka, S. P., et. al., Transactions on Electron Devices, (VED - 27, 8, 1980), p.1409 – 1417.Google Scholar
12. Murarka, S. P., Transactions on Electron Devices, (IEEE, 1979), p. 454 – 457.Google Scholar
13. Pelleg, J., Zevin, L. Z., Lungo, S. and Croitoru, N., Thin Solid Films 197, p. 117 (1991).Google Scholar
14. Goldfarb, I., Pelleg, J., Zevin, L. and Croitoru, N., Thin Solid Films 200, p. 117 (1991).Google Scholar
15. Murarka, S. P. and Fraser, D. B., J. Appl. Phys. 51, p. 350 (1980).Google Scholar
16. Williamson, G. K. and Hall, W. H., Acta Met. 1, p. 22 (1953).Google Scholar
17. JCPDS-ICDD, card number 35–785, (1991).Google Scholar
18. Angilello, J., d'Heurle, F., Peterson, S. and Segmuller, A., J. Vac. Sci. Technol. 17(I), p. 471 (1980).Google Scholar
19. Rozenkranz, R., Frommeyer, G. and Smarsly, W., Materials Science and Eng. A152, p. 288 (1992).Google Scholar
20. Rosenberg, R., Sullivan, M. J. and Howard, J. K. in Poate, J. M., Tu, K. N. and Mayer, J. W. (Eds.), “Thin Films – Interdiffusion and Reactions”. The Electronical Soc. Inc. (Princeton, NJ, 1978) p. 15.Google Scholar
21. Price, I. E. and Bethoud, L. A., Solid State Electron. 16, p. 1303 (1973).Google Scholar
22. Pelleg, J., Zalkind, S., Zevin, L. and Ditchek, B. M., Thin Solid Films 249, p. 126 (1994).Google Scholar