Corrosion Resistance of Ceramic Refractories to Simulated Waste Glasses at High Temperatures

Published online by Cambridge University Press:  15 February 2011

Shi-Ben Xing ,
Yijing Lin ,
Robert K. Mohr  and
Ian L. Pegg
Shi-Ben Xing
Affiliation:
Vitreous State Laboratory, The Catholic University of America, Washington D.C. 20064
Yijing Lin
Affiliation:
Vitreous State Laboratory, The Catholic University of America, Washington D.C. 20064
Robert K. Mohr
Affiliation:
Vitreous State Laboratory, The Catholic University of America, Washington D.C. 20064
Ian L. Pegg
Affiliation:
Vitreous State Laboratory, The Catholic University of America, Washington D.C. 20064
Get access

Abstract

In many vitrification processes, refractory materials are used to contain the waste glass melt. The corrosive nature of the high-temperature melt consumes the waste feed materials but also limits refractory life. As vitrification is applied to more diverse waste streams, and particularly in higher-temperature applications, increasingly severe demands are placed on the refractory materials. A variety of potential refractory materials including Fused-cast AZS, Monofrax K3, Monofrax E, and the Corhart refractories ER1195, ER2161, C1215, C1215Z, Rechrome, and TI 186, were subjected to corrosion testing at 1450°C using the ASTM C-621 procedure. A series of simulated waste glasses was used which included F, Cl, S, Cu, Zn, Pb; these minor components were found to cause significant, and in some cases drastic, increases in corrosion rates. The corrosion tests were conducted over a range of time intervals extending to 144 hrs in order to investigate the kinetics of the corrosion processes. The change of the concentrations of constituents in the glass was monitored by compositional analysis of glass samples and correlated to the observed extent of corrosion; typically, components of the material under test increase with time while key minor components, such as Cu and Pb, decrease. The rate of corrosion of high-zirconia refractories was slowed considerably by adding zirconia to the waste glass composition; this has the added benefit of improving the aqueous leach resistance of the waste form that is produced.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 412: Symposium V – Scientific Basis for Nuclear Waste Management XIX , 1995 , 181
Copyright
Copyright © Materials Research Society 1996

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

[1]. Pegg, I.L., Ceramics Trans., Vol.39, 13–22, (1994).Google Scholar
[2]. Rankin, W. N., “Advances in Ceramics”, Vol.8, Nuclear Waste Management I, 559–566, (1980).Google Scholar
[3]. Wicks, G.G., “Ceramics in Nuclear Waste management”, DOE, 82–85, (1980).Google Scholar
[4]. Bickford, D.F., Ondrejcin, R.S., and Salley, L., “Advance in Ceramics”, Vol.20, Nuclear Waste Management II, 65–78 (1984).Google Scholar
[5]. ASTM C621-84, “Standard Test Method for Isothermal Corrosion Resistance of Refractories to Molten Glass,” American Society for Testing and Materials, Philadelphia, PA, (1992).Google Scholar
[6]. Sundaram, S. Kamakshi, Hsu, J.-Y., Speyer, R. F., J. Amer. Ceram. Soc., vol.77, 1613–1624.Google Scholar
[7]. Feng, Xiangdong, Pegg, Ian, Barkatt, Aaron, Macedo, Pedro B., Cucinell, Samuel J., and Lai, Shantao, “Correlation Between Composition Effects on Glass Durability and the Structural Role of the Constituent Oxides”, Vol.85, Nuclear Technology, 334 (1989).Google Scholar